Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | <= 43.0 MPa | <= 6240 psi | ISO 178 |
Polykemi AB POLYfill PP CIP16020FCS Polypropylene, Fast Cycle Information provided by Polykemi AB |
|||
Flexural Strength | <= 43.0 MPa | <= 6240 psi | ISO 178 |
Polykemi AB POLYfill PPC T1030 Polypropylene Copolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
Flexural Strength | <= 43.0 MPa | <= 6240 psi | ISO 178 |
Polykemi AB POLYfill PP TOUCH 25325 Polypropylene, Glass Fiber Reinforced Information provided by Polykemi AB |
|||
Flexural Strength | <= 43.0 MPa | <= 6240 psi | ISO 178 |
Polykemi AB POLYfill PP TOUCH 25325 R3 Polypropylene, Glass Fiber Reinforced, Scratch Resistant Information provided by Polykemi AB |
|||
Flexural Strength | <= 43.0 MPa | <= 6240 psi | ISO 178 |
Polykemi AB POLYfill PPC BGK601213 CR Polypropylene Copolymer, Multifiller Information provided by Polykemi AB |
|||
Flexural Strength | 43.0 MPa | 6240 psi | 2 mm/min; ISO 178 |
Ineos ABS Lustran® ABS E112LG Pellets Lustran® ABS E112LG is extrusion grade for low gloss surfaces. It is used for the production of molded plastic articles. |
|||
Flexural Strength | 43.0 MPa | 6240 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP KB006 Acetal LNP* THERMOCOMP* KB006 is a compound based on Acetal containing 30% Glass Bead. |
|||
Flexural Strength | 43.0 MPa | 6240 psi | |
Borealis HK030U Polypropylene Compound HK030U is a special low viscosity polypropylene compound developed to fit the production of PP-GF composites in the direct LFT compression and injection molding process as well as in combination wit.. |
|||
Flexural Strength | 43.0 MPa | 6240 psi | ASTM D790 |
A. Schulman POLYFLAM™ FLP 3714 20% Glass Filled HDPE DescriptionPolyfort® FLP 3714 is a 20% glass filled HDPE product. Information provided by A. Schulman. |
|||
Flexural Strength | 43.0 MPa | 6240 psi | ISO 178 |
Unitika A125 PA66, Conditioned Information provided by Unitika Ltd. |
|||
Flexural Strength | 43.0 MPa | 6240 psi | ASTM D790 |
A. Schulman POLYFLAM™ FLP 3714 20% Glass Filled HDPE DescriptionPolyfort® FLP 3714 is a 20% glass filled HDPE product. Information provided by A. Schulman. |
|||
Flexural Strength | 43.0 MPa | 6240 psi | ASTM D790 |
A. Schulman POLYFLAM™ FLP 3714 20% Glass Filled HDPE DescriptionPolyfort® FLP 3714 is a 20% glass filled HDPE product. Information provided by A. Schulman. |
|||
Flexural Strength | 43.0 MPa | 6240 psi | ASTM D790 |
A. Schulman POLYFORT™ FPP 3452 Mineral Filled Copolymer Polypropylene DescriptionPolyfort® FPP 3452 is a 30% mineral filled copolymer polypropylene.Information provided by A. Schulman. |
|||
Flexural Strength | 43.0 MPa | 6240 psi | ASTM D790 |
A. Schulman POLYFORT™ FPP 3452 Mineral Filled Copolymer Polypropylene DescriptionPolyfort® FPP 3452 is a 30% mineral filled copolymer polypropylene.Information provided by A. Schulman. |
|||
Flexural Strength | 43.0 MPa | 6240 psi | ASTM D790 |
A. Schulman POLYFORT™ FPP 3452 Mineral Filled Copolymer Polypropylene DescriptionPolyfort® FPP 3452 is a 30% mineral filled copolymer polypropylene.Information provided by A. Schulman. |
|||
Flexural Strength | 43.0 MPa | 6240 psi | ASTM D790 |
A. Schulman POLYFLAM™ FLP 3714 20% Glass Filled HDPE DescriptionPolyfort® FLP 3714 is a 20% glass filled HDPE product. Information provided by A. Schulman. |
|||
