Polymer Property : Flexural Strength = 98.1 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Strength	98.1 MPa	14200 psi
Shinil Chemical SHINFLAME PC Flame Retardant Polymer Film SHINFLAME is a flame retardant (FR) compound which exhibits inherent flame retardant properties during fire. Shinil uses its patented dispersion blending technology with variety of polymers to prod..
Flexural Strength	98.1 MPa	14200 psi	2.8 mm/min; ASTM D790
Samsung Cheil Industries InfinoÂ® HR-8070 MPPE, Unreinforced Information provided by Samsung Cheil Industries.
Flexural Strength	98.1 MPa	14200 psi	2.8 mm/min; ASTM D790
Samsung Cheil Industries InfinoÂ® NH-1037 PC/ABS, Unreinforced FR Information provided by Samsung Cheil Industries.
Flexural Strength	98.1 MPa	14200 psi	2.8 mm/min; ASTM D790
Samsung Cheil Industries StarexÂ® GR-4010 ABS, 10% Glass Filled Material with 10% GF reinforcement with high stiffness that can be used in refrigerator vegetable boxesInformation provided by Samsung Cheil Industries.
Flexural Strength	98.1 MPa	14200 psi	2.8 mm/min; ASTM D790
Samsung Cheil Industries StarexÂ® GR-4015A ABS, Glass Filled Information provided by Samsung Cheil Industries.
Flexural Strength	98.1 MPa	14200 psi	2.8 mm/min; ASTM D790
Samsung Cheil Industries InfinoÂ® HR-8070 MPPE, Unreinforced Information provided by Samsung Cheil Industries.
Flexural Strength	98.1 MPa	14200 psi	2.8 mm/min; ASTM D790
Samsung Cheil Industries InfinoÂ® NH-1037 PC/ABS, Unreinforced FR Information provided by Samsung Cheil Industries.
Flexural Strength	98.1 MPa	14200 psi	2.8 mm/min; ASTM D790
Samsung Cheil Industries StarexÂ® GR-4010 ABS, 10% Glass Filled Material with 10% GF reinforcement with high stiffness that can be used in refrigerator vegetable boxesInformation provided by Samsung Cheil Industries.
Flexural Strength	98.1 MPa	14200 psi	2.8 mm/min; ASTM D790
Samsung Cheil Industries StarexÂ® GR-4015A ABS, Glass Filled Information provided by Samsung Cheil Industries.
Flexural Strength	98.1 MPa	14200 psi	ASTM D790
E-Polymers TEKAFIN® PH70G1 HIPP + 10% Glass Fiber Reinforced Scratch Resistance Compounded-PP Modified PP: TEKAFIN is modified PP resins formulated with various fillers and modifiers. It has product lines for impact modified, glass fiber reinforced, inorganic filler reinforced and hybrids.I..
Flexural Strength	98.1 MPa	14200 psi	ASTM D790
E-Polymers TEKAMID® H24WC High Toughness Heat Strength PA/ABS Alloy Polyamide (Nylon) Resin. TEKAMID is widely being used in manufacturing of automotive and industrial parts with its outstanding mechanical, thermal and chemical properties.H-series: PA6/ABS, PA66/AB..
Flexural Strength	98.1 MPa	14200 psi	ASTM D790
E-Polymers TEKAPPO® J910 10% Glass Fiber Reinforced M-PPO Modified PPO/PPE: TEKAPPO is a modified PPO/PPE, blending PPO with HIPS in order to improve HDT and processability. It displays various HDT range with halogen-free flammability, impact resistance a..
Flexural Strength	98.1 MPa	14200 psi	ASTM D790
E-Polymers TEKAMID® H12T Unreinforced High Impact PA/ABS Alloy Polyamide (Nylon) Resin. TEKAMID is widely being used in manufacturing of automotive and industrial parts with its outstanding mechanical, thermal and chemical properties.H-series: PA6/ABS, PA66/AB..
Flexural Strength	98.1 MPa	14200 psi	ASTM D790
E-Polymers TEKAMID® H24M10 MF 10% Heat resistance Dimensional stability PA/ABS Alloy Polyamide (Nylon) Resin. TEKAMID is widely being used in manufacturing of automotive and industrial parts with its outstanding mechanical, thermal and chemical properties.H-series: PA6/ABS, PA66/AB..
Flexural Strength	98.1 MPa	14200 psi	2.8mm/min; ASTM D790
Asia International Enterprise (Hong Kong) 3010F Polybutylene terephthalate Information provided by Asia International Enterprise (Hong Kong) Ltd.
Flexural Strength	98.1 MPa	14200 psi	2.8mm/min; ASTM D790
Asia International Enterprise (Hong Kong) 60T6 Nylon 66, 30% Filled Information provided by Asia International Enterprise (Hong Kong) Ltd.
Flexural Strength	98.1 MPa	14200 psi	ASTM D790
E-Polymers SEPAZ® N3040HI Nanoclay 4% High Impact Nano Composite Resin Nanocomposite: SEPAZ Nano PA6 nanocomposites have been prepared successfully in commercial scale through 'in situ' polymerization or melt extrusion. The unique performance properties of nanocomposi..