Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 86.0 MPa | 12500 psi | |
Poco Graphite Glassmate® LT Graphite In very high wear situations, LT, with a hardness rating higher than GM material, will resist wear longer. |
|||
Flexural Strength | 86.2 MPa | 12500 psi | Stress at 5% Strain, Test Method I, Procedure B (chs speed 0.05 in/min); ASTM D790 |
Network Polymers PC-1006 L Description: Colors and Natural Polycarbonate with UVInformation provided by Network Polymers Inc. |
|||
Flexural Strength | 86.2 MPa | 12500 psi | ASTM D790 |
Niche Polymer PPHG20BK Homopolymer PP, 20% Glass Fiber Filled Information provided by Niche Polymer |
|||
Flexural Strength | 86.2 MPa | 12500 psi | ASTM D790 |
Ravago Manufacturing Americas Hylex® P1032L Polycarbonate, Unreinforced Entec's proprietary products include a full range of compounds in the Nylon 6/6, Nylon 6, ABS, PBT, Polycarbonate, PC/ABS, PC/ASA, PC/PBT, and PPO/PPE resin families.Information provided by Ente.. |
|||
Flexural Strength | 86.0 MPa | 12500 psi | ISO 178 |
SABIC Innovative Plastics LNP FARADEX NS003 PC+ABS LNP* FARADEX* NS003 is a compound based on PC+ABS resin containing 15% Stainless Steel. Added features of this material include: Electrically Conductive, EMI/RFI Shielding. |
|||
Flexural Strength | 86.0 MPa | 12500 psi | ASTM D790 |
Resinoid 2205 Phenolic Molding, Cellulose Reinforced Data provided by the manufacturer.The Resinoid 2000 organic fiber reinforced series compounds feature mechanical strength, dimensional stability, and shock resistance |
|||
Flexural Strength | 86.0 MPa | 12500 psi | |
Poco Graphite AXF-5Q Industrial Grade Graphite POCO’s specialty graphite materials are used in a wide range of highly technical and industrial applications. Each grade has characteristics and properties that allow the user to match the ideal gr.. |
|||
Flexural Strength | 86.2 MPa | 12500 psi | ASTM D790 |
PolyOne Lubri-Tech™ ATH-000/2T Acetal-Homopolymer, PTFE Lubricated
(discontinued **) Description/Features:PTFE LubricatedInformation provided by PolyOne Corporation. |
|||
Flexural Strength | 86.2 MPa | 12500 psi | ASTM D790 |
I. Stern WC-102 General Purpose Crystal Polystyrene Features:Good Processing CharacteristicsUL Classification 94 HBExcellent Water ClarityComplies with FDA Title 21 CFR 177.1640ApplicationsExtrusion FoamDisplaysInformation provided by I. Stern & Co. .. |
|||
Flexural Strength | 86.21 MPa | 12500 psi | ASTM D790 |
Lucent Polymers PC/ABS-1020 Polycarbonate+ABS, General Purpose, Injection Grade Add "R" for Added ReleaseAdd "U" for UV StabilizerInformation provided by Lucent Polymers, Inc. |
|||
Flexural Strength | 86.2 MPa @Thickness 3.17 mm, Temperature 22.8 °C |
12500 psi @Thickness 0.125 in, Temperature 73.0 °F |
ASTM D790 |
MRC Polymers NAXELLâ„¢ PC23MS Polycarbonate, Impact Modified, High MFR, EZ Flow Economy GradeImpact modifiedCan be UV stabilizedGenerally for black onlyInternal and external lubricant can be addedInformation provided by MRC Polymers Inc. |
|||
Flexural Strength | 86.0 MPa | 12500 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Valox® V3903WX PBT+PC (Asia Pacific) Unreinforced fllame retardant PBT/PC blends with good chemical resistance and low temperature impact, UV stablized |
|||
Flexural Strength | 86.2 MPa | 12500 psi | ASTM D790 |
A. Schulman SCHULADUR® A GB20 20% Glass Bead Reinforced PBT Information provided by A. Schulman. |
|||
Flexural Strength | 86.2 MPa | 12500 psi | ASTM D790 |
A. Schulman SCHULADUR® A GB20 20% Glass Bead Reinforced PBT Information provided by A. Schulman. |
|||
Flexural Strength | 86.0 MPa | 12500 psi | ASTM D790 |
Adell AI-10 Nylon 66, Impact Modified Data provided by Adell Plastics, Inc. |
|||
Flexural Strength | 86.2 MPa | 12500 psi | ASTM D-790 |
Axiall 7045 Rigid PVC, Extrusion Georgia Gulf 7045 is a special purpose rigid PVC profile extrusion compound designed for applications requiring the following properties: Impact Strength & ToughnessFlame RetardantColorabilityDimen.. |
|||
Flexural Strength | 86.2 MPa | 12500 psi | ASTM D790 |
Asahi Kasei Thermylene® P-15FG-0860 15% Glass Fiber Reinforced, UV Stabilized Information provided by Asahi Thermofil |
|||
Flexural Strength | 86.0 MPa | 12500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP PH0800A PA 6 LNP* THERMOCOMP* PH0800A is a compound based on Nylon 6 resin. Added feature of this material is: High Specific Gravity. |