Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 145 MPa | 21000 psi | STN EN ISO 178 |
Plastcom SLOVAMID® 6 GF 20 FRA 5 PA6 reinforced with glass fiber, flame retarded PA 6 for injection molding, reinforced with 20% glass fiber, flame retarded with halogen flame retardant. Main features: flammability in accordance with UL 94 5 at 1.6 mm, glow wire at 960°C. Appli.. |
|||
Flexural Strength | 145 MPa | 21000 psi | ASTM D790 |
PolyOne Stat-Tech™ LC-20NCF/000 V3 Natural Liquid Crystal Polymer (LCP) Stat-Tech™ Electrically Conductive Compounds are specifically engineered to provide anti-static, ESD and RFI/EMI shielding performance for critical electronic equipment applications. These compound.. |
|||
Flexural Strength | 145 MPa | 21000 psi | ASTM D790 |
Quadrant EPP Techtron® 1000 PPS Extruded Polyphenylene Sulfide (ASTM Product Data Sheet) |
|||
Flexural Strength | 145 MPa | 21000 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Lexan® 3414R PC (Europe-Africa-Middle East) LEXAN 3414R is a high viscosity, 40% glass reinforced, flame retardant grade, especially designed for applications requiring high rigidity together with high heat resistance. |
|||
Flexural Strength | 145 MPa | 21000 psi | Resin |
Renegade Materials Corporation RM-3002 Bismaleimide (BMI) Resin IM7 12K Carbon Uni-tape Developed using state-of-the-art formulating technologies, RM-3002 BMI prepreg products deliver superior hot/wet performance in airframe, missile and propulsion applications at service temperatures .. |
|||
Flexural Strength | 145 MPa | 21000 psi | |
Cookson Group Plaskon® 3100 Novolac Epoxy Molding Compound
(discontinued **) Test specimens were transfer molded and post cured 4 hours at 175°C.A flame retardant, novolac-hardened epoxy molding compound recommended for semiconductor packages that are not stress sensitive. |
|||
Flexural Strength | 145 MPa | 21000 psi | ASTM D790 |
Ravago Manufacturing Americas Hylon® N1025HLFR Nylon 6/6, 25% Fiberglass, Heat Stabilized, Lubricated, Flame retardant (Cond) Information provided by Ravago. |
|||
Flexural Strength | 145 MPa | 21000 psi | |
Lehmann & Voss LUVOCOM® 1105-8199 PEEK, with CNT Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Electrically conductive, suitable for continuous discharging of statically generated elect.. |
|||
Flexural Strength | 145 MPa | 21000 psi | |
Lehmann & Voss LUVOCOM® PEEK CLASSIX 7994 PEEK, unreinforced Applications: medical engineeringEspecially suitable for medical parts, superheated steam sterilizable, hydrolysis resistanceHigh chemical resistance parts, non flammable.Inherent flame resistance.S.. |
|||
Flexural Strength | 145 MPa | 21000 psi | 3.5%; ISO 178 |
GEHR Plastics PEI Polyetherimide Polyetherimide has a high mechanical strength in connection with a good chemical and heat resistance, good dimensional stability and creep resistance. Its unique torque strength permits the economic.. |
|||
Flexural Strength | 145 MPa | 21000 psi | ISO 178 |
Mitsubishi Xantar® G4F 23 UR Polycarbonate-20% Glass Reinforced Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances .. |
|||
Flexural Strength | 145 MPa | 21000 psi | |
Haysite ETS-FR-II Glass Reinforced Polyester Sheet, Electrical Grade (GPO2) A NEMA GPO-2 glass mat reinforced thermoset polyester molded sheet. ETS-FR-II is UL recognized with a flame rating of 94V-0 and arc resistance of 185 seconds. This grade is an IEEE Thermal Class B, .. |
|||
Flexural Strength | 145 MPa | 21000 psi | |
Lehmann & Voss LUVOCOM® 1105/GN7348 PEEK, unreinforced, laser markable Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.High chemical resistance parts, non flammable.Not flammable.Especially suitable for medica.. |
|||
Flexural Strength | 145 MPa | 21000 psi | ASTM D790 |
Techmer ES HiFill® PA6 GF15 L UV BK 15% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 15% Filler by Weight Additive: UV Stabilizer and LubricantFeatures: Good UV Resistance and LubricatedAppeara.. |
|||
Flexural Strength | 145 MPa | 21000 psi | ISO 178 |
SABIC Innovative Plastics LNP Stat-kon NX03602 PC+ABS (Asia Pacific) LNP* STAT-KON* NX03602 is a compound based on PC+ABS Blend resin containing Carbon Fiber, Flame Retardant. Added features of this material include: Electrically Conductive.This data was supplied by.. |
|||
Flexural Strength | 145 MPa | 21000 psi | |
SPS Guang Zhou POBUXâ„¢ 3001EPG30 Non-halogen flame retardance/GF30%-PBT Characteristic: Good flame retardance, high mechanical properties, high rigidity, superior heat resistance, good dimensional stabilityApplications: E/E partsInformation Provided by SPS (Guang Zhou) .. |
|||
Flexural Strength | 145 MPa | 21000 psi | ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP WF0039U PBT LNP* THERMOCOMP* WF0039U is a compound based on PBT resin containing 15% Glass Fiber. Added features of this grade include: Flame Retardant and UV Stabilized. |
|||
Flexural Strength | 145 MPa | 21000 psi | ASTM D790 |
SABIC Innovative Plastics NORYL PX4716 PPE+HIPS (Asia Pacific) PPE+PS GF15% FR V-1 |
|||
Flexural Strength | 145 MPa | 21000 psi | ASTM D790 |
Asahi Kasei Thermylene® P6-40FG-0874 40% Glass Fiber Reinforced, Heat and UV Stabilized Information provided by Asahi Thermofil |
|||
Flexural Strength | 145 MPa | 21000 psi | ASTM D790 |
Teknor Apex Chemlon® 140 MH Nylon 66, 40% Mineral Reinforced Notes: 40% Mineral; High rigidity with exceptional control of warpage and surface sink marks; Excellent for large parts; Fast cycling Features: Fast Molding Cycle; High Rigidity; Heat Stabilized; Lo.. |
|||
Flexural Strength | 145 MPa | 21000 psi | ISO 178 |
SABIC Innovative Plastics LNP VERTON MV006BS PP LNP* VERTON* MV006BS is a compound based on Polypropylene resin containing 30% Long Glass Fiber. Added features of this grade include: Heat Stabilized, Burst Pressure, Structural, Chemically Coupl.. |