Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 61.0 MPa | 8850 psi | ASTM D790-92 |
Multibase Multi-Pro® 2005 XRC Black 20% Filler Content Polypropylene Multi-Pro 2005 XRC is specifically designed for injection molded electronic industrial uses. This product shows higher heat distortion and notched izod than typical glass filled polypropylene. Thi.. |
|||
Flexural Strength | <= 61.0 MPa | <= 8850 psi | ISO 178 |
Polykemi AB POLYshine PBT D241 PBT, Impact Modified Information provided by Polykemi AB |
|||
Flexural Strength | 61.0 MPa | 8850 psi | ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP AL003 ABS (Europe-Africa-Middle East) LNP LUBRICOMP* AL003 is a compound based on Acrylonitrile Butadiene Styrene resin containing PTFE. Added features of this material include: Internally Lubricated. |
|||
Flexural Strength | 61.0 MPa | 8850 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP AI0019 ABS (Europe-Africa-Middle East) LNP* Lubricomp* AI0019 is a compound based on Acrylonitrile Butadiene Styrene resin containing Flame Retardant, Silicone. Added features of this material include: Flame Retardant. |
|||
Flexural Strength | 61.0 MPa | 8850 psi | ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP AL003 ABS (Asia Pacific) LNP LUBRICOMP* AL003 is a compound based on Acrylonitrile Butadiene Styrene resin containing PTFE. Added features of this material include: Internally Lubricated. |
|||
Flexural Strength | 61.0 MPa | 8850 psi | ASTM D790 |
LG Chemical LUCEL HI-515 High Impact POM, Unreinforced LUCEL semi-crystalline acetal copolymer resins are produced by gas phase polymerization. LUCEL resins can be widely accepted as the replacement of thermosets, aluminum and zinc die-casts or other m.. |
|||
Flexural Strength | 61.0 MPa | 8850 psi | ISO 178 |
Lucite International Diakon® Rapide CLG 910B Enhanced Molding Acrylic Polymer Specially designed to reduce injection molding cycle times and therefore provide production cost benefits.Information provided by Lucite International |
|||
Flexural Strength | 61.0 MPa | 8850 psi | ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP DP003EH PC LNP LUBRICOMP* DP003EH is a compound based on Polycarbonate resin containing 15% PTFE/Silicone. Added features of this material include: Easy Molding, Internally Lubricated, Healthcare. |
|||
Flexural Strength | 61.0 MPa | 8850 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP KAL22 Acetal Copolymer (Europe-Africa-Middle East) LNP* Lubricomp* KAL22 is a compound based on Acetal Copolymer resin containing PTFE, Aramid Fiber. |
|||
Flexural Strength | 61.0 MPa | 8850 psi | ISO 178 |
Solvay TECHNYL® A 50H1 PA66, Conditioned Description: Flame retardant polyamide 66, unreinforced, heat stabilized, for injection molding.Available in: Asia Pacific, Europe, Latin America and North AmericaProduct Applications: This phospho.. |
|||
Flexural Strength | 61.0 MPa | 8850 psi | ASTM D790 |
SABIC Innovative Plastics LNP STAT-KON AX00756 ABS LNP STAT-KON* AX00756 is a compound based on ABS resin containing Stainless Steel. Added feature of this material is: Electrically Conductive. |
|||
Flexural Strength | 61.0 MPa | 8850 psi | ISO 178 |
SABIC Innovative Plastics LNP STAT-KON RX08408 PA 66 LNP* STAT-KON* RX08404 is a compound based on Nylon 66 containing Carbon Powder. Added features of this material include: Electrically Conductive, High Impact. |
|||
Flexural Strength | 61.0 MPa | 8850 psi | ISO 178 |
SABIC Innovative Plastics LNP Stat-kon RX08408_NA1D004 PA 66 LNP* Stat-Kon* RX08404_NA1D004 is a compound based on Nylon 66 containing Carbon Powder. Characteristics of this grade include: Electrically Conductive, High Impact.This data was supplied by SABI.. |
|||
Flexural Strength | 61.0 MPa | 8850 psi | ISO 178 |
