Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 262 MPa | 38000 psi | ASTM D790 |
Ravago Manufacturing Americas Hylon® N1033HL Nylon 6/6 (DAM) Information provided by Ravago. |
|||
Flexural Strength | 262 MPa | 38000 psi | ASTM D790 |
LNP Thermocomp® LF-1006 EM Polyetheretherketone, Glass Fiber Reinforcement
(discontinued **) Features: Good MoldabilityForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are st.. |
|||
Flexural Strength | 262 MPa | 38000 psi | ISO 178 |
Ravago Manufacturing Americas Hylon® N1030HL Nylon 6/6
(discontinued **) Available in North America Filler: Glass Fiber Reinforcement, 30% Filler by WeightAdditive: Heat Stabilizer and Lubricant Features: Lubricated and Heat StabilizedAuto Specifications: GM GMW3038P-PA.. |
|||
Flexural Strength | 262 MPa | 38000 psi | ASTM D790 |
Ravago Manufacturing Americas Hylon® N1033L Nylon 6/6 (DAM)
(discontinued **) Information provided by Ravago. |
|||
Flexural Strength | 262 MPa | 38000 psi | ASTM D790 |
IDI Composites M-209 Thermoset Polyester, Sheet MECHANICAL - Versatile family of compounds designed to meet a variety of mechanical, electro-mechanical, and corrosion applications. Outstanding structural properties at lowest possible costs.Data p.. |
|||
Flexural Strength | 262 MPa | 38000 psi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP LCL33 PEEK LNP* LUBRICOMP* LCL33 is a compound based on Polyetheretherketone resin containing 15% Carbon Fiber, 15% PTFE. Added features of this material include: Wear Resistant. |
|||
Flexural Strength | 262 MPa | 38000 psi | ASTM D790 |
Solvay Specialty Polymers Ryton® R-4-240NA Polyphenylene Sulfide (PPS), 40% Glass Fiber Ryton® R-4-240NA and R-4-240BL 40% glass fiber reinforced polyphenylene sulfide compounds provide enhanced mechanical strength and toughness compared to other polyphenylene sulfide compounds.Feat.. |
|||
Flexural Strength | 262 MPa | 38000 psi | ASTM D790 |
SABIC Innovative Plastics LNP STAT-KON OE008A PPS - Branched LNP* STAT-KON* OE008A is a compound based on PPS - Branched resin containing 40% Carbon Fiber. Added feature of this grade is: Electrically Conductive. |
|||
Flexural Strength | 262 MPa | 38000 psi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP EX93452 PEI (Asia Pacific) LNP* THERMOCOMP* EX93452 is a compound based on Polyetherimide resin containing Carbon Fiber. Added features of this material include: Electrically Conductive. |
|||
Flexural Strength | 262 MPa | 38000 psi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP IC006 PA 6/12 (Asia Pacific) LNP* Thermocomp* IC006 is a compound based on Nylon 6/12 resin containing Carbon Fiber. Added features of this material include: Electrically Conductive. |
|||
Flexural Strength | 262 MPa | 38000 psi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP IX95700 PA6.12 LNP* THERMOCOMP* IX95700 is a compound based on Nylon 6/12 resin containing Glass Fiber. |
|||
Flexural Strength | 262 MPa | 38000 psi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP LF006E PEEK LNP* THERMOCOMP* LF006E is a compound based on Polyetheretherketone resin containing 30% Glass Fiber. Added features of this material include: Easy Molding. |
|||
Flexural Strength | 262 MPa | 38000 psi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP RF00AH PA 66 LNP* THERMOCOMP* RF00AH is a compound based on Nylon 66 resin containing 50% Glass Fiber. Added feature of this grade is: Healthcare. |
|||
Flexural Strength | 262 MPa | 38000 psi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP RF00AH PA 66 (Asia Pacific) LNP* Thermocomp* RF00AH is a compound based on Nylon 66 resin containing Glass Fiber. |
|||
Flexural Strength | 262 MPa | 38000 psi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP EF006H PEI (Asia Pacific) LNP* Thermocomp* EF006H is a compound based on Polyetherimide resin containing Glass Fiber. |
|||
Flexural Strength | 262 MPa | 38000 psi | 20 x 40 mm |
CeramTec 771 94% Alumina (Al2O3) Te value is 840°C. Hasselman Thermal Shock value is 200 K.Data provided by CeramTec North America. |
|||
Flexural Strength | 262 MPa | 38000 psi | ASTM D790 |
Chase Plastics CP Pryme® NN133GL (DAM) Nylon 66, 33% Glass Fiber Reinforced, Internally Lubricated Information provided by Chase Plastics. |
|||
Flexural Strength | 262 MPa | 38000 psi | ASTM D790 |
Chase Plastics CP Pryme® NN133GLUV (DAM) Nylon 66, 33% Glass Fiber Reinforced, Internally Lubricated, UV Stabilized Information provided by Chase Plastics. |
|||
Flexural Strength | 262 MPa | 38000 psi | ASTM D790 |
A. Schulman ComAlloy Lubrilon® 646 Nylon 6/12, Carbon Fiber/PTFE Reinforced Data provided by the manufacturer, ComAlloy International Company. High performance and excellent lubricity with minimal surface wear.The ComAlloy product line has been integrated into the A Schulma.. |