Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Ball Indentation Hardness | 100 MPa | 14500 psi | ISO2039.1 DIN.53456 |
Omnia Plastica Akulon® PA 66 - Akulon 66 - at 50% RH Polyamide obtained by the polymerisation of Hexamethylenediamine and Adipic acid. It is one of the oldest engineering plastics, having been created in the USA in 1930. Due to its origin it is widely.. |
|||
Ball Indentation Hardness | 100 MPa | 14500 psi | ISO2039.1 DIN.53456 |
Omnia Plastica Noryl® PPO m Polyphenylenoxide Noryl is a resin based on polyphenylene oxide, modified with styrene. Its main field of application is the electrical one.Features:Good electrical properties, even at high frequency Dimensional stab.. |
|||
Ball Indentation Hardness | 100 MPa | 14500 psi | ISO2039.1 DIN.53456 |
Omnia Plastica Omniamid PA6 G - G - at 50% RH Cast nylon 6. The method of production of this polyamide (i.e. the polymerisation of the caprolactam directly in the mould) allows the production of stock shapes in larger than normal dimensions, su.. |
|||
Ball Indentation Hardness | 100 MPa | 14500 psi | ISO2039.1 DIN.53456 |
Omnia Plastica Omniamid PA6 GHR - HR - at 50% RH Cast nylon 6 produced with the addition of graphite and a special lubricator which gives to this product better properties than natural PA6G. Whilst retaining the general features of OMNIAMID G it i.. |
|||
Ball Indentation Hardness | 100 MPa | 14500 psi | ISO2039.1 DIN.53456 |
Omnia Plastica PA 11 Rilsan B The only engineering plastic of natural origin (derived from castor oil), it is a polyamide which, unlike the other nylons, does not absorb humidity. It has all the good mechanical features of polya.. |
|||
Ball Indentation Hardness | 100 MPa | 14500 psi | ISO2039.1 DIN.53456 |
Omnia Plastica PVDF Kynar PVDF is a relatively new fluoropolymer. Like the other fluoropolymers, its best feature is its chemical resistance. The mechanical features of PVDF are notably higher than PTFE and it does not suffe.. |
|||
Ball Indentation Hardness | 100 MPa | 14500 psi | ISO 2039-1 |
Polycasa XT 610 PMMA QUINN XT sheets have good optical properties and a brilliant surface. QUINN XT sheets offer excellent transparency, good mechanical properties, are UV resistant, have very good weathering and ageing.. |
|||
Ball Indentation Hardness | 100 MPa | 14500 psi | ISO 2039-1 |
Nilit FRIANYL A63 S20 Nylon 6.6 for injection molding Nylon 6.6 for injection molding, impact modified.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Ball Indentation Hardness | 100 MPa | 14500 psi | ISO 2039-1 |
Nilit FRIANYL B63 L-HS-GV30 Nylon 6 for injection molding, 30% glass fiber reinforced Nylon 6 for injection molding, improved fluidity, high impact modified.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Ball Indentation Hardness | 100 MPa | 14500 psi | ISO 2039-1 |
Nilit FRIANYL B63 S20 Nylon 6 for injection molding Nylon 6 for injection molding, impact modified.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Ball Indentation Hardness | 100 - 116 MPa | 14500 - 16800 psi | Average value: 112 MPa Grade Count:21 |
Overview of materials for Polycarbonate, UV Stabilized This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, UV Stabilized". Each property range of values reported is minimum and maximum values of a.. |
|||
Ball Indentation Hardness | 100 MPa | 14500 psi | ISO 2039-1 |
Ineos ABS Lustran® Ultra 4115 ABS Pellets (a-methylstyrene-SAN / PC-modified), Very High Heat Grade Lustran® Ultra 4115 is very high heat grade with high impact resistance and is PC-modified. It is used for the production of molded plastic articles. |
|||
Ball Indentation Hardness | 100 MPa | 14500 psi | Hc 30; ISO 2039; partially |
Schwartz Technical Plastics LAMIGAMID® 1200 Cast Polyamide 12, Dry Application: sprockets, chain-wheels, pulleys, wheels, slide and seal rings, curve disks, etc.Information provided by Schwartz Technical Plastics GmbH |
|||
Ball Indentation Hardness | 100 MPa | 14500 psi | Hc 30; ISO 2039; partially |
Schwartz Technical Plastics LAMIGAMID® 200 Polyamide 66, Conditioned Application: bearing bushes, machine parts, gears, linersInformation provided by Schwartz Technical Plastics GmbH |
|||
Ball Indentation Hardness | <= 100 MPa | <= 14500 psi | Hc 30; ISO 2039; partially |
Schwartz Technical Plastics LAMIGAMID® 400 Cast Polyamide 6, Elastomer Modified, Dry Application: gear-wheels, chain-wheels, hydrocyclones, housings, outrigger floatsInformation provided by Schwartz Technical Plastics GmbH |
|||
Ball Indentation Hardness | 100 MPa | 14500 psi | ISO 2039-1 |
Styrolution Novodur® 4115 ABS Novodur Ultra 4115 is a PC modified high heat injection molding grade. It provides good heat resistance combined with high impact strength.Information provided by Styrolution |
|||
Ball Indentation Hardness | 100 MPa | 14500 psi | ISO 2039-1 |
Styrolution Novodur® 5300 ABS Novodur 5300 is a high heat injection molding grade with high impact strength, good chemical resistance and reduced emission (PC modified)Information provided by Styrolution |
|||
Ball Indentation Hardness | 100 MPa | 14500 psi | DIN 53456 |
Zell-Metall Engineering Plastics Zellamid 1200 G Zellamid® 1200 G is manufactured by an activated anionic reaction. Finished and semi-finished parts are produced by a static cast process. This process makes it possible to produce a material wit.. |
|||
Ball Indentation Hardness | 100 MPa | 14500 psi | H 358/30; ISO 2039; DIN 53456 |
Zell-Metall Engineering Plastics Zellamid 250 (PA6.6) at 50% RH Zellamid® 250 is noted for its high temperature resistance and high tensile strength. It is the hardest and most rigid type of extruded Nylon. Main characteristics are high resistance to fuels, oil.. |
|||
Ball Indentation Hardness | 100 MPa | 14500 psi | dry; ISO 2039-1 |
EMS-Grivory Grivory® XE 4188 nat PA612 Product description: Grilamid XE 4188 natural is a high viscosity, unreinforced, impact resistant polyamide 612 (PA612) extrusion grade. Unique features of Grilamid XE 4188 natural are: High viscosi.. |
|||
Ball Indentation Hardness | 100 MPa | 14500 psi | H358/30; ISO 2039-1 |
Chi Mei Wonderlite® PC-108U Polycarbonate - UV Stabilized UV Stabilized |
|||
Ball Indentation Hardness | 100 - 170 MPa @Time 30.0 sec |
14500 - 24700 psi @Time 0.00833 hour |
DIN 53 456 |
Hippe PA 66 Nylon 66 The polyamide with high degree of hardness, stiffness, scuff strength and stability of shape under heat. Preferred polyamide for components subjected to high load and heat stress in electrical, mec.. |
|||
Ball Indentation Hardness | 100 MPa | 14500 psi | dry; ISO 2039-1 |
EMS-Grivory Grivory® EB 50 H DZ PA6 Product description: Grilon EB 50 H DZ is a high viscosity, unreinforced, heat stabilized, impact modified PA6 extrusion blow molding grade. Grilon EB 50 H DZ has the following important properties:.. |
|||
Ball Indentation Hardness | 100 MPa | 14500 psi | H358/30; ISO 2039-1 |
Chi Mei Wonderlite® PC-110N Polycarbonate - Flame Retardant Opaque |
|||
Ball Indentation Hardness | 100 MPa | 14500 psi | value at 30 sec.; ISO 2039-1 |
CENTROPLAST CENTROPHEN Polyphenylene ether modified This material is a lightweight plastic with low moisture absorption, and is impact resistant at low temperatures. Applications include fittings, drive components for domestic appliances, and compon.. |
|||
Ball Indentation Hardness | 100 - 115 MPa | 14500 - 16700 psi | ISO 2032 |
Adamas Adalon® 453 PTFE, Mica filler Information provided by Adamas, HPM |
|||
Ball Indentation Hardness | 100 MPa @Time 30.0 sec |
14500 psi @Time 0.00833 hour |
DIN 53 456 |
Hippe PVC-U Polyvinyl Chloride Material at reasonable price, high strength. Used in machine construction as covers, pipes, section, façade elements.Information provided by Hippe. |
|||
Ball Indentation Hardness | 100 - 175 MPa | 14500 - 25400 psi | Average value: 149 MPa Grade Count:8 |
Overview of materials for Acrylic, Extruded This property data is a summary of similar materials in the MatWeb database for the category "Acrylic, Extruded". Each property range of values reported is minimum and maximum values of appropriate .. |
|||
Ball Indentation Hardness | 100 MPa | 14500 psi | conditioned; ISO 2039-1 |
EMS-Grivory Grivory® LC-15H black PA12-CF15 Product description: Grilamid LC-15H black is a Polyamide 12 injection molding product reinforced with 15% carbon fibers. The product is inherently black and is only available in this color.Main Att.. |