| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Flexural Strength | 118 MPa | 17100 psi | ASTM D-790 |
| Plaskolite Optix® CP - 81 General Purpose Acrylic Resin OPTIX® general purpose acrylics are available in a variety of performance grades that offer varying melt flow rates, heat resistance, color/opacity and gloss levels.Information provided by Plaskoli.. |
|||
| Flexural Strength | 118 MPa | 17100 psi | ASTM D-790 |
| Plaskolite Optix® CP - 82 General Purpose Acrylic Resin OPTIX® general purpose acrylics are available in a variety of performance grades that offer varying melt flow rates, heat resistance, color/opacity and gloss levels.Information provided by Plaskoli.. |
|||
| Flexural Strength | 118 MPa | 17100 psi | ASTM D-790 |
| Plaskolite Optix® CP - 82 UVA General Purpose Acrylic Resin OPTIX® general purpose acrylics are available in a variety of performance grades that offer varying melt flow rates, heat resistance, color/opacity and gloss levels.Information provided by Plaskoli.. |
|||
| Flexural Strength | 118 MPa | 17100 psi | ASTM D-790 |
| Plaskolite West Optix® CP - 86 General Purpose Acrylic Resin Generally unaffected by alkalis, hydrocarbons, non-oxidizing acids, and salt water. Transparent, translucent, opaque, and custom colors in various grades of melt flow rate and heat resistance are av.. |
|||
| Flexural Strength | 118 MPa | 17100 psi | ASTM D790 |
| Nilit Polynil® P240HSLV High Viscosity, Heat Stabilized Nylon 66 Description: Polynil P240 HSLV was developed for injection molding applications, where a combination of heat aging resistance, abrasion resistance and impact strength is needed, such as chain tensio.. |
|||
| Flexural Strength | 118 MPa | 17100 psi | ISO 178 |
| SABIC Innovative Plastics LNP COLORCOMP JX91550 PES LNP COLORCOMP* JX91550 is an unfilled Polyethersulfone. |
|||
| Flexural Strength | 118 MPa | 17100 psi | ISO 178 |
| SABIC Innovative Plastics LNP LUBRICOMP DFL22 PC LNP* Lubricomp* DFL22 is a compound based on Polycarbonate resin containing 10% Glass Fiber and 10% PTFE. Added features include: Internally Lubricated. |
|||
| Flexural Strength | 118 MPa | 17100 psi | ASTM D-790 |
| Plaskolite West Optix® CP - 81 General Purpose Acrylic Resin Generally unaffected by alkalis, hydrocarbons, non-oxidizing acids, and salt water. Transparent, translucent, opaque, and custom colors in various grades of melt flow rate and heat resistance are av.. |
|||
| Flexural Strength | 118 MPa | 17100 psi | ASTM D790 |
| LG Chemical LUCEL MR-320 Low Warpage POM, 20% Mineral Filled LUCEL semi-crystalline acetal copolymer resins are produced by gas phase polymerization. LUCEL resins can be widely accepted as the replacement of thermosets, aluminum and zinc die-casts or other m.. |
|||
| Flexural Strength | 118 MPa | 17100 psi | ASTM D790 |
| Kolon KOCETAL® GF702 G/F Reinforced Acetal Resin Glass fiber reinforced, improved stiffness. Applications: Products for high stiffness, improved fatigue properties. Information provided by API-Kolon. |
|||
| Flexural Strength | 118 MPa | 17100 psi | ASTM D790 |
| LG Chemical LUCON PO-3000 Electrically Conductive Thermoplastic LG Chemicals has formulated a diverse range of LUCON thermoplastic compounds containing conductive additives, such as carbon powder, (nickel coated) carbon fiber, or stainless steel fiber for solvin.. |
|||
| Flexural Strength | 118 MPa | 17100 psi | ASTM D790 |
| Kolon KOPA® KN333MT30BL Mineral Reinforced Nylon 66 MF reinforcedApplications Cam shaftsInformation provided by API-Kolon. |
|||
| Flexural Strength | 118 MPa | 17100 psi | ASTM D790 |
| Kotec Carbotex KG-10MRA Polycarbonate, 10% Glass Fiber Reinforced Features: Glass fiber 10% reinforced, Mold release, Translucent, Dimensional stability, Flame retardant, High rigidityApplications: OA equipment, Communications, Precision parts, Machineries, E & E .. |
|||
| Flexural Strength | 118 MPa | 17100 psi | ASTM D790 |
| Kotec Carbotex KGN-10MRA Polycarbonate, Flame Retardant, 10% Glass Fiber Reinforced Features: Glass fiber 10% reinforced, Mold release, Translucent, Dimensional stability, Flame retardant, High rigidityApplications: OA equipment, Communications, Precision parts, Machineries, E & E .. |
|||
| Flexural Strength | 118 MPa | 17100 psi | ISO 178 |
| SABIC Innovative Plastics LNP LUBRICOMP LL004C PEEK LNP* LUBRICOMP* LL004C is a compound based on Polyetheretherketone resin containing 20% PTFE. Added features of this material include: Wear Resistant, Clean Compounding System. |
|||
| Flexural Strength | 118 MPa | 17100 psi | ISO 178 |
| SABIC Innovative Plastics LNP LUBRICOMP LL004C PEEK (Asia Pacific) LNP* Lubricomp* LL004C is a compound based on Polyetheretherketone resin containing PTFE. Added features of this material include: Internally Lubricated, Clean Compounding System. |
|||
| Flexural Strength | 118 MPa | 17100 psi | 2.8 mm/min; ASTM D790 |
| Samsung Cheil Industries Infino® HF-3200H PC, Glass Filled High Impact Information provided by Samsung Cheil Industries. |
|||
| Flexural Strength | 118 MPa | 17100 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics LNP THERMOCOMP ZF004 PPE+PS LNP THERMOCOMP* ZF004 is a compound based on PPE+PS resin containing 20% Glass Fiber. |
|||
| Flexural Strength | 118 MPa | 17100 psi | ISO 178 |
| SABIC Innovative Plastics LNP THERMOCOMP ZF0049 PPE+PS (Asia Pacific) LNP* Thermocomp* ZF0049 is a compound based on PPE+PS Blend resin containing Flame Retardant. Added features of this material include: Flame Retardant. |
|||
| Flexural Strength | 118 MPa | 17100 psi | ISO 178 |
| SABIC Innovative Plastics LNP LUBRICOMP LL004 PEEK (Asia Pacific) LNP LUBRICOMP* LL004 is a compound based on Polyetheretherketone resin containing PTFE. Added features of this material include: Internally Lubricated. |
|||
| Flexural Strength | 118 MPa | 17100 psi | ISO 178 |
| SABIC Innovative Plastics LNP THERMOCOMP ZF0049 PPE+PS LNP* THERMOCOMP* ZF0049 is a compound based on PPE+PS resin containing 20% Glass Fiber. Added feature of this material is: Flame Retardant. |
|||
| Flexural Strength | 118 MPa | 17100 psi | ISO 178 |
| Unitika A3130 PA6, 35% Mineral Reinforced, Dry Information provided by Unitika Ltd. |
|||
| Flexural Strength | 118 MPa | 17100 psi | 2 mm/min; ISO 178 |
| Eurostar Starflam AFR560B5 PA66, Mineral/Glass Fiber Reinforced, Flame Retardant, Injection Molding Starflam AFR560B5 is a Flame Retardant, Mineral Filled and Glass Fiber Reinforced Polyamide 66, Injection Molding ResinInformation provided by Eurostar. |
|||
| Flexural Strength | 118 MPa | 17100 psi | ASTM D790 |
| A. Schulman ComAlloy Comtuf® 621 Nylon 6/6, Glass Reinforced, Impact Modified, Flow Enhanced Data provided by the manufacturer, ComAlloy International Company.13% Glass Reinforced. Superior toughness and impact resistance characterize Comtuf® materialsThe ComAlloy product line has been int.. |
|||
| Flexural Strength | 118 MPa | 17100 psi | Dry; ASTM D790 |
| Asahi Kasei Leona® 1700S Nylon 66 Similar to 1500 but with even higher molecular weight. Suitable for extrusion of thick-wall parts.Applications:Rods, films Information provided by Asahi Kasei |
|||
| Flexural Strength | 118 MPa | 17100 psi | Dry; ASTM D790 |
| Asahi Kasei Leona® FR200 Nylon 66 UL94 V-0; halogen-free and phosphor-free.Applications:Connectors, switches, and other electrical and electronic parts Information provided by Asahi Kasei |
|||
| Flexural Strength | 118 MPa | 17100 psi | ASTM D-790 |
| Plaskolite West Optix® CP - 82 General Purpose Acrylic Resin Generally unaffected by alkalis, hydrocarbons, non-oxidizing acids, and salt water. Transparent, translucent, opaque, and custom colors in various grades of melt flow rate and heat resistance are av.. |
|||
| Flexural Strength | 118 MPa | 17100 psi | 2.8 mm/min; ASTM D790 |
| Samsung Cheil Industries Infino® GP-3200G PBT/ABS, 20% Glass Filled PBT/ABS with 20% GF reinforcement that can be used in air-conditioner bladesInformation provided by Samsung Cheil Industries. |
|||
| Flexural Strength | 118 MPa | 17100 psi | 2.0 in/min; ASTM D790 |
| LTL Color Compounds ColorFast® NY1 Nylon 6 Injection molding nylon 6, with or without lubeAll information provided by LTL Color Compounders, Inc. |
|||