Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 162 MPa | 23500 psi | ASTM D790 |
PolyOne Trilliant™ HC HC3320-0020 RS Natural Polybutylene Terephthalate (PBT) The Trilliant® specialty compounds offer a complete system of specialty engineered materials, certified processes, services and technical support that enable healthcare OEM's to get to market ahead.. |
|||
Flexural Strength | 162 MPa | 23500 psi | ASTM D 790 |
SABIC Innovative Plastics Enduran 7062X PBT+PET (Asia Pacific) This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
Flexural Strength | 162 MPa @Temperature 23.0 °C |
23500 psi @Temperature 73.4 °F |
DAM; ASTM D790 |
DuPont Performance Polymers Zytel® HTN 51G15HSL BK083 Polyphthalamide (PPA)
(Unverified Data**) Zytel® HTN51G15HSL BK083 is a 15% glass reinforced, heat stabilized, lubricated high performance polyamide resin. It is also a PPA resin.Information provided by DuPont Performance Polymers |
|||
Flexural Strength | 162 MPa | 23500 psi | ASTM D790 |
Kotec Carbotex KG-30MRA Polycarbonate, 30% Glass Fiber Reinforced Features: Glass fiber 30% reinforced, Mold release, Translucent, Dimensional stability, Flame retardant, High rigidityApplications: OA equipment, Communications, Precision parts, Machineries, E & E .. |
|||
Flexural Strength | 162 MPa | 23500 psi | 2 mm/min; ISO 178 |
Ineos ABS Lustran® SAN GF20 Glass Fiber Reinforced |
|||
Flexural Strength | 162 MPa | 23500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics NORYL PX5558 PPE+PS 30% glass reinforced, high flow PPO. |
|||
Flexural Strength | 162 MPa | 23500 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
SABIC Innovative Plastics LNP Stat-kon AE004E ABS LNP* Stat-Kon* AE004E is an ABS compound containing Glass Fiber. Characteristics of this grade are Statically Conductive and Easy Molding.This data was supplied by SABIC-IP for the Americas region... |
|||
Flexural Strength | 162 MPa | 23500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP STAT-KON ZX08301 PPE (Asia Pacific) Stat-Kon* ZX08301 compound is a high heat compounds with ESD safe and low warpage performance suitable for use in Semiconductor Packaging Applications. |
|||
Flexural Strength | 162 MPa | 23500 psi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP DF004E PC LNP THERMOCOMP* DF004E is a compound based on Polycarbonate resin containing 20% Glass Fiber. Added features of this material include: Easy Molding. |
|||
Flexural Strength | 162 MPa | 23500 psi | ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP DF004P PC LNP THERMOCOMP* DF004P is a compound based on Polycarbonate resin containing 20% Glass Fiber. Added features of this material include: Exceptional Processing. |
|||
Flexural Strength | 162 MPa | 23500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP GX05482 PSU LNP* THERMOCOMP* GX05482 is a compound based on Polysulfone resin containing 30% Glass Fiber. Added features of this material include: Flame Retardant. |
|||
Flexural Strength | 162 MPa | 23500 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP VERTON MV007SUP PP (Europe-Africa-Middle East) LNP* VERTON* MV007SUP is a compound based on PP resin containing Long Glass Fiber. Added features include; Chemically Coupled, Heat Stabilized, UV Stabilized. |
|||
Flexural Strength | 162 MPa | 23500 psi | ISO 178 |
SABIC Innovative Plastics LNP VERTON NV003E PC+ABS (Asia Pacific) LNP* Verton* NV003E is a compound based on PC+ABS Blend resin containing Long Glass Fiber. Added features of this material include: Easy Molding. |
|||
Flexural Strength | 162 MPa | 23500 psi | ISO 178 |
SABIC Innovative Plastics LNP VERTON NV003E PC+ABS LNP* VERTON* NV003E is a compound based on PC+ABS Blend resin containing 15% Long Glass Fiber. Added features of this material include: Easy Molding, Structural. |
|||
Flexural Strength | 162 MPa | 23500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics NORYL EM7430 PPE+PS 30% glass reinforced, high flow PPO. Automotive. Energy management material. |
|||
Flexural Strength | 162 MPa @Temperature 150 °C |
23500 psi @Temperature 302 °F |
ASTM D790 |
DuPont Performance Polymers VESPEL TP-8541 Polyimide Thermoplastic parts from filled PI (polyimide) for high mechanical properties and impact performance in high temperature environmentsInformation provided by DuPont Performance Polymers |
|||
Flexural Strength | 162 MPa | 23500 psi | ASTM D790 |
Applied Composites 185 Polyester SMC Industry Application: TransportationProduct Application: Lawn and GardenDistinct Features: Limited PigmentabilityInformation provided by Applied Composites Corporation. |
|||
Flexural Strength | 162 MPa | 23500 psi | ASTM D790 |
Teknor Apex Chemlon® 214 GH Nylon 6, 14% Short Glass Fiber Features: Good Creep Resistance; Good Dimensional Stability; Good Processability; Good Toughness; Heat Stabilized; High Strength Processing Method: Injection Molding Forms: Pellets Additive: Heat S.. |
|||
Flexural Strength | 162 MPa | 23500 psi | ASTM D790 |
Gharda Chemicals Gafone™ B2315GF Polysupersulfone (PSS)
(discontinued **) Characteristics: Excellent Dimensional properties Transparent Improved Impact Strength and Toughness as compared to PES Excellent Hydorlytic Stability High Stress Cracking Resistance Good Chemical.. |
|||
Flexural Strength | 162 MPa | 23500 psi | ASTM D790 |
Solvay Specialty Polymers Veradel® AG-320 Polyethersulfone (PESU)
(Unverified Data**) Veradel AG-320 is a 20% glass fiber reinforced grade of polyethersulfone (PESU). Adding glass fiber to polyethersulfone substantially increases the rigidity, tensile strength, creep resistance, dime.. |