Polymer Property : Flexural Strength = 39000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Strength	269 MPa	39000 psi	ASTM D790
Oxford Polymers Oxnilon 6-33GF 33% Glass Fiber Filled Nylon 6 for Injection Molding 33% Glass Fiber Filled Nylon 6 for Injection MoldingInformation provided by Oxford Polymers.
Flexural Strength	269 MPa	39000 psi	ASTM D790
Polymer Resources NY6/12-G43 Nylon 612, 43% Glass Reinforced Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades are tested dry as molded (DAM).Information provide..
Flexural Strength	269 MPa	39000 psi	ASTM D790
LNP Thermocomp® EF-1006 BK8-114 Polyetherimide, Glass Fiber Reinforcement (discontinued **) Forms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names..
Flexural Strength	269 MPa	39000 psi
Premix Premi-Glas® 1200-50VE 1200-50 VE SMC (discontinued **) Description: Premi-Glas® 1200-50 VE is a sheet molding compound.Market: StructuralInformation provided by Premix.
Flexural Strength	269 MPa	39000 psi	ISO 178
SABIC Innovative Plastics LNP LUBRICOMP OCL36EXP PPS - LINEAR LNP* LUBRICOMP* OCL36EXP is a compound based on Linear PPS containing 30% Carbon Fiber, 15% PTFE. Added features of this grade include; Wear Resistant, Electrically Conductive.
Flexural Strength	269 MPa	39000 psi	ASTM D790
Solvay Specialty Polymers RytonÂ® BR42B Polyphenylene Sulfide (PPS), 40% Glass Fiber RytonÂ® BR42B 40% glass fiber reinforced polyphenylene sulfide compound is specially formulated to provide low coefficient of friction and reduced wear rate for use in applications requiring low s..
Flexural Strength	269 MPa	39000 psi	ASTM D790
Solvay Specialty Polymers RytonÂ® R-4-200NA Polyphenylene Sulfide (PPS), 40% Glass Fiber RytonÂ® R-4-200NA and R-4-200BL 40% glass fiber reinforced polyphenylene sulfide compounds provide enhanced mechanical strength and low maintenance molding using conventional molding equipmentFeat..
Flexural Strength	269 MPa	39000 psi	ASTM D790
Solvay Specialty Polymers RytonÂ® R-4-222NA Polyphenylene Sulfide (PPS), 40% Glass Fiber RytonÂ® R-4-222NA 40% glass fiber reinforced polyphenylene sulfide compound provides enhanced mechanical strength after constant or repeated exposure to high temperature water and complies with Un..
Flexural Strength	269 MPa	39000 psi	ASTM D790
Techmer ES HiFillÂ® PA4/6 GF30 TL15 30% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 30% Filler by WeightAdditive: Heat Stabilizer and PTFE LubricantFeatures: Heat Stabilized and LubricatedInfo..
Flexural Strength	269 MPa	39000 psi	ASTM D790
Techmer ES HiFillÂ® PA4/6 GF33 TL15 33% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 33% Filler by WeightAdditive: Heat Stabilizer and PTFE LubricantFeatures: Heat Stabilized and LubricatedInfo..
Flexural Strength	269 MPa	39000 psi	ASTM D790
Techmer ES HiFillÂ® PA6 GF50 HS L 50% Glass Filled (Conditioned) Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 50% Filler by WeightAdditive: Lubricant and Heat StabilizerFeatures: Lubricated and Heat StabilizerInformati..
Flexural Strength	269 MPa	39000 psi	ASTM D790
Techmer ES HiFillÂ® PA6 GF50 L 50% Glass Filled (Conditioned) Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 50% Filler by WeightAdditive: LubricantFeatures: LubricatedInformation provided by TP Composites, Inc.
Flexural Strength	269 MPa	39000 psi	ASTM D790
Techmer ES LuriblendÂ® PA6/6 GF43 ML2 43% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 43% Filler by WeightAdditive: Molybdenum Disulfide Lubricant(2%)Features: LubricatedInformation provided by TP Composites,..
Flexural Strength	269 MPa	39000 psi	ASTM D790
Techmer ES LuriblendÂ® PA6/6 GF43 ML2 BK 43% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 43% Filler by WeightAdditive: Molybdenum Disulfide Lubricant(2%)Features: Lubricated Appearance: BlackTPCI# 8047101Informa..
Flexural Strength	269 MPa	39000 psi	ISO 178
SABIC Innovative Plastics LNP THERMOCOMP EC006 PEI LNP THERMOCOMP* EC006 is a compound based on Polyetherimide resin containing 30% Carbon Fiber. Added features of this material include: Electrically Conductive.
Flexural Strength	269 MPa	39000 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP STAT-KON OE006C1 PPS - Linear LNP* STAT-KON* OE006C1 is a compound based on PPS - Linear resin containing 30% Carbon Fiber. Added features of this material include: Electrically Conductive.
Flexural Strength	269 MPa	39000 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP STAT-KON RE0069S PA 66 LNP* STAT-KON* RE0069S is a compound based on Nylon 66 resin containing 30% Carbon Fiber. Added features of this material include: Electrically Conductive, Flame Retardant, Heat Stabilized.
Flexural Strength	269 MPa	39000 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP THERMOCOMP RC004SXS PA 66 (Europe-Africa-Middle East) LNP* Thermocomp* RC004SXS is a compound based on PA 66 resin containing Carbon Fiber. Added features include; Heat Stabilized, Electrically Conductive.
Flexural Strength	269 MPa	39000 psi	ASTM D790
Chase Plastics CP Pryme® N130GL (DAM) Nylon 6, 30% Glass Fiber Reinforced, Internally Lubricated Information provided by Chase Plastics.
Flexural Strength	269 MPa	39000 psi	ASTM D790
Ashley Polymers Ashlene® 528L-40G Nylon 66, 40% Glass Reinforced A general purpose 40% glass reinforced Nylon 66 resin.Data provided by the manufacturer
Flexural Strength	269 MPa	39000 psi	ASTM D790
PolyOne Edgetek® AM-20CF/000 Polyphthalamide (PPA), Carbon Fiber Reinforced (discontinued **) Description/Features:Carbon Fiber ReinforcedPolyOne First ChoiceInformation provided by PolyOne Corporation.
Flexural Strength	269 MPa @Temperature 23.0 °C	39000 psi @Temperature 73.4 °F	ISO 178
Solvay Specialty Polymers Amodel® A-4133 L Polyphthalamide (PPA), Dry (discontinued **) Amodel A-4133L polyphthalamide (PPA) is a 33% glass reinforced resin designed to offer high crystallinity when molded in water-cooled molds. Key properties include high heat resistance, reduced outg..