- Polymer Property : Flexural Strength = 90.0 MPa
Polymer Property : Flexural Strength = 90.0 MPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Flexural Strength | 90.0 MPa | 13100 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Ovation Polymers Nemcon™ E PET 30131 PET PET-Fiber Grade with ESD Range Conductivity with improved processability. Information provided by Ovation Polymers |
|||
| Flexural Strength | 90.0 MPa | 13100 psi | ISO 178 |
| Nilit FRIANYL B63 KF20 Nylon 6 for injection molding, 20% short glass fiber reinforced Nylon 6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
| Flexural Strength | 90.0 MPa | 13100 psi | ISO 178 |
| Nilit FRIANYL B63 KLZ Nylon 6 for injection molding Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
| Flexural Strength | 90.0 MPa | 13100 psi | ISO 178 |
| Nilit FRIANYL B63 UF Nylon 6 for injection molding Nylon 6 for injection molding, highly crystallized, UV stabilizedInformation provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
| Flexural Strength | <= 90.0 MPa | <= 13100 psi | ISO 178 |
| Polykemi AB SCANMID 6 B12^ NH9 Nylon 6, Flame Retardant, Halogen Free Information provided by Polykemi AB |
|||
| Flexural Strength | 90.0 MPa | 13100 psi | 2 mm/min; ISO 178 |
| Hexion Bakelite™ PF 1141 Phenolic Formaldehyde Resin, High Surface Quality, Resistant to High Temperatures, Dishwasher Proof Phenolic molding compound, inorganically/organically filled, glass fiber reinforced, increased heat resistance, hot steam and hot water resistant (not suitable for use of higher voltage).Application.. |
|||
| Flexural Strength | 90.0 MPa | 13100 psi | 2 mm/min; ISO 178 |
| Hexion Bakelite™ PF 38110 Phenolic Formaldehyde Resin, High Surface Quality
(discontinued **) Phenolic molding compound, mainly organically filled.Application areas: Devices for the electrical installation, pan handles, knobs, mainly for compression molding.Information provided by Bak AGBak .. |
|||
| Flexural Strength | 90.0 MPa | 13100 psi | ISO 178 |
| Mitsubishi Xantar® 22 R Polycarbonate Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances .. |
|||
| Flexural Strength | 90.0 MPa | 13100 psi | ISO 178 |
| Mitsubishi Xantar® 25 UR Polycarbonate Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances .. |
|||
| Flexural Strength | 90.0 MPa | 13100 psi | ISO 178 |
| Mitsubishi Xantar® 27 SR FD Polycarbonate Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances .. |
|||
| Flexural Strength | 90.0 MPa | 13100 psi | ISO 178 |
| Mitsubishi Xantar® FC 22 UR Polycarbonate Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances .. |
|||
| Flexural Strength | 90.0 MPa | 13100 psi | ISO 178 |
| Mitsubishi Xantar® FC 25 R Polycarbonate Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances .. |
|||
| Flexural Strength | 90.0 MPa | 13100 psi | ASTM D790 |
| Mitsui APELâ„¢ APL8008T Cyclo Olefin Copolymer (COC) This material possesses many characteristics inherent in polyolefins such as excellent electrical insulating properties and outstanding moisture resistance. In addition, it features good melt proces.. |
|||
| Flexural Strength | 90.0 MPa | 13100 psi | ISO 178-93 |
| Wellman Wellamid® T-731E-BK 10% Reinforced Abrasion Resistant Nylon 6 Description: Abrasion Resistant Nylon 6Information provided by Wellman. |
|||
| Flexural Strength | 90.0 MPa | 13100 psi | ASTM D790 |
| Polyram RamTough PZ503 Polycarbonate, Flame Retardant Flame retardant polycarbonate for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
| Flexural Strength | 90.0 MPa | 13100 psi | ISO 178 |
| Polyram RamTough RZ320G2 Polycarbonate, 10% Glass Fiber, Flame Retardant 10% Glass fiber reinforced, flame retardant polycarbonate for injection molding applications.Information provided by Polyram. |
|||
| Flexural Strength | >= 90.0 MPa @Diameter >=100 mm |
>= 13100 psi @Diameter >=3.94 in |
Perpendicular to laminations; IEC 1212-2 4.1 |
| Hippe PF CC 42 Woven Cotton Cloth Reinforced Phenolic Resin - Round, Molded Tube and Rod Used in mechanical and electrical applications. Coarse weave (18 to 30 threads per cm).Information provided by Hippe. |
|||
| Flexural Strength | 90.0 - 150 MPa | 13100 - 21800 psi | |
| Alliance S-28B Samarium Cobalt Magnetic Material |
|||
| Flexural Strength | 90.0 MPa | 13100 psi | ISO 178 |
| Ascend Performance Materials Vydyne® M344 BLK Nylon 66, Flame Retardant, DAM Vydyne® M344 BLK is a halogenated, unfilled, flame-retardant PA66/6 copolymer designed with excellent strength and toughness. It is lubricated for machine feed and easy mold release and has Underwr.. |
|||
| Flexural Strength | 90.0 MPa | 13100 psi | ASTM D790 |
| Ashley Polymers Ashlene® 528LS Nylon 66 A general purpose Nylon 66, lubricated and heat stabilized for injection molding.Data provided by the manufacturer |
|||
| Flexural Strength | 90.0 MPa | 13100 psi | ASTM D790 |
| Ashley Polymers Ashlene® P252WO PPO A flame retardant resin with excellent heat deflection temperature and good impact strength.Data provided by the manufacturer |
|||
| Flexural Strength | 90.0 MPa | 13100 psi | ASTM D790 |
| Beijing Chemical Industry KAIFA® 101 PBT Resin Unreinforced, good toughnessInformation provided by Beijing Chemical Industry Research Institute (Group) |
|||
| Flexural Strength | 90.0 MPa | 13100 psi | ASTM D790 |
| A. Schulman ComAlloy Voloy® 411 Mineral Reinforced, PBT Alloy, Flame Retardant, UL Data provided by the manufacturer, ComAlloy International Company.25% Mineral Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
| Flexural Strength | 90.0 MPa | 13100 psi | ASTM D790 |
| Beijing Chemical Industry KAIFA® HN301-M30 PA6 Resin Mineral filled, Good flowInformation provided by Beijing Chemical Industry Research Institute (Group) |
|||
| Flexural Strength | 90.0 MPa | 13100 psi | ASTM D790 |
| A. Schulman ComAlloy Hiloy® 212 Polystyrene, Glass Reinforced Data provided by the manufacturer, ComAlloy International Company.20% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
| Flexural Strength | 90.0 MPa | 13100 psi | ISO 178 |
| BLUESTAR BS270 Acetal Copolymer Information provided by Polymer Technology and Services, LLC (PTS). |
|||
| Flexural Strength | 90.0 - 150 MPa | 13100 - 21800 psi | |
| Alliance S-26H Samarium Cobalt Magnetic Material |
|||
| Flexural Strength | 90.0 MPa | 13100 psi | 3.5%; ISO 178 |
| GEHR Plastics PVC-U Polyvinylchloride Polyvinyl chloride is a flame retardant material with an exceptional chemical resistance and also with lower stress cracking. PVC-U shows high mechanical strength, tensile strength and the continuou.. |
|||
| Flexural Strength | 90.0 MPa | 13100 psi | ISO 178 |
| Mitsubishi Xantar® F 22 UR Polycarbonate Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances wher.. |
|||
| Flexural Strength | 90.0 MPa @Temperature 23.0 °C |
13100 psi @Temperature 73.4 °F |
|
| Elisto THERMOSTAR® MD 100 Pattern material Densified laminated woodInformation provided by elisto |
|||