Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 165 MPa | 23900 psi | 1.3 mm/min; ASTM D790 |
PolyOne LubriOne™ PS-30GF/15T Natural Polybutylene Terephthalate (PBT) LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. L.. |
|||
Flexural Strength | 165 MPa | 23900 psi | STN EN ISO 178 |
Plastcom SLOVAMID® 6/66 GF 15 GB 15 PA6/66 reinforced with glass fiber, glass beads PA 6 and PA 66 alloy for injection molding, reinforced with 15% glass fiber and 15 % glass beads, for moldings used in the automotive, electrical, building, engineering and hobby industry - holders .. |
|||
Flexural Strength | 165 MPa | 23900 psi | 1.3 mm/min; ASTM D790 |
PolyOne Edgetek® PS-20GF/000 NATURAL Polybutylene Terephthalate (PBT) Information provided by PolyOne |
|||
Flexural Strength | <= 165 MPa | <= 23900 psi | ISO 178 |
Polykemi AB POLYshine PBT D201 GF20 PBT, Glass Fiber Reinforced Information provided by Polykemi AB |
|||
Flexural Strength | 165 MPa | 23900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Lexan® 3412HF PC 20% glass reinforced, high flow PC. UL rated V-1 at 0.059"", |
|||
Flexural Strength | 165 MPa | 23900 psi | ISO 178 |
Nilit FRIANYL B63 FK 1020 Nylon 6 for injection molding, 10% glass fiber and 20% glass ball reinforced Nylon 6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Flexural Strength | 165 MPa | 23900 psi | |
Lehmann & Voss LUVOCOM® 1105-8476 PEEK, with carbon fiber Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Chemical and hydrolysis resistance parts, non flammable.High dimensionally stable precisio.. |
|||
Flexural Strength | 165 MPa | 23900 psi | |
Lehmann & Voss LUVOCOM® 1106-8087/BL Polyether imide, unreinforced, laser markable Applications: High continuous use and heat distortion temperature. Non flammable.Dynamic stressed parts at high movement velocity.High dimensionally stable precision parts.Information provided by Le.. |
|||
Flexural Strength | 165 MPa | 23900 psi | |
Lehmann & Voss LUVOTECH® MR 1025 BK Polyamide 66, with mineral filler Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Low warpage.Isotropic shrinkage characteristics.Information provided by Lehmann & Voss & Co.KG |
|||
Flexural Strength | 165 MPa | 23900 psi | |
Lehmann & Voss LUVOCOM® 1106-8232 Polyether imide, unreinforced, laser markable Applications: High continuous use and heat distortion temperature. Non flammable.Dynamic stressed parts at high movement velocity.High dimensionally stable precision parts.Information provided by Le.. |
|||
Flexural Strength | 165 MPa | 23900 psi | ASTM D790 |
Solvay Specialty Polymers Amodel® A-4122 LS WH678 Polyphthalamide (PPA), 22% Glass Fiber Amodel® A-4122 LS is a 22% glass fiber reinforced, light-stabilized, high-reflectivity white grade of Amodel polyphthalamide (PPA). It is designed to provide high crystallinity when molded in wat.. |
|||
Flexural Strength | 165 MPa | 23900 psi | ASTM D790 |
SABIC Innovative Plastics LNP STAT-KON DE002ER PC LNP STAT-KON* DE002ER is a compound based on Polycarbonate resin containing 10% Carbon Fiber. Added features of this material include: Easy Molding. Mold Release, Electrically Conductive. |
|||
Flexural Strength | 165 MPa | 23900 psi | ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP DF0049E PC (Asia Pacific) LNP* Thermocomp* DF0049E is a compound based on Polycarbonate resin containing Glass Fiber, Flame Retardant. Added features of this material include: Easy Molding, Flame Retardant. |
|||
Flexural Strength | 165 MPa | 23900 psi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP DF0049P PC (Asia Pacific) LNP* Thermocomp* DF0049P is a compound based on Polycarbonate resin containing Glass Fiber. Added features of this material include: Exceptional Processing, Flame Retardant. |
|||
Flexural Strength | 165 MPa | 23900 psi | ISO 178-93 |
Wellman Wellamid® MRGF25/15 22H-NBK1/WE-1364 40% Mineral/Glass Reinforced Nylon 66 Description: Mineral/Glass Reinforced Nylon 66Information provided by Wellman. |
|||
Flexural Strength | 165 MPa | 23900 psi | ASTM D790 |
Polyram RamSter PF300J50 PBT, 50% Glass Fiber + Glass beads 50% Glass-fiber and glass beads reinforced PBT.Information provided by Polyram Ram On Ind. |
|||
Flexural Strength | 165 MPa | 23900 psi | ASTM D790 |
A. Schulman ComAlloy® E-13370 Lubricated Reinforced Polyester Alloy Information provided by A. Schulman.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Flexural Strength | 165 MPa | 23900 psi | 2 mm/min; ISO 178 |
Eurostar Staramide RF003S PA66, 15% Glass Fiber Filled, Injection Molded Staramide RF003S is a 15% Glass Fiber Reinforced Polyamide 66 Injection Molding ResinInformation provided by Eurostar. |
|||
Flexural Strength | <= 165 MPa | <= 23900 psi | 3.5% flexure; ISO 178 |
Azoty Tarnow™ Tarnamid® T-27 GF15 MW25 Polyamide 6 - Mineral Reinforced 15% Glass fiber reinforced and 25% Mineral filled, medium viscosity injection molding grade, also used for compounding, for production of monofilament, bristles and fibers.Tarnamid® has the followi.. |
|||
Flexural Strength | 165 MPa | 23900 psi | ASTM D790 |
Beijing Chemical Industry KAIFA® HN301-G30 PA6 Resin 30% glass fiber reinforced, flame retardantInformation provided by Beijing Chemical Industry Research Institute (Group) |
|||
Flexural Strength | 165 MPa | 23900 psi | ASTM D790 |
A. Schulman ComAlloy Voloy® 417 Polyester - PBT, Glass/Mineral Reinforced, Flame Retardant, UL Data provided by the manufacturer, ComAlloy International Company.43% Glass/Mineral Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Flexural Strength | 165 MPa | 23900 psi | 2 [mm/min]; ISO 178 |
Akro-Plastic Akromid® A3 GF 20 (2419) PA 6.6 Conditioned, 20% Glass Filled AKROMID® A (Polyamide 6.6) is an engineering compound, characterized by high mechanical strength, stiffness and thermal resistance. Furthermore, this polyamide offers high toughness at low temperat.. |
|||
Flexural Strength | 165 MPa | 23900 psi | ASTM D790 |
Beijing Chemical Industry KAIFA® 301-G15RF PBT Resin 15% glass fiber reinforced, flame retardant, good toughness, low bleedingInformation provided by Beijing Chemical Industry Research Institute (Group) |
|||
Flexural Strength | 165 MPa | 23900 psi | 2 mm/min; ISO 178-A |
Lanxess Pocan® BFN 4231 000000 PBT, 25% Glass Fiber PBT, 25% glass fibers, injection molding, halogen free flame retardantInformation provided by LANXESS. |