SABIC Innovative Plastics LNP STAT-LOY AF3009 ABS (Asia Pacific) LNP* Stat-loy* AF3009 is a compound based on Acrylonitrile Butadiene Styrene resin containing Glass Fiber, Flame Retardant. Added features of this material include: Antistat, Flame Retardant. |
|||
Flexural Strength | 61.0 MPa | 8850 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP HH0420A PA11 LNP* THERMOCOMP* HH0420A is a compound based on Nylon 11 containing proprietary fillers. Added features of this material are High Specific Gravity. |
|||
Flexural Strength | 61.0 MPa | 8850 psi | ISO 178 |
SABIC Innovative Plastics LNP STAT-LOY W3000XXJ PBT LNP* STAT-LOY* W3000XXJ is a compound based on PBT. Added features of this grade include: Anti-Stat, Colorable, Healthcare |
|||
Flexural Strength | 61.0 MPa | 8850 psi | Method 1, .05"/min; ASTM D790 |
Stratasys® ABS-M30 ABS-M30 is 25-70 percent stronger than standard Stratasys ABS and is an ideal material for conceptual prototyping, design verification, and direct digital manufacturing. ABS-M30 has greater tensile,.. |
|||
Flexural Strength | 61.0 MPa | 8850 psi | ASTM D790 |
UBE UBESTA® 3035LU1 Rigid Piping Grade Nylon 12 Description: UBESTA contributes to the field of Utilities such as plastic pipe system evolutionary developed for gas industry. It is used for both burial and for rehabilitation of existing cast iron.. |
|||
Flexural Strength | 61.0 MPa @Temperature 23.0 °C |
8850 psi @Temperature 73.4 °F |
EN ISO 178 |
Ensinger TECASINT™ 2062 Polyimide, Anthrazit Gleamy, 15% Graphite, 10% PTFE (PI) TECASINT™ 2000 series of polyimide stock shapes provide a superior combination of high temperature and bearing and wear, properties that make it an ideal choice for the most demanding applications... |
|||
Flexural Strength | 61.0 MPa | 8850 psi | ASTM D790 |
Diamond Polymers NYLON 6615 Black, Super Tough Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc. |
|||
Flexural Strength | 61.0 MPa | 8850 psi | 2 mm/min; ISO 178 |
Chi Mei Polylac® PA-756S ABS - High Flow Super high flow, medium impact |
|||
Flexural Strength | 61.0 MPa | 8850 psi | Dry; ISO 178 |
Arkema Group Orgalloy® RS 60E10 Polyamide Alloy Polyamide Alloy, Rigid Blown film gradeTubes / Mandrels / Profiles / CablesInformation provided by Arkema Group |
|||
Flexural Strength | 61.0 MPa | 8850 psi | ISO 178 |
Azoty Tarnow™ TARNOFORM 300 LS POM Injection molding grade based on Tarnoform 300 modified with soluble light stabilizers improving weathering stability.Information provided by Zakłady Azotowe w Tarnowie-Moscicach S.A. |
|||
Flexural Strength | 61.0 MPa | 8850 psi | ISO 178 |
Azoty Tarnow™ TARNOFORM 300 POM Basic, fast cycling injection molding grade suitable for many applications.Information provided by Zakłady Azotowe w Tarnowie-Moscicach S.A. |
|||
Flexural Strength | 61.0 MPa | 8850 psi | ISO 178 |
Azoty Tarnow™ TARNOFORM 300 UV POM Injection molding grade based on Tarnoform 300 modified with carbon black giving best weathering stability.Information provided by Zakłady Azotowe w Tarnowie-Moscicach S.A. |
|||
Flexural Strength | 61.0 MPa | 8850 psi | ISO 178 |
Azoty Tarnow™ TARNOFORM 500 UV POM High flow injection molding grade based on Tarnoform 500 modified with carbon black giving best weathering stability.Information provided by Zakłady Azotowe w Tarnowie-Moscicach S.A. |
|||
Flexural Strength | 61.0 MPa | 8850 psi | ASTM D790 |
A. Schulman ComAlloy Comtuf® 420 Polyester - PBT, High Impact Modified Data provided by the manufacturer, ComAlloy International Company. Superior toughness and impact resistance characterize Comtuf® materialsThe ComAlloy product line has been integrated into the A Sc.. |
|||
Flexural Strength | 61.0 MPa | 8850 psi | ASTM D790 |
Aclo Accutech Polypropylene Copolymer CP0436G20M10CL Glass/Mineral Reinforced Coupled |
|||
Flexural Strength | 61.0 MPa | 8850 psi | ASTM D790 |
Plaskolite West Optix® CA-1000 E Impact Modified Acrylic Resin Extrusion Grade Pellets. Excellent blend stock material for impact applications. |