Flexural Strength | 43.0 MPa | 6240 psi | ASTM D790 |
A. Schulman POLYFLAM™ FLP 3714 20% Glass Filled HDPE DescriptionPolyfort® FLP 3714 is a 20% glass filled HDPE product. Information provided by A. Schulman. |
|||
Flexural Strength | 43.0 MPa | 6240 psi | ASTM D790 |
Goodfellow TPX® DX231 Coating/Extrusion Grade Polymethylpentene This grade is highly recommended for paper coating or for fiber extrusion.TPX® is semi-crystalline, transparent, very light and - for a polyolefin - expensive. It has good release characteristics a.. |
|||
Flexural Strength | 43.0 MPa | 6240 psi | 2 mm/min, 4 mm; ISO 178 |
Chi Mei Kibiton® PB-5925 SBC Transparency, high stiffness, injection grade |
|||
Flexural Strength | 43.0 MPa | 6240 psi | ASTM D790 |
Aclo Accutech Polypropylene Homopolymer HP0336M10CL Mica Reinforced Coupled |
|||
Flexural Strength | 43.0 MPa | 6240 psi | ASTM D790 |
Aclo Accutech Polypropylene Homopolymer HP0339W40L1 Wollastonite Reinforced |
|||
Flexural Strength | 43.0 MPa | 6240 psi | ISO 178 |
Ascend Performance Materials Vydyne® M344 Nylon 66/6, ignition resistant, Conditioned Vydyne® M344 is a halogenated, unfilled, flame-retardant PA66/6 copolymer designed with excellent strength and toughness. It is lubricated for machine feed and easy mold release and has an Underwri.. |
|||
Flexural Strength | 43.0 MPa | 6240 psi | ASTM D790 |
Teknor Apex Sinpolene CPP1020 Polypropylene Availability: Africa & Middle East; Latin America; Asia Pacific; South America Calcium Carbonate Filler, 20% Filler by Weight Features: Homopolymer Uses: Appliance Components; Furniture; Housings F.. |
|||
Flexural Strength | 43.0 MPa | 6240 psi | |
Plastcom SLOVALEN PH 82 T 20 PP, 20% mineral filling FeaturesModified homopolymer PP for injection moulding with the content of 20% mineral filling. Increased rigidity, strength and thermal use up to 130°C depending on the talc conte nt. Decreased sh.. |
|||
Flexural Strength | 43.0 MPa | 6240 psi | ASTM D790 |
A. Schulman POLYFORT™ FPP 3452 Mineral Filled Copolymer Polypropylene DescriptionPolyfort® FPP 3452 is a 30% mineral filled copolymer polypropylene.Information provided by A. Schulman. |
|||
Flexural Strength | 43.0 MPa | 6240 psi | ASTM D790 |
Reliance Industries PVAXX H60 The key property of all PVAXX polymer is this product`s unique capacity to biodegrade into non-toxic residues under both aerobic and non-aerobic conditions.Information provided by Reliance Industrie.. |
|||
Flexural Strength | 43.0 MPa | 6240 psi | ISO 178 |
Ascend Performance Materials Vydyne® M344 BLK Nylon 66, Flame Retardant, Conditioned Vydyne® M344 BLK is a halogenated, unfilled, flame-retardant PA66/6 copolymer designed with excellent strength and toughness. It is lubricated for machine feed and easy mold release and has Underwr.. |
|||
Flexural Strength | 43.0 MPa | 6240 psi | ISO 178 |
SABIC Innovative Plastics LNP STAT-KON MFD02 PP LNP* STAT-KON* MFD02 is a compound based on Polypropylene resin containing 10% Glass Fiber. Added features of this material include: Electrically Conductive. |
|||
Flexural Strength | 43.0 MPa | 6240 psi | ISO 178 |
SABIC Innovative Plastics LNP STAT-KON MFD02 PP (Asia Pacific) LNP* Stat-kon* MFD02 is a compound based on Polypropylene resin containing Glass Fiber, Carbon Powder. Added features of this material include: Electrically Conductive. |