Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Compressive Yield Strength | 100 - 207 MPa | 14500 - 30000 psi | Average value: 155 MPa Grade Count:4 |
Overview of materials for Polyphthalamide (PPA), 20% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polyphthalamide, 20% Glass Fiber Reinforced". Specific grades with glass content between 15% and 24% are.. |
|||
Compressive Yield Strength | 34.0 - 207 MPa | 4930 - 30000 psi | Average value: 106 MPa Grade Count:6 |
Overview of materials for Polyamide-Imide, Molded This property data is a summary of similar materials in the MatWeb database for the category "Polyamide-Imide, Molded". Each property range of values reported is minimum and maximum values of approp.. |
|||
Compressive Yield Strength | 103 - 207 MPa | 15000 - 30000 psi | Average value: 157 MPa Grade Count:13 |
Overview of materials for Nylon 66, 20% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 20% Glass Fiber Filled". Specific grades with glass content between 15% and 24% are included. .. |
|||
Compressive Yield Strength | 103 - 207 MPa | 14900 - 30000 psi | Average value: 172 MPa Grade Count:3 |
Overview of materials for PEKK, Unreinforced This property data is a summary of similar materials in the MatWeb database for the category "PEKK, Unreinforced". Each property range of values reported is minimum and maximum values of appropriate.. |