Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Ball Indentation Hardness | 70.0 - 150 MPa | 10200 - 21800 psi | ISO.2039-2 |
Polimersan Plastics POLIPA® (PA 6) Polyamide POLIPA® PA6 (POLYAMIDE) is produced by poly condensation of e-aminoacid and by the help of d-carbon acid and d-amine poly condensation. Its characteristics depend upon the numbers of the main struc.. |
|||
Ball Indentation Hardness | 70.0 - 150 MPa | 10200 - 21800 psi | ISO.2039-2 |
Polimersan Plastics POLIPA® (PA 6) Polyamide POLIPA® PA6 (POLYAMIDE) is produced by poly condensation of e-aminoacid and by the help of d-carbon acid and d-amine poly condensation. Its characteristics depend upon the numbers of the main struc.. |
|||
Ball Indentation Hardness | 70.0 MPa | 10200 psi | ISO 2039-1 |
Quadrant EPP Semitron® ESd 225 POM-C, static dissipative, extruded (ISO Data) Semitron ESd 225 is an acetal based static dissipative material ideal for material handling operations. It is also an excellent choice for fixturing used in the manufacturing of hard disk drives or .. |
|||
Ball Indentation Hardness | 70.0 - 95.0 MPa | 10200 - 13800 psi | Average value: 80.0 MPa Grade Count:5 |
Overview of materials for Acrylonitrile Butadiene Styrene (ABS), Transparent, Molded This property data is a summary of similar materials in the MatWeb database for the category "Acrylonitrile Butadiene Styrene (ABS), Transparent, Molded". Each property range of values reported is m.. |
|||
Ball Indentation Hardness | 70.0 - 205 MPa | 10200 - 29700 psi | Average value: 151 MPa Grade Count:10 |
Overview of materials for Nylon 6, 30% Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 30% Mineral Filled". Specific grades with primary filler content between 25% and 34% are includ.. |
|||
Ball Indentation Hardness | 70.0 MPa | 10200 psi | H 358/30; ISO 2039-1 |
LyondellBasell Moplen HP400H Polypropylene Homopolymer Description: Moplen HP400H is a homopolymer for extrusion applications. Moplen HP400H exhibits easy processability and a good stiffness/impact balance at ambient temperature. The main applications .. |
|||
Ball Indentation Hardness | 70.0 MPa | 10200 psi | DIN 53456 |
Global PP-2300-K Polypropylene Block Copolymer Description-opacity, medium to high stiffness, high impact strength at low temperatureApplications-furniture, crates, closures, electrical appliances, automotiveInformation provided by Global Polyme.. |
|||
Ball Indentation Hardness | 70.0 MPa | 10200 psi | Hc 30; ISO 2039; partially |
Schwartz Technical Plastics LAMIGAMID® 410 Cast Polyamide 6, Elastomer Modified, Low Temp, Dry Application: outrigger floats, rollersInformation provided by Schwartz Technical Plastics GmbH |
|||
Ball Indentation Hardness | 70.0 MPa @Load 36.5 kg, Time 30.0 sec |
10200 psi @Load 80.5 lb, Time 0.00833 hour |
ISO 2039-1 |
Styrolution Luran® S 776 S Colored ASA Description: Injection molding grade with good toughness and strength. Uses include parts for garden equipment, parts for office chairs and antennas.Information provided by STYROLUTION, which is a j.. |
|||
Ball Indentation Hardness | 70.0 MPa @Load 36.5 kg, Time 30.0 sec |
10200 psi @Load 80.5 lb, Time 0.00833 hour |
ISO 2039-1 |
Styrolution Luran® S 776 S UV ASA Description: Injection molding grade with good toughness and strength. Uses include parts for garden equipment, parts for office chairs and antennas.Information provided by STYROLUTION, which is a j.. |
|||
Ball Indentation Hardness | 70.0 MPa @Load 36.5 kg, Time 30.0 sec |
10200 psi @Load 80.5 lb, Time 0.00833 hour |
ISO 2039-1 |
Styrolution Terblend® N NM-19 XP Beige 38163 ABS+PA (Conditioned) Description: Terblend® N NM-19 XP is an UV stabilized ABS/PA blend combining very high impact strength, even at low temperatures with an outstanding processability and excellent surface appearanc.. |
|||
Ball Indentation Hardness | 70.0 MPa @Load 36.5 kg, Time 30.0 sec |
10200 psi @Load 80.5 lb, Time 0.00833 hour |
ISO 2039-1 |
Styrolution Terlux® 2802 TR Q434 Transparent MABS Description: Terlux® 2802 TR Q434 is a new grade with enhanced toughness.Information provided by STYROLUTION, which is a joint venture between BASF and INEOS |
|||
Ball Indentation Hardness | 70.0 MPa | 10200 psi | ISO 2039-1 |
Styrolution Terlux® HD 2822 MABS Terlux® HD 2822 is a new standard-injection molding grade based on a MABS polymer. Terlux® HD 2822 offers a well balanced combination of stiffness and toughness and the high transparency well .. |
|||
Ball Indentation Hardness | 70.0 MPa | 10200 psi | 358 N/30 s; ISO 2039 |
Borealis HF700SA Polypropylene HF700SA is a polypropylene homopolymer intended for injection molding. This material has excellent balanced mechanical properties and is easy to process. Applications: household applications.Infor.. |
|||
Ball Indentation Hardness | 70.0 MPa | 10200 psi | H 358/30; ISO 2039; DIN 53456 |
Zell-Metall Engineering Plastics Zellamid 202 (PA 6) at 50% RH Zellamid® 202 is a tough material with high resistance to abrasion and impact. It features good mechanical properties. By water absorption the excellent shock and vibration resistance is increased... |
|||
Ball Indentation Hardness | 70.0 MPa | 10200 psi | conditioned; ISO 2039-1 |
EMS-Grivory Grivory® BG-30 FR PA6-GF30 FR Information provided by EMS Grivory |
|||
Ball Indentation Hardness | 70.0 MPa | 10200 psi | conditioned; ISO 2039-1 |
EMS-Grivory Grivory® BM-30 PA6-MD30 Product description: Grilon BM-30 is a 30% mineral reinforced PA6 injection moulding grade. Grilon BM-30 has the following important properties: heat stabilizedimpact resistantisotropic shrinkagelig.. |
|||
Ball Indentation Hardness | 70.0 MPa | 10200 psi | conditioned; ISO 2039-1 |
EMS-Grivory Grivory® L 16 GM nat PA12 Grilamd L16 GM is a low-viscosity, non-reinforced PA 12 grade, UV- and heat-stabilized. The modification with a crystallization regulator causes a quick freeze and a fine, crystalline structure. Due.. |
|||
Ball Indentation Hardness | 70.0 MPa | 10200 psi | conditioned; ISO 2039-1 |
EMS-Grivory Grivory® L 20 G HL PA12 Product Description: Grilamid L 20 GHL is a, medium viscosity injection molding grade, based on Polyamide 12 (PA12). Grilamid L 20 GHL is UV-stabilized, and heat stabilized The special features of G.. |
|||
Ball Indentation Hardness | 70.0 MPa | 10200 psi | conditioned; ISO 2039-1 |
EMS-Grivory Grivory® XE 3926 black 9992 PA12 Product description: Grilamid XE 3926 black 9992 is a low viscosity extrusion type, based on Polyamide 12 (PA 12). The special features of Grilamid XE 3926 black 9992 are: Very good chemical resista.. |
|||
Ball Indentation Hardness | 70.0 MPa | 10200 psi | conditioned; ISO 2039-1 |
EMS-Grivory Grivory® XE 3959 black 9992 PA610 Product description: Grilamid XE 3959 is a high viscosity Polyamide 610 especially suitable for extrusion applications. This PA610 product is to a large extent based on renewable raw materials and i.. |
|||
Ball Indentation Hardness | 70.0 MPa | 10200 psi | conditioned; ISO 2039-1 |
EMS-Grivory Grivory® XE 4071 black 9992 PA612 Product description: Grilamid XE 4071 BLACK 9992 is an impact modified unreinforced high viscosity polyamide 612 (PA612) extrusion grade with superior heat and hydrolysis resistance. Compared to sta.. |
|||
Ball Indentation Hardness | 70.0 MPa | 10200 psi | conditioned; ISO 2039-1 |
EMS-Grivory Grivory® XE 4188 black 9992 PA612 Product description: Grilamid XE 4188 black 9992 is a high viscosity, unreinforced, impact resistant polyamide 612 (PA612) extrusion grade. Unique features of Grilamid XE 4188 black 9992 are: High v.. |
|||
Ball Indentation Hardness | 70.0 MPa | 10200 psi | conditioned; ISO 2039-1 |
EMS-Grivory Grivory® XE 4188 nat PA612 Product description: Grilamid XE 4188 natural is a high viscosity, unreinforced, impact resistant polyamide 612 (PA612) extrusion grade. Unique features of Grilamid XE 4188 natural are: High viscosi.. |
|||
Ball Indentation Hardness | 70.0 MPa | 10200 psi | conditioned; ISO 2039-1 |
EMS-Grivory Grivory® L 25 H PA12 Product Description: Grilamid L 25 H is a high viscosity heat stabilized Polyamide 12 extrusion grade and is suitable for application requiring a long-term usage temperature of 100 - 120°C. The mai.. |
|||
Ball Indentation Hardness | 70.0 - 230 MPa | 10200 - 33400 psi | Average value: 169 MPa Grade Count:52 |
Overview of materials for Nylon 6, 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 30% Glass Fiber Filled". Specific grades with glass content between 25% and 34% are included. E.. |
|||
Ball Indentation Hardness | 70.0 MPa | 10200 psi | Fm=358N; Ø 50x4mm; ISO 2039-1 |
SYNTHOS Krasten® 552M High Impact Polystyrene High impact grade with a wide range of Applications. Processed mainly by injection moulding. Production of consumer goods and technical parts subjected to increased mechanical stress. Good results i.. |
|||
Ball Indentation Hardness | 70.0 - 150 MPa | 10200 - 21800 psi | Average value: 109 MPa Grade Count:11 |
Overview of materials for Nylon 6, Impact Grade This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Impact Grade". Each property range of values reported is minimum and maximum values of appropri.. |
|||
Ball Indentation Hardness | 70.0 - 175 MPa | 10200 - 25400 psi | Average value: 140 MPa Grade Count:35 |
Overview of materials for Nylon 6, Cast This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Cast". Each property range of values reported is minimum and maximum values of appropriate MatW.. |
|||
Ball Indentation Hardness | 70.0 - 200 MPa | 10200 - 29000 psi | Average value: 155 MPa Grade Count:31 |
Overview of materials for Nylon 6, 20% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 20% Glass Fiber Filled".Specific grades with glass content between 15% and 24% are included. Ea.. |