Polymer Property : Flexural Strength = 15400 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Strength	106 MPa	15400 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics Cycoloy® C7210A PC+ABS (Asia Pacific) Cycoloy* C7210A resin is talc-filled PC+ABS, nonhalogenated FR for thinwall molding applications. Very good modulus-ductility balance.
Flexural Strength	106 MPa	15400 psi
Quadrant EPP Ertacetal® H POM-H, extruded (ISO Data) Ertacetal H is Quadrant’s homopolymer acetal grade. It offers a higher mechanical strength, stiffness, hardness and creep resistance as well as a lower thermal expansion rate and often also a bette..
Flexural Strength	106 MPa	15400 psi	ASTM D790
Quantum Polysulfone Information provided by Quantum Advanced Engineering Plastics
Flexural Strength	106 MPa	15400 psi	ASTM D790
Polymer Resources NY6-GP1-[color]H Nylon, General Purpose, Heat Stabilized (DAM) Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades are tested dry as molded (DAM).Information provide..
Flexural Strength	106 MPa	15400 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Lexan® JK2000 PC+ABS (Asia Pacific) Lexan* JK2000 compound is a glass reinforced, non-Br and non-Cl FR polycarbonate blends designed for thinwall molding applications.
Flexural Strength	106 MPa	15400 psi	ASTM D790
Solvay Specialty Polymers Udel® P-1700 LCD Polysulfone (PSU) (Unverified Data**) Udel P-1700 LCD polysulfone is especially well suited for the fabrication of porous membranes for filtration applications. The membranes are usually in the form of hollow fibers, but tube, plate or ..
Flexural Strength	106 MPa	15400 psi	ASTM D790
Solvay Specialty Polymers Udel® P-3703 Polysulfone (PSU) (Unverified Data**) Udel P-3703 is a high-flow grade of polysulfone intended for injection molding applications with thin walls or long flow lengths. This grade has higher flow than Udel P-1700 and a slightly greater t..
Flexural Strength	106 MPa	15400 psi	ASTM D790
Solvay Specialty Polymers Udel® P-1800 Polysulfone (PSU) (discontinued **) Udel P-1800 is a powdered grade of polysulfone with molecular weight similar to that of Udel P-1700 polysulfone. It is well suited for the fabrication of porous membranes that can be made into hollo..
Flexural Strength	106 MPa	15400 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP LUBRICOMP OL004 PPS - Linear (Europe-Africa-Middle East) LNP* Lubricomp* OL004 is a compound based on PPS - Linear resin containing PTFE.
Flexural Strength	106 MPa	15400 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP LUBRICOMP RAL22 PA 66 (Europe-Africa-Middle East) LNP* LUBRICOMP* RAL22 is a compound based on PA66 resin containing PTFE, Aramid Fiber. Added Features: Internally Lubricated
Flexural Strength	106 MPa	15400 psi	ISO 178
Solvay Specialty Polymers AvaSpireÂ® AV-621 Polyaryletherketone (PAEK) AvaSpireÂ® AV-621 is an unreinforced polyaryletherketone (PAEK) that offers improved ductility and impact strength relative to PEEK while retaining most of the key performance attributes of PEEK. ..
Flexural Strength	106 MPa	15400 psi	ASTM D790
Solvay Specialty Polymers UdelÂ® P-3500 LCD Polysulfone (PSU) UdelÂ® P-3500 LCD is a very high molecular weight grade of polysulfone, and therefore offers the greatest toughness and chemical resistance of the available grades. It is well-suited for extrusion..
Flexural Strength	106 MPa	15400 psi	ISO 178
SABIC Innovative Plastics LNP STAT-KON KEP33 Acetal (Asia Pacific) LNP STAT-KON* KEP33 is a compound based on Acetal resin containing Silicone, Carbon Fiber, PTFE. Added features of this material include: Electrically Conductive.
Flexural Strength	106 MPa	15400 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP THERMOCOMP Lexan_JK2000 PC+ABS LNP* Thermocomp* Lexan_JK2000 compound is a 22% GR, ECO-compliant FR, PC+ABS for thinwall molding applications.
Flexural Strength	106 MPa	15400 psi	ISO 178
Styrolution Polystyrol 168 N GR 21 PS Description: Polystyrol 168 N is a high molecular, heat grade used where high strength is required. Suitable for physically or chemically expanded extruded sheet. As blend component with high impact..
Flexural Strength	106 MPa	15400 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP MF004SU PP LNP* THERMOCOMP* MF004SU is a compound based on Polypropylene containing 20% Glass Fiber. Characteristics of this grade are: Heat Stabilized, Chemically Coupled, UV Stabilized.
Flexural Strength	106 MPa	15400 psi	ISO 178
Styrolution PS 168 N/L GPPS Styrolution PS 168N/L is a high molecular weight, heat resistant grade with high mechanical strength. It is suitable for physically or chemically expanded extruded sheet. It is also suitable for use..
Flexural Strength	106 MPa	15400 psi	ISO 178
Styrolution PS 168N GPPS Styrolution PS 168N is a high molecular weight, heat resistant grade used where high strength is required. Suitable for physically or chemically expanded extruded sheet. Also use as a blend componen..
Flexural Strength	106 MPa	15400 psi	ASTM D790
Solvay Specialty Polymers UdelÂ® P-1700 Polysulfone (PSU) UdelÂ® P-1700 polysulfone (PSU) is a tough, rigid, high-strength thermoplastics suitable for continuous use up to 300Â°F (149Â°C). It is resistant to oxidation and hydrolysis and withstand pro..
Flexural Strength	106 MPa	15400 psi	ISO 178
SABIC Innovative Plastics LNP STAT-LOY PF306 PA 6 LNP* STAT-LOY* PF306 is a compound based on Nylon 6 resin containing 30% Glass Fiber. Added feature of this grade includes: Antistat.
Flexural Strength	106 MPa	15400 psi	ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP MF004S PP LNP THERMOCOMP* MF004S is a compound based on Polypropylene resin containing 20% Glass Fiber. Added features of this material include: Chemically Coupled, Heat Stabilized.
Flexural Strength	106 MPa	15400 psi
Zeon Chemicals Zeonex® E48R Cyclo-Olefin Polymer
Flexural Strength	106 MPa	15400 psi	1.3 mm/min; ASTM D790
A. Schulman POLYFLAM™ E-14526-31 30% Glass Reinforced Chemically Coupled Polypropylene DescriptionPolyfort® E-14526-31 is a 30% glass reinforced chemically coupled polypropylene black. Information provided by A. Schulman.
Flexural Strength	106 MPa	15400 psi	ISO 178
Unitika TERRAMAC TE-2000 Polylactic Acid (PLA) Basic grade, Injection grade. Bio-based materials produced from annually renewable raw materials.Information provided by Unitika Ltd.
Flexural Strength	106 MPa	15400 psi	ASTM D790
Unitika UM-8430RG Characteristics: High dimensional accuracy (circularity and planarity) Large warping resistance Low linear expansion coefficientInformation provided by Unitika Ltd.
Flexural Strength	106 MPa	15400 psi	ISO 178
Azoty Tarnow™ TARNOFORM 300 MW4 POM Mineral filled injection molding grade based on Tarnoform 300 reinforced with 20% wollastonite; such a compound has high stiffness, dimensional stability and hardness combined with low shrinkage.Inf..
Flexural Strength	106 MPa	15400 psi	ASTM D790
Ashley Polymers Ashlene® 829LF Nylon 6 Basic Nylon 6, low viscosity, lubricated. This is FDA approved.Data provided by the manufacturer
Flexural Strength	106 MPa	15400 psi	ISO 178
Solvay Specialty Polymers AvaSpire® AV-621 Polyaryletherketone (PAEK) (Unverified Data**) AvaSpire AV-621 is an unreinforced polyaryletherketone (PAEK) that offers improved ductility and impact strength relative to PEEK while retaining most of the key performance attributes of PEEK. The ..