Mechanical Properties	Metric	English	Comments
Compressive Yield Strength	7.00 MPa	1020 psi	Typical; ASTM C365
Parabeam Industrie ParaTank 4.5 3D Glass Fabric Parabeam® 3D Glass Fabric is a fabric woven out of a 100% E-glass yarn and consists of two decklayers bonded together by vertical piles in a sandwich structure. These piles are woven into the deckl..
Compressive Yield Strength	7.00 - 23.4 MPa	1020 - 3400 psi	Average value: 11.7 MPa Grade Count:7
Overview of materials for Polytetrafluoroethylene (PTFE), Conductive Carbon Filled This property data is a summary of similar materials in the MatWeb database for the category "Polytetrafluoroethylene (PTFE), Conductive Carbon Filled". Each property range of values reported is min..
Compressive Yield Strength	7.00 - 100 MPa	1020 - 14500 psi	Average value: 46.3 MPa Grade Count:6
Overview of materials for Nylon 66, Unreinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Unreinforced". Each property range of values reported is minimum and maximum values of appropr..
Compressive Yield Strength	7.00 - 9.00 MPa @Strain 1.00 %	1020 - 1310 psi @Strain 1.00 %	ASTM D695
Guarniflon PTFE G416 Polytetrafluoroethylene 40% Bronze, 2% Carbon PTFE G Special Compound with bronze Properties: Enhanced compressive strength. Good wear resistance and high thermal conductivity.Application: Unlubricated bearings for high speed excluding hard ..
Compressive Yield Strength	7.00 - 9.00 MPa @Strain 1.00 %	1020 - 1310 psi @Strain 1.00 %	ASTM D695
Guarniflon PTFE G453 Polytetrafluoroethylene 25% Carbographite PTFE G Standard Compound with carbon..Properties: Good thermal and electrical conductivity. Good resistance to deformation. Excellent resistance to load with low coefficient of friction and high ..
Compressive Yield Strength	7.00 - 11.0 MPa @Strain 1.00 %	1020 - 1600 psi @Strain 1.00 %	ASTM D695
Guarniflon PTFE G456 Polytetrafluoroethylene 25% Hard Carbon PTFE G Special Compound with carbon..Properties: Good thermal and electrical conductivity. Good resistance to deformation. Excellent resistance to load with low coefficient of friction and high w..
Compressive Yield Strength	7.00 - 9.00 MPa @Strain 1.00 %	1020 - 1310 psi @Strain 1.00 %	ASTM D695
Guarniflon PTFE G415 Polytetrafluoroethylene 25% Soft Carbon PTFE G Standard Compound with carbon..Properties: Good thermal and electrical conductivity. Good resistance to deformation. Excellent resistance to load with low coefficient of friction and high ..
Compressive Yield Strength	7.03 MPa	1020 psi	Stabilized, typ
Hexcel® HexWeb® CR III 1/8-5052-.0015 Corrosion Resistant Specification Grade Aluminum Honeycomb Grade is designated as "Cell Size-Alloy-Foil Gauge."5052 and 5056 expanded aerospace grade aluminum honeycomb materials are available in a wide selection of cell sizes and foil gauges. The HexWeb CR..
Compressive Yield Strength	7.03 MPa	1020 psi	Stabilized, typ
Hexcel® HexWeb® CR-PAA™ 1/8-5052-0.0015 Phosphoric Acid Anodized Aluminum Honeycomb Grade is designated as "Cell Size-Alloy-Foil Gauge." The life cycle of aluminum honeycomb sandwich structures in a given application can be directly related to the quality of the bond between the fa..
Compressive Yield Strength	7.03 MPa	1020 psi	Stabilized, typ
Hexcel® HexWeb® HRH-10 - 3/16 - 6.0 Aramid Fiber/Phenolic Resin Honeycomb Designation: Material-Cell Size-Density.Hexweb HRH-10 is manufactured from NOMEX aramid fiber sheets. A thermosetting adhesive is used to bond these sheets at the nodes, and after expanding to the h..