Polymer Property : Flexural Strength = 96.5 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Strength	96.5 MPa	14000 psi	ASTM D790
PolyOne LubriOne™ NN-000/10T-2S Black Polyamide 66 (Nylon 66) LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. L..
Flexural Strength	96.5 MPa	14000 psi	ASTM D790
Polymer Resources PC-FD1-[color]-1 Polycarbonate, FDA-compliant Feedstocks, Low Flow with Mold Release, Gamma Resistant Polycarbonate, FDA-compliant Feedstocks, Low Flow with Mold Release, Gamma ResistantProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigm..
Flexural Strength	96.5 MPa	14000 psi	ASTM D790
Polymer Resources TP-FR2 Polybutylene Terephthalate, Flame Retardant Polybutylene Terephthalate, Flame Retardant Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided..
Flexural Strength	96.5 MPa	14000 psi	ASTM D790
Ravago Manufacturing Americas Hylex® P1018FRVNHE Polycarbonate Polycarbonate, 18 Melt Flow, Flame Retardant, Non HalogenatedInformation provided by Ravago.
Flexural Strength	96.5 MPa	14000 psi	1.3 mm/min; ASTM D790
PolyOne Edgetek® AT-15CF/000 BLACK Acetal (POM) Copolymer The Edgetek® Engineering Thermoplastic Compounds portfolio covers a broad range of standard and custom-formulated high performance materials. This portfolio includes high-temperature materials for ..
Flexural Strength	96.5 MPa	14000 psi	ASTM D790
Polymer Resources PC-FD1 Polycarbonate, FDA-compliant Feedstocks, Low Flow, Gamma Resistant Polycarbonate, FDA-compliant Feedstocks, Low Flow, Gamma ResistantProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test sample..
Flexural Strength	96.5 MPa	14000 psi	ASTM D790
Quadrant EPP Semitron® CMP LL5 Polyester (ASTM Product Data Sheet) Enhanced semi-crystalline polyester product for extended service in CMP retaining rings. Superior performance, especially in oxide processes, and cost effective relative to standard ring materials. ..
Flexural Strength	96.5 MPa	14000 psi	ASTM D790
PolyOne Lubri-Tech™ PF-000/15T Polysulfone, PTFE Lubricated (discontinued **) Description/Features:PTFE LubricatedUL 94 V0PolyOne First ChoiceInformation provided by PolyOne Corporation.
Flexural Strength	96.5 MPa	14000 psi	ASTM D790
Technetics Group Amicon™ Nylon 6/66 (Unverified Data**) Information provided by Technetics Group (formerly Plastomer Technologies)
Flexural Strength	96.5 MPa	14000 psi	ASTM D790
Techmer ES HiFillÂ® PET GF15 IM 15% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 15% Filler by WeightAdditive: Impact ModifierFeatures: Impact ModifiedInformation provided by TP Composites,..
Flexural Strength	96.5 MPa	14000 psi	ASTM D790
Techmer ES PlaslubeÂ® NY-1/TF/20 NAT PA66
Flexural Strength	96.5 MPa	14000 psi	ASTM D 790
Styrolution PS 1611 GPPS Injection moldingGood balance of flow, strength and set-up propertiesUL Classification 94 HBInformation provided by Styrolution
Flexural Strength	96.5 MPa	14000 psi	ASTM D790
Styron CALIBREâ„¢ 201-10 Polycarbonate Information provided by DowThis product line was spun off from Dow Chemical to Styron in 2010.
Flexural Strength	96.5 MPa	14000 psi	3-points, 2 mm/min; ASTM D790
Styron CALIBREâ„¢ 2061-22 Polycarbonate CALIBREâ„¢ 2061-22 resin is used in applications involving steam or ethylene oxide for sterilization - though suitability for use in these applications is dependent upon autoclave cycle times and..
Flexural Strength	96.5 MPa	14000 psi	Method I (3 point load), 2.0 mm/min; ASTM D790
Styron CALIBREâ„¢ 301V-6 Polycarbonate Resin Overview: CALIBREâ„¢ 301V-6 Polycarbonate resins offer exceptional impact resistance and heat distortion resistance, and meets UL94 V-2 rating. CALIBRE 301V-6 contains a mold release agent and is..
Flexural Strength	96.5 MPa	14000 psi	Method I (3 point load), 2.0 mm/min; ASTM D790
Styron CALIBREâ„¢ 302-10 Polycarbonate Resin Overview: CALIBREâ„¢ 300-10 polycarbonate resins offer exceptional impact resistance, heat distortion resistance and optical clarity as well as high melt strength for blow molding and sheet appli..
Flexural Strength	96.5 MPa	14000 psi	ASTM D790
Styron CALIBREâ„¢ 303-15 Polycarbonate Information provided by DowThis product line was spun off from Dow Chemical to Styron in 2010.
Flexural Strength	96.5 MPa	14000 psi	Method I (3 point load), 2.0 mm/min; ASTM D790
Styron CALIBREâ„¢ MEGARAD 2081-6LR Polycarbonate Resin Overview: CALIBREâ„¢ 2081-6LR Polycarbonate resin was developed for medical applications requiring improved resistance to lipids over standard polycarbonate resins. When exposed to a 20% intralip..
Flexural Strength	96.5 MPa	14000 psi	0.125 in, injection molded, unannealed; ASTM D790
Styron EMERGEâ„¢ 4310-15 Polycarbonate EMERGEâ„¢ PC 4310-15 advanced resin is high-performance polycarbonate resin offering high heat resistance and maximum toughness. Applications: Consumer Electronics and Information Technology Eq..
Flexural Strength	96.5 MPa	14000 psi	ASTM D638
Plastics Group Polifil® GFRMPPCC-40 40% Glass Reinforced Polypropylene, High Impact Polifil® GFRMPPCC series compounds are high impact polypropylenes reinforced with chemically coupled glass fibers. This combination provides higher impact strength while retaining high stiffness.Ap..
Flexural Strength	96.5 MPa	14000 psi	ASTM D790
Chase Plastics CP Pryme® PC310GR Polycarbonate (Utility Grade), 10% Glass Fiber Reinforced, Mold Release Information provided by Chase Plastics.
Flexural Strength	96.5 MPa	14000 psi	ASTM D790
Total PSC 529 Polystyrene Polystyrene 529 is a medium flow crystal specially formulated for mar resistance. The easy to process crystal minimizes visual defects from ejection and automated part handling. Typical applications..
Flexural Strength	96.5 MPa	14000 psi	ASTM D790
Entec Hylex® P1010L2 HB Polycarbonate Available in North America Additive: Mold Release Features: Good Mold Release and Medium Flow RoHS Compliant Form: Pellets Appearance: Blue Information provided by Entec
Flexural Strength	96.5 MPa	14000 psi	ASTM D790
Asahi Kasei Thermylene® P6-30FG-0708 30% Glass Fiber Reinforced, High Impact Information provided by Asahi Thermofil
Flexural Strength	96.5 - 110 MPa	14000 - 16000 psi
Bulk Molding Compounds BMC T15(GPT) General Purpose Molding Compound BMC T15(GPT) is a high strength, low shrink general purpose molding compound. Due to the excellent flow and controlled reactivity, BMC T15(GPT) is well suited for injection, transfer or compression..