Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Charpy Impact | 8.00 J @Temperature 23.0 °C |
5.90 ft-lb @Temperature 73.4 °F |
Longitudinal |
Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, 1.6 mm thick sheet Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
Charpy Impact | 8.00 J @Temperature 23.0 °C |
5.90 ft-lb @Temperature 73.4 °F |
Longitudinal |
Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, 12.7 mm (1/2 in.) thick plate Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
Charpy Impact | 8.00 J @Temperature 23.0 °C |
5.90 ft-lb @Temperature 73.4 °F |
Longitudinal |
Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, 15.9 mm thick bar Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
Charpy Impact | 8.00 J @Temperature 23.0 °C |
5.90 ft-lb @Temperature 73.4 °F |
Longitudinal |
Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 1.0 mm thick sheet Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
Charpy Impact | 8.00 J @Temperature 23.0 °C |
5.90 ft-lb @Temperature 73.4 °F |
Longitudinal |
Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 1.7 mm thick sheet Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
Charpy Impact | 8.00 J @Temperature 23.0 °C |
5.90 ft-lb @Temperature 73.4 °F |
Longitudinal |
Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 11.1 mm thick plate Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
Charpy Impact | 8.00 J @Temperature 23.0 °C |
5.90 ft-lb @Temperature 73.4 °F |
Longitudinal |
Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 15.9 mm thick plate Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
Charpy Impact | 8.00 J @Temperature 23.0 °C |
5.90 ft-lb @Temperature 73.4 °F |
Longitudinal |
Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 15.9 mm thick plate, aged 3 hours at 816°C Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
Charpy Impact | 8.00 J @Temperature 23.0 °C |
5.90 ft-lb @Temperature 73.4 °F |
Longitudinal |
Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 4.8 mm thick sheet Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
Charpy Impact | 8.00 J @Temperature 23.0 °C |
5.90 ft-lb @Temperature 73.4 °F |
Longitudinal |
Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 7.9 mm thick plate Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
Charpy Impact | 8.00 J @Temperature 23.0 °C |
5.90 ft-lb @Temperature 73.4 °F |
Longitudinal |
Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 7.9 mm thick plate, aged 3 hours at 816°C Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
Charpy Impact | 8.00 J @Temperature 23.0 °C |
5.90 ft-lb @Temperature 73.4 °F |
Longitudinal |
Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 3.2 mm thick sheet Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
Charpy Impact | 8.00 J @Temperature 23.0 °C |
5.90 ft-lb @Temperature 73.4 °F |
Longitudinal |
Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 11.1 mm thick plate, aged 3 hours at 816°C Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
Charpy Impact | 8.00 - 16.0 J @Temperature -20.0 °C |
5.90 - 11.8 ft-lb @Temperature -4.00 °F |
Transverse |
Bisalloy Steels BisPlate HHA Thickness 5-25 mm A quenched and tempered steel armor plate suitable for use in both military and civil applications where light weight and resistance to ballistic projectiles is required. |