- Polymer Property : Flexural Strength = 76.0 MPa
Polymer Property : Flexural Strength = 76.0 MPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Flexural Strength | 76.0 MPa | 11000 psi | ASTM D790 |
| Plaskolite West Optix® CA-927 Impact Modified Acrylic Resin Injection Molding Grade Pellets. Better impact strength than CA-924. Excellent surface gloss, optical clarity, and practical toughness. |
|||
| Flexural Strength | 76.0 MPa | 11000 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics LNP KONDUIT PX08322 PA 6 (Europe-Africa-Middle East) Thermally conductive mineral filled PA6 non-halogen FR compound |
|||
| Flexural Strength | 76.0 MPa | 11000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics LNP KONDUIT PX11311 PA 6 (Asia Pacific) Thermally conductive mineral filled PA6 FR compound |
|||
| Flexural Strength | 76.0 MPa | 11000 psi | ASTM D790 |
| Resinoid 2225 Phenolic Molding, Cellulose Reinforced Data provided by the manufacturer.The Resinoid 2000 organic fiber reinforced series compounds feature mechanical strength, dimensional stability, and shock resistance |
|||
| Flexural Strength | 76.0 MPa | 11000 psi | |
| Cookson Group Plaskon® 150.401 Encapsulation Resin
(discontinued **) Test specimens were transfer molded and post cured 4 hours at 175°C.A second generation SMT-B family product. This material is the initial developmental, general purpose SMT-B encapsulation grade .. |
|||
| Flexural Strength | 76.0 MPa | 11000 psi | ASTM D790 |
| LG Chemical LUPOY HR-5007AX Heat Resistant PC/ABS Alloy, Unreinforced Among the characteristics of LUPOY polycarbonate resins are excellent mechanical properties, high heat resistance, high impact strength, and dimensional stability.Applications:Automotive: Automotive.. |
|||
| Flexural Strength | 76.0 MPa | 11000 psi | ASTM D790 |
| KYDEX® 110 Metallic Thermoplastic Fire-rated Sheet Features:For deep or hard to form parts where good finished detail is requiredMore rigid than most thermoplastics, parts deform less when loadedMeets highest standard for chemical resistance for the.. |
|||
| Flexural Strength | 76.0 MPa | 11000 psi | ASTM D790 |
| SABIC Innovative Plastics LNP LUBRICOMP KP004AXC Acetal Homopolymer LNP LUBRICOMP* KP004AXC is a compound based on Acetal Homopolymer resin containing 20% PTFE/Silicone. Added feature of this material is: Wear Resistant. |
|||
| Flexural Strength | 76.0 MPa | 11000 psi | ISO 178 |
| SABIC Innovative Plastics LNP LUBRICOMP KP004AXC Acetal Homopolymer LNP LUