Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Ball Indentation Hardness | 124 MPa | 18000 psi | 132 N/10s; ISO 2039 |
Borealis GB311U Polypropylene Compound, Glass Fiber Reinforced GB311U is a 30% chemically coupled glass fiber reinforced polypropylene compound intended for injection molding. This material shows excellent mechanical properties also at elevated temperatures. .. |
|||
Ball Indentation Hardness | 124 MPa | 18000 psi | H 385/30; ISO 2039 |
Borealis Xmod™ K65G2 20% Glass Fiber Reinforced Polypropylene Compound Xmod K65G2 is a 20% glass fiber reinforced grade intended for injection molding. Xmod K65G2 has been developed especially for the car industry, to be used UTB parts. Xmod K65G2 offers good balance.. |
|||
Ball Indentation Hardness | 124 MPa @Load 36.5 kg, Time 30.0 sec |
18000 psi @Load 80.5 lb, Time 0.00833 hour |
ISO 2039-1 |
BASF Ultrason® P 3010 MR SW 10101 PPSU Description: Unreinforced, higher viscosity injection molding grade, flame retardant and with improved chemical resistance. This grade is black colored and demolding optimized. Abbreviated designati.. |
|||
Ball Indentation Hardness | 124 MPa @Load 36.5 kg, Time 30.0 sec |
18000 psi @Load 80.5 lb, Time 0.00833 hour |
ISO 2039-1 |
BASF Ultrason® P 3010 PPSU Unreinforced Polyphenylsulfone Description: Medium viscosity injection-molding and extrusion grade with good toughness and chemical resistance (stress crack resistance), resistant against superheated steam. The property profile m.. |