Polymer Property : Flexural Strength = 24900 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Strength	172 MPa	24900 psi	STN EN ISO 178
Plastcom SLOVAMID 6 GF 15 Polyamide 6, 15% Glass Fiber FeaturesPA 6 for injection moulding, chemically reinforced with 15% glass fiber. Application: impacted mouldings and mouldings with high strength applied in automotive, electrical, engineering and ..
Flexural Strength	172 MPa	24900 psi	Three Point Bend
Osprey Metals CE11 Al-Si Controlled Expansion Alloy Al-50%Si controlled expansion alloy manufactured and patented by Osprey Metals Ltd.Information provided to MatWeb by Osprey Metals.
Flexural Strength	172 MPa	24900 psi
Pyrotek TS-107 Thermoset Electrical Insulation Product (Nema Grade: G-7) Glass reinforcement, Silicone resin, White color. High temperature resistance. Good electrical properties in humidity.ApplicationsSuperstructure support pads Bus bar insulators Pot cradle insulato..
Flexural Strength	172 MPa	24900 psi	STN EN ISO 178
Plastcom SLOVAMID 6 GF 10 FRG 5 Polyamide 6, 10% Glass Fiber, Flame Retardant FeaturesPA 6 for injection moulding, chemically strengthened with 10% glass fiber. Application: impacted mouldings with high strength applied in automotive, electrical, engineering and consumer-goo..
Flexural Strength	172 MPa	24900 psi	ASTM D790
PolyOne Stat-Tech™ PC-08CF/000 FR V0 Polycarbonate (PC) Stat-Tech™ Electrically Conductive Compounds are specifically engineered to provide anti-static, ESD and RFI/EMI shielding performance for critical electronic equipment applications. These compound..
Flexural Strength	172 MPa	24900 psi	ISO 178
SABIC Innovative Plastics LNP LUBRICOMP DFL36P PC LNP* Lubricomp* DFL36P is a compound based on Polycarbonate containing 30% Glass Fiber 15% PTFE. Added features include: Exceptional Processing. Internally Lubricated.
Flexural Strength	172 MPa	24900 psi	ASTM D790
Kolon SPESINÂ® KP213G15SIBL Glass Fiber Reinforced PBT Compound Resin G/F 15%, high toughness, excellent surfaceApplications: Various types of housingsInformation provided by API-Kolon.
Flexural Strength	172 MPa	24900 psi	ASTM D790
Glastic Laminates/Shapes Polyester, Channels and Structural Shapes (GPO3) Data provided by Glastic Corporation.NEMA GPO-3. Average data - may vary with the size and shape of the electrical insulating structural product.
Flexural Strength	172 MPa	24900 psi	ASTM D790
SABIC Innovative Plastics LNP LUBRICOMP IFL34 PA 6/12 (Asia Pacific) LNP* Lubricomp* IFL34 is a compound based on Nylon 6/12 resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.
Flexural Strength	172 MPa	24900 psi	ISO 178
SABIC Innovative Plastics LNP LUBRICOMP KFI15 ACETAL LNP* LUBRICOMP* KFI15 is a compound based on Acetal containing 25% Glass Fiber, 2% Silicone. Added feature of this grade is: Wear Resistant.
Flexural Strength	172 MPa	24900 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP LUBRICOMP Lexan_LF1530A PC LNP* Lubricomp* Lexan_LF1530A compound is a 30% glass reinforced, 15% PTFE filled PC. Flame retardant and wear resistant. Tight tolerances.
Flexural Strength	172 MPa	24900 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP LUBRICOMP Lexan_LF1530A PC (Europe-Africa-Middle East) LNP* Lubricomp* Lexan_FL1530 compound is a 30% glass reinforced, 15% PTFE filled PC. Flame retardant and wear resistant. Tight tolerances.
Flexural Strength	172 MPa	24900 psi	ISO 178
SABIC Innovative Plastics LNP LUBRICOMP PFL36 PA 6 LNP* LUBRICOMP* PFL36 is a compound based on Nylon 6 resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Wear Resistant.
Flexural Strength	172 MPa	24900 psi	2.6 mm/min, 100 mm span; ASTM D 790
SABIC Innovative Plastics Ultem 2212 PEI (Asia Pacific) 20% Milled glass filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing.This data was supplied by SABIC-IP for the Asia Pacific region.
Flexural Strength	172 MPa	24900 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics ValoxÂ® 830 PBT (Asia Pacific) 30% GR PBTP, excellent surface finish. Typical applications are hot air gun housing assemblies, industrial glue guns, appliance housings and handles.
Flexural Strength	172 MPa	24900 psi	ASTM D 790
SABIC Innovative Plastics LNP Stat-kon PE002 PA 6 (Asia Pacific) LNP* Stat-kon* PE002 is a compound based on Nylon 6 resin containing Carbon Fiber. Added features of this material include: Electrically Conductive.This data was supplied by SABIC-IP for the Asia P..
Flexural Strength	172 MPa	24900 psi	ISO 178
SABIC Innovative Plastics LNP THERMOCOMP DE004ERP PC LNP* Thermocomp* DE004ERP is a compound based on Polycarbonate resin containing 20% Carbon Fiber. Added features include: Electrically Conductive, Easy Molding, Mold Release.
Flexural Strength	172 MPa	24900 psi	ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP DX06410 PC (Asia Pacific) LNP* Thermocomp* DX06410 is a compound based on Polycarbonate resin containing Glass Fiber. Added features of this material include: Easy Molding, Mold Release.
Flexural Strength	172 MPa	24900 psi	ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP DX06412H PC LNP* THERMOCOMP* DX06412H is a compound based on Polycarbonate resin containing 30% Glass Fiber. Added features of this material include: Easy Molding, Mold Release.
Flexural Strength	172 MPa	24900 psi	ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP JF003XXZ PES LNP* THERMOCOMP* JF003XXZ is a compound based on Polyethersulfone resin containing 15% Glass Fiber.
Flexural Strength	172 MPa	24900 psi	ASTM D 790
SABIC Innovative Plastics LNP Thermocomp JX89569 PES LNP THERMOCOMP* JX89569 is a compound based on Polyethersulfone resin containing Glass Fiber.This data was supplied by SABIC-IP for the Americas region.
Flexural Strength	172 MPa	24900 psi	ASTM D 790
SABIC Innovative Plastics LNP Thermocomp OFM66 PPS LNP* Thermocomp* OFM66 is a compound based on Polyphenylene Sulfide resin containing Glass Fiber, Mineral. Added features of this material include: Low Warpage.This data was supplied by SABIC-IP fo..
Flexural Strength	172 MPa	24900 psi	ISO 178
Polyplastics Duranex® C5315 Polybutylene Terephthalate (PBT), Higher gloss, Better surface appearance, 15% GF filled DURANEX® is a crystalline thermoplastic based on polybutylene terephthalate (PBT) that can be readily strengthened, modified, or otherwise performance enhanced through the addition of glass fibers ..
Flexural Strength	172 MPa	24900 psi	ASTM Test
BASF Ultramid® 8231G HS 14% Glass Filled PA6 (Dry) Ultramid 8231G HS is a heat stabilized, 14% glass fiber reinforced nylon 6 injection molding compound. It is also available in non-heat stabilized (Ultramid 8231) and/or pigmented versions. The gla..
Flexural Strength	172 MPa	24900 psi	ASTM D790
A. Schulman ComAlloy Hiloy® 621 Nylon 6/6, Glass Reinforced Data provided by the manufacturer, ComAlloy International Company.15% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.
Flexural Strength	171.68 MPa	24900 psi	ASTM D790
E-Polymers SEPAZ® C130GP 30% Glass Fiber Reinforced LCP Resin Liquid Crystal Polymer Resin: SEPAZ LCP resin has a unique structure and performance unthought of in a traditional plastics. Beside SEPAZ LCP takes the excels in all-around performance and molding ..
Flexural Strength	172 MPa @Temperature 23.0 °C	24900 psi @Temperature 73.4 °F	ISO 178
Solvay Specialty Polymers Amodel® A-1240 L Polyphthalamide (PPA) (discontinued **) Amodel A-1240 L is a 40% mineral filled polyphthalamide (PPA) that offers low warpage and excellent dimensional stability. This resin also has a high deflection temperature, flexural modulus and ten..
Flexural Strength	172 MPa	24900 psi	ASTM D 790
SABIC Innovative Plastics LNP Thermocomp JX89569 PES (Asia Pacific) LNP* THERMOCOMP* JX89569 is a compound based on Polyethersulfone resin containing Glass Fiber.This data was supplied by SABIC-IP for the Asia Pacific region.
Flexural Strength	172 MPa	24900 psi	ASTM D790
LNP Thermocomp® JF-1006 E LE BK8-055 Polyethersulfone, Glass Fiber Reinforcement (discontinued **) Features: High Viscosity, Low ExtractablesForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many L..