Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Compressive Yield Strength | 7.00 MPa | 1020 psi | Typical; ASTM C365 |
Parabeam Industrie ParaTank 4.5 3D Glass Fabric Parabeam® 3D Glass Fabric is a fabric woven out of a 100% E-glass yarn and consists of two decklayers bonded together by vertical piles in a sandwich structure. These piles are woven into the deckl.. |
|||
Compressive Yield Strength | 7.00 - 23.4 MPa | 1020 - 3400 psi | Average value: 11.7 MPa Grade Count:7 |
Overview of materials for Polytetrafluoroethylene (PTFE), Conductive Carbon Filled This property data is a summary of similar materials in the MatWeb database for the category "Polytetrafluoroethylene (PTFE), Conductive Carbon Filled". Each property range of values reported is min.. |
|||
Compressive Yield Strength | 7.00 - 100 MPa | 1020 - 14500 psi | Average value: 46.3 MPa Grade Count:6 |
Overview of materials for Nylon 66, Unreinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Unreinforced". Each property range of values reported is minimum and maximum values of appropr.. |
|||
Compressive Yield Strength | 7.00 - 9.00 MPa @Strain 1.00 % |
1020 - 1310 psi @Strain 1.00 % |
ASTM D695 |
Guarniflon PTFE G416 Polytetrafluoroethylene 40% Bronze, 2% Carbon PTFE G Special Compound with bronze Properties: Enhanced compressive strength. Good wear resistance and high thermal conductivity.Application: Unlubricated bearings for high speed excluding hard .. |
|||
Compressive Yield Strength | 7.00 - 9.00 MPa @Strain 1.00 % |
1020 - 1310 psi @Strain 1.00 % |
ASTM D695 |
Guarniflon PTFE G453 Polytetrafluoroethylene 25% Carbographite PTFE G Standard Compound with carbon..Properties: Good thermal and electrical conductivity. Good resistance to deformation. Excellent resistance to load with low coefficient of friction and high .. |
|||
Compressive Yield Strength | 7.00 - 11.0 MPa @Strain 1.00 % |
1020 - 1600 psi @Strain 1.00 % |
ASTM D695 |
Guarniflon PTFE G456 Polytetrafluoroethylene 25% Hard Carbon PTFE G Special Compound with carbon..Properties: Good thermal and electrical conductivity. Good resistance to deformation. Excellent resistance to load with low coefficient of friction and high w.. |
|||
Compressive Yield Strength | 7.00 - 9.00 MPa @Strain 1.00 % |
1020 - 1310 psi @Strain 1.00 % |
ASTM D695 |
Guarniflon PTFE G415 Polytetrafluoroethylene 25% Soft Carbon PTFE G Standard Compound with carbon..Properties: Good thermal and electrical conductivity. Good resistance to deformation. Excellent resistance to load with low coefficient of friction and high .. |