Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 16.0 MPa | 2320 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
Ovation Polymers Nima™ HL 18400 HDPE High Density Polyethylene - Halogenated FR compound with good impact resistance. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. All samples are prepa.. |
|||
Flexural Strength | 16.0 MPa | 2320 psi | |
Quadrant EPP TIVAR® Dryslide PE-UHMW + internal lubricant + other additives (ISO Data) Thanks to the lubricant built into a PE-UHMW matrix with higher molecular weight, TIVAR DrySlide offers a lower coefficient of friction and enhanced wear and abrasion resistance than TIVAR 1000. The.. |
|||
Flexural Strength | 16.0 MPa | 2320 psi | |
Quadrant EPP TIVAR® DS PE-UHMW + additives (ISO Data) TIVAR DS is a modified PE-UHMW with extremely high molecular weight. The latter in combination with a particular manufacturing process result in a PE-UHMW grade with superior wear and abrasion resis.. |
|||
Flexural Strength | 16.0 MPa | 2320 psi | |
Quadrant EPP TIVAR® H.O.T. PE-UHMW + specific additives (ISO Data) TIVAR H.O.T. [Higher Operating Temperature] is formulated to maintain inherent PE-UHMW key properties over an extended service temperature range, in this way considerably increasing part life in low.. |
|||
Flexural Strength | 16.0 MPa | 2320 psi | ASTM D790 |
LG Chemical LUPOL TE-5005H Thermoplastic Elastomer Alloy, Dimensional Stability LUPOL resins, based on polyolefin with a wide range of characteristics, are a family of low cost engineering plastics.Applications: Automotive exterior parts.Information Provided by LG Chem |
|||
Flexural Strength | 16.0 MPa | 2320 psi | ISO 178 |
SABIC Innovative Plastics LNP Stat-kon TD000 LNP* Stat-kon* TD000 is a compound based on Polyurethane resin. Added features of this material include: Electrically Conductive.This data was supplied by SABIC-IP for the Americas region. |
|||
Flexural Strength | 16.0 MPa | 2320 psi | ISO 178 |
SABIC Innovative Plastics LNP STAT-KON TD000 PU LNP* STAT-KON* TD000 is an unfilled compound based on Polyurethane resin. Added feature of this material is: Electrically Conductive. |
|||
Flexural Strength | 16.0 MPa | 2320 psi | ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP TH0450A PUR LNP THERMOCOMP* TH0450A is a compound based on Polyurethane resin. Added features of this material include: High Specific Gravity. |
|||
Flexural Strength | 16.0 MPa | 2320 psi | ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP TH0450A PUR (Asia Pacific) LNP THERMOCOMP* TH0450A is a compound based on Polyurethane resin. Added features of this material include: High Specific Gravity. |
|||
Flexural Strength | 16.0 MPa | 2320 psi | ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP 2X03624H FP-F (FEP) LNP* THERMOCOMP* 2X03624H is a compound based on FEP resin containing Proprietary Filler(s). |
|||
Flexural Strength | 16.0 MPa | 2320 psi | Olsen; ASTM D747 |
UBE F022 Polyethylene Description: UBE Polyethylene is polymerized at high pressure using a tubular reactor. Production conditions are strictly controlled ensuring the product's superior physical and mechanical prope.. |
|||
Flexural Strength | 16.0 MPa | 2320 psi | Olsen; ASTM D747 |
UBE F022NH Polyethylene Description: UBE Polyethylene is polymerized at high pressure using a tubular reactor. Production conditions are strictly controlled ensuring the product's superior physical and mechanical prope.. |
|||
Flexural Strength | 16.0 MPa | 2320 psi | Olsen; ASTM D747 |
UBE F120N Polyethylene Description: UBE Polyethylene is polymerized at high pressure using a tubular reactor. Production conditions are strictly controlled ensuring the product's superior physical and mechanical prope.. |
|||
Flexural Strength | 16.0 MPa | 2320 psi | ASTM D790 |
UBE UBESTA® 3030JI7 Plasticized Industrial Grade Nylon 12 Description: UBE UBESTA® Industrial grade Nylon 12Comments: low migrationInformation provided by UBE. |
|||
Flexural Strength | 16.0 MPa | 2320 psi | ASTM D790 |
UBE PAE1201U Nylon Elastomer Description: UBESTA Nylon 12 ElastomerInformation provided by UBE. |
|||
Flexural Strength | 16.0 MPa | 2320 psi | ASTM D790 |
UBE UBESTA® 3030JNU Short Cycle Time Electronic Grade Nylon 12 Description: UBESTA Nylon 12 has an excellent termite resistance than other plastics. UBESTA contributes as a material for jacket and sheath which lay for telephone and telegram Communication System.. |
|||
Flexural Strength | 16.0 MPa | 2320 psi | cond; ISO 178 |
DSM Novamid® ST145 NAT PA6-I Impact Modified, Injection Molding |
|||
Flexural Strength | 16.0 MPa | 2320 psi | 2 mm/min; ISO 178 |
Eurostar Staramide AG3X3 PA66, Glass Fiber Reinforced, Impact Modified, Injection Molding Staramide AG3X3 is an Impact Modified, Glass Fiber Reinforced Polyamide 66, Injection Molding ResinInformation provided by Eurostar. |
|||
Flexural Strength | 16.0 MPa | 2320 psi | ASTM D790 |
Aclo Accutech Polypropylene Copolymer CP0437C10L Calcium Reinforced |
|||
Flexural Strength | 16.0 MPa | 2320 psi | ASTM D790 |
Aclo Accutech Polypropylene Copolymer CP0437C20L Calcium Reinforced |
|||
Flexural Strength | 16.0 MPa | 2320 psi | SAE J949 |
Azdel SuperLite® SL551000-100 PP Resin Matrix / 55% Glass Fiber (3 mm Molded Thickness) AZDEL SuperLite® SL551000-100 is a low pressure, thermoformable, thermoplastic composite of polypropylene and long chopped glass fibers. Usually combined with outer layers as needed for the applic.. |
|||
Flexural Strength | 16.0 MPa | 2320 psi | cond.; ISO 178 |
Azoty Tarnow™ Tarnamid® T-27 MCS HI Polyamide 6 - Impact Modified Very high impact resistance, cold impact grade (to -40°C). Medium viscosity injection molding grade, also used for compounding, for production of monofilament, bristles and fibers.Tarnamid® has t.. |