Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 93.0 MPa | 13500 psi | ISO 178 |
Nilit FRIANYL A63 N-V2 Nylon 6.6 for injection molding Nylon 6.6 for injection molding, low viscosity, flame retardant, halogen and phosphorus free.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Flexural Strength | 93.0 MPa | 13500 psi | ISO 178 |
Nilit FRIANYL A63 SG15 Nylon 6.6 for injection molding, 15% mineral filled Nylon 6.6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Flexural Strength | 93.0 MPa | 13500 psi | ASTM D790 |
SABIC Innovative Plastics Cycoloy® MC5300 PC+ABS (Asia Pacific) Cycoloy MC5300 resin is a high heat, flame retardant PC/ABS blend. MC5300 resin passes UL-94 listing of 1.5mm V0 and 2.5mm 5VB. The balance of good flow, impact performance and heat resistance makes.. |
|||
Flexural Strength | 93.0 MPa | 13500 psi | ASTM D790 |
SABIC Innovative Plastics Lexan® BPL1000 PC (Asia Pacific) Lexan* BPL1000 Polycarbonate (PC) resin is an injection moldable grade featuring high flow and good impact peroformance. It contains non-chlorinated and non-brominated flame retardant systems with U.. |
|||
Flexural Strength | 93.0 MPa | 13500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Lexan® OQ1022 PC Standard Flow OQ Resin |
|||
Flexural Strength | 93.0 MPa | 13500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Lexan® OQ1022 PC (Asia Pacific) Standard Flow OQ Resin |
|||
Flexural Strength | 93.0 MPa @Temperature 150 °C |
13500 psi @Temperature 302 °F |
ISO 178 |
Solvay Specialty Polymers Amodel® A-1133 HS Polyphthalamide (PPA)
(Unverified Data**) Amodel A-1133 HS is a 33% glass reinforced, heat stabilized polyphthalamide (PPA) with a high heat deflection temperature, high flexural modulus and high tensile strength. Excellent creep resistance.. |
|||
Flexural Strength | 93.0 MPa | 13500 psi | ASTM D790 |
SABIC Innovative Plastics Lexan® ML1665 PC (Asia Pacific) |
|||
Flexural Strength | 93.0 MPa | 13500 psi | ASTM D 790 |
SABIC Innovative Plastics Lexan® SR1400R PC (Asia Pacific) This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
Flexural Strength | 93.0 MPa | 13500 psi | ASTM D790 |
LG Chemical LUCEL N145-02 General Purpose POM, Unreinforced, Externally Lubricated, Ultra High Flow LUCEL semi-crystalline acetal copolymer resins are produced by gas phase polymerization. LUCEL resins can be widely accepted as the replacement of thermosets, aluminum and zinc die-casts or other m.. |
|||
Flexural Strength | 93.0 MPa | 13500 psi | ASTM D 790 |
MRC Polymers NAXELL™ PC210HR General Purpose Polycarbonate, High MFR • Black onlyInformation provided by MRC Polymers Inc. |
|||
Flexural Strength | 93.0 MPa | 13500 psi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP DX96651 PC LNP LUBRICOMP* DX96651 is a compound based on Polycarbonate resin containing Proprietary Filler(s). Added feature of this material is: Wear Resistant. |
|||
Flexural Strength | 93.0 MPa | 13500 psi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP DX96651 PC (Asia Pacific) LNP LUBRICOMP* DX96651 is a compound based on Polycarbonate resin containing Proprietary Filler(s). Added features of this material include: Internally Lubricated. |
|||
Flexural Strength | 93.0 MPa | 13500 psi | 2mm/min; ISO 178 |
Teijin Panlite® LN-3000RM High Light Reflection, Halogen-Free Flame Resistant Polycarbonate Resin Polycarbonate-resin-based halogen-free flame retardant and good light-reflection grade. It exhibits high light-reflection (over 96 %) at whole visible light range and also good light shut-out even a.. |
|||
Flexural Strength | 93.0 MPa | 13500 psi | 2mm/min; ISO 178 |
Teijin Panlite® LV-2225L Standard (mold release/ice color grade) Polycarbonate Resin Flame retardant and mold release grade with high fluidity, while maintaining intrinsic transparency of polycarbonate resin. It is suitable for thin wall injection moldings.Applications:Electric, ele.. |
|||
Flexural Strength | 93.0 MPa | 13500 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
SABIC Innovative Plastics NORYL GTX GTX951W PPE+PA66 (Asia Pacific) A new high flow GTX designed for under-the-hood applications such as power distribution boxes, relay boxes and junction boxes. Developmental name: EXNX0151. |
|||
Flexural Strength | 93.0 MPa | 13500 psi | ISO 178 |
SABIC Innovative Plastics LNP STAT-LOY WF306C PBT LNP* STAT-LOY* WF306C is a compound based on PBT resin containing 30% Glass Fiber. Added features of this material include: Antistat, Clean Compound System. |
|||
Flexural Strength | 93.0 MPa | 13500 psi | ISO 178 |
SABIC Innovative Plastics LNP STAT-LOY WF306C PBT (Asia Pacific) LNP* Stat-loy* WF306C is a compound based on Polybutylene Terephalate resin containing Glass Fiber. Added features of this material include: Antistat, Clean Compounding System. |
|||
Flexural Strength | 93.0 MPa | 13500 psi | 2mm/min; ISO 178 |
Teijin Panlite® L-1250ZW Extrusion Grade Polycarbonate Resin Information provided by Teijin Chemicals Ltd. |
|||
Flexural Strength | 93.0 MPa | 13500 psi | 2mm/min; ISO 178 |
Teijin Panlite® LV-2250Z Transparent and Weather Resistant grade Polycarbonate Resin Typical injection molding grade that has weather resistance and is bluish-tinted to exhibit clear color.Applications:Components of electric, electronic, business machine and industrial equipment com.. |
|||
Flexural Strength | 93.0 MPa | 13500 psi | ASTM D790 |
A. Schulman POLYFORT™ FPP 3710 Glass Filled Homopolymer Polypropylene DescriptionPolyfort® FPP 3710 is a 45% glass filled homopolymer polypropylene product. Information provided by A. Schulman. |
|||
Flexural Strength | 93.0 MPa | 13500 psi | 2 mm/min; ISO 178 |
Covestro Makrolon® 2405 MAS056 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• General purpose• Low.. |
|||
Flexural Strength | 93.0 MPa | 13500 psi | 2 mm/min; ISO 178 |
Chi Mei Kibisan® PN-117 SAN Injection Molding |
|||
Flexural Strength | 93.0 MPa | 13500 psi | ASTM D790, ISO 178 |
EPICHEM Epilon PC IX3000 Polycarbonate, High Impact Characteristics: high fluidity, high impact |
|||
Flexural Strength | 93.0 MPa | 13500 psi | 2 mm/min; ISO 178 |
Eurostar Staramide PB00A PA6, 50% Glass Bead Filled, Injection Molded Staramide PB00A is a 50% Glass Bead Reinforced, Polyamide 6 Injection Molding ResinInformation provided by Eurostar. |
|||
Flexural Strength | 93.0 MPa | 13500 psi | ASTM D790 |
A. Schulman ComAlloy Comtuf® 106 Polypropylene, Glass/Mineral Reinforced, Chemically Coupled, Impact Modified, UL Data provided by the manufacturer, ComAlloy International Company.30% Glass/Mineral Reinforced. Superior toughness and impact resistance characterize Comtuf® materialsThe ComAlloy product line has .. |
|||
Flexural Strength | 93.0 MPa | 13500 psi | ASTM D790 |
A. Schulman ComAlloy Hiloy® 272 Polystyrene Alloy, Glass Reinforced, Flow Enhanced Data provided by the manufacturer, ComAlloy International Company.20% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Flexural Strength | 93.0 MPa | 13500 psi | ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP PH0460A PA 6 (Asia Pacific) LNP* Thermocomp* PH0460A is a compound based on Nylon 6 resin containing High Specific Gravity Filler. Added features of this material include: High Specific Gravity. |
|||
Flexural Strength | 93.0 MPa | 13500 psi | ISO 178 |
Styrolution Luran® S KR 2863 C UV Colored ASA+PC Description: Grade with very high heat resistance for automotive interiors and exteriors as well as electrical parts.Information provided by STYROLUTION, which is a joint venture between BASF and IN.. |
|||
Flexural Strength | 93.0 MPa | 13500 psi | ASTM D790 |
Ashley Polymers Ashlene® PC/ABS Alloy 307 General purpose with high impact, good low temperature properties and high heat resistance.Data provided by the manufacturer |