Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 227 MPa @Temperature 100 °C |
32900 psi @Temperature 212 °F |
ISO 178 |
Solvay Specialty Polymers Amodel® A-1133 HS Polyphthalamide (PPA)
(Unverified Data**) Amodel A-1133 HS is a 33% glass reinforced, heat stabilized polyphthalamide (PPA) with a high heat deflection temperature, high flexural modulus and high tensile strength. Excellent creep resistance.. |
|||
Flexural Strength | 227 MPa | 32900 psi | ISO 178 |
Solvay TECHNYL® R AR 130/GF Nylon 66, 30% glass fiber, DRY Description: TECHNYL® AR 130/GF is a polyamide 66, reinforced with 30% of glass fiber, heat stabilized, for injection molding. It contains recycled raw materials. This product is available in bla.. |
|||
Flexural Strength | 227 MPa | 32900 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
SABIC Innovative Plastics ULTEM 2200 PEI 20% Glass fiber filled, standard flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing. NSF 51 listing, WRAS certification in recognized colors. |
|||
Flexural Strength | 227 MPa | 32900 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
SABIC Innovative Plastics ULTEM 2200 PEI (Asia Pacific) 20% Glass fiber filled, standard flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing. NSF 51 listing, WRAS certification in recognized colors. |
|||
Flexural Strength | 227 MPa | 32900 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
SABIC Innovative Plastics ULTEM 2200R PEI 20% Glass fiber filled, standard flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming, UL94 V0 and 5VA listing. |
|||
Flexural Strength | 227 MPa | 32900 psi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP UFL269SA PPA LNP* Lubricomp* UFL269SA is a compound based on Polyphthalamide resin containing Glass Fiber, PTFE, Flame Retardant. Added features of this material include: Internally Lubricated, Heat Stabilized,.. |
|||
Flexural Strength | 227 MPa | 32900 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
SABIC Innovative Plastics ULTEM 2200R PEI (Asia Pacific) 20% Glass fiber filled, standard flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming, UL94 V0 and 5VA listing. |
|||
Flexural Strength | 227 MPa | 32900 psi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP UFL269SA PPA (Asia Pacific) LNP* Lubricomp* UFL269SA is a compound based on Polyphthalamide resin containing Glass Fiber, PTFE, Flame Retardant. Added features of this material include: Internally Lubricated, Heat Stabilized,.. |
|||
Flexural Strength | 227 MPa | 32900 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
SABIC Innovative Plastics ULTEM 2210 PEI 20% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing. |
|||
Flexural Strength | 227 MPa | 32900 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
SABIC Innovative Plastics ULTEM 2210 PEI (Asia Pacific) 20% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing. |
|||
Flexural Strength | 227 MPa | 32900 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
SABIC Innovative Plastics ULTEM 2210R PEI 20% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming, UL94 V0 and 5VA listing. |
|||
Flexural Strength | 227 MPa | 32900 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
SABIC Innovative Plastics ULTEM 2210R PEI (Asia Pacific) 20% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming, UL94 V0 and 5VA listing. |
|||
Flexural Strength | 227 MPa | 32900 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
SABIC Innovative Plastics ULTEM 2300 PEI 30% Glass fiber filled, standard flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing. NSF 51 listing, WRAS certification, KTW certification in recognized colors. |
|||
Flexural Strength | 227 MPa | 32900 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
SABIC Innovative Plastics ULTEM 2300 PEI (Asia Pacific) 30% Glass fiber filled, standard flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing. NSF 51 listing, WRAS certification, KTW certification in recognized colors. |
|||
Flexural Strength | 227 MPa | 32900 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
SABIC Innovative Plastics ULTEM 2300R PEI 30% Glass fiber filled, standard flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming, UL94 V0 and 5VA listing. |
|||
Flexural Strength | 227 MPa | 32900 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
SABIC Innovative Plastics ULTEM 2300R PEI (Asia Pacific) 30% Glass fiber filled, standard flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming, UL94 V0 and 5VA listing. |
|||
Flexural Strength | 227 MPa @Temperature 100 °C |
32900 psi @Temperature 212 °F |
4; ISO 178 |
Solvay Specialty Polymers Amodel® AE-1133 Polyphthalamide (PPA), 33% Glass Fiber Amodel® AE-1133 is a 33% glass reinforced, heat stabilized polyphthalamide (PPA) designed to work in the modern automotive electrical environment. It has a high heat deflection temperature, high .. |
|||
Flexural Strength | 227 MPa | 32900 psi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP IF007 PA 6/12 (Asia Pacific) LNP* THERMOCOMP* IF007 is a compound based on Nylon 6/12 resin containing Glass Fiber. |
|||
Flexural Strength | 227 MPa | 32900 psi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP PX85100 PA 6 LNP* THERMOCOMP* PX85100 is a compound based on Nylon 6 resin containing Proprietary Filler(s). |
|||
Flexural Strength | 227 MPa | 32900 psi | ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP QF007 PA 6/10 LNP* THERMOCOMP* QF007 is a compound based on Nylon 6/10 resin containing 35% Glass Fiber. |
|||
Flexural Strength | 227 MPa | 32900 psi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP RF006LXP PA 66 (Asia Pacific) LNP* Thermocomp* RF006LXP is a compound based on Nylon 66 resin containing Glass Fiber. Added features of this material include: Low Extractible. |
|||
Flexural Strength | 227 MPa | 32900 psi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP RX02743 PA 66 LNP* Thermocomp* RX02743 is a compound based on Nylon 66 resin containing Glass Fiber. |
|||
Flexural Strength | 227 MPa | 32900 psi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP RX02743 PA 66 (Asia Pacific) LNP* Thermocomp* RX02743 is a compound based on Nylon 66 resin containing Glass Fiber. |
|||
Flexural Strength | 227 MPa | 32900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP VF008A PA 66 LNP* THERMOCOMP* VF008A is a compound based on High Impact Nylon 66 containing 40% Glass Fiber. |
|||
Flexural Strength | 227 MPa @Temperature 100 °C |
32900 psi @Temperature 212 °F |
4; ISO 178 |
Solvay Specialty Polymers Amodel® A-1133 HS Polyphthalamide (PPA), 33% Glass Fiber (Dry) Amodel® A-1133 HS is a 33% glass reinforced, heat stabilized polyphthalamide (PPA) with a high heat deflection temperature, high flexural modulus and high tensile strength. Excellent creep resist.. |
|||
Flexural Strength | 227 MPa | 32900 psi | |
Sumitomo Bakelite Durez® 32633 Glass Filled Phenolic, Injection Grade Durez 32633 Black Phenolic is a two-stage, glass filled, special purpose molding compound. It is designed for applications requiring high physical strengths, dimensional stability, and heat resista.. |
|||
Flexural Strength | 227 MPa | 32900 psi | ASTM D790 |
Sumitomo Bakelite Sumikon® PM-9640 Glass Filled Phenolic Two stage glass fiber filled black phenolic. It is especially designed for applications requiring high strength and dimensional stability with excellent heat resistance. PM-9640 is widely used in .. |
|||
Flexural Strength | 227 MPa | 32900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP 9X11427 LNP* THERMOCOMP* 9X11427 is a compound based on Miscellanbeous resin containing 40% specialty glass filled TP alloy. Added features of this grade include: Ultra-Stiff Toughness, Improved Impact, G.. |
|||
Flexural Strength | 227 MPa | 32900 psi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP IF007 PA6.12 LNP THERMOCOMP* IF007 is a compound based on Nylon 6/12 resin containing 35% Glass Fiber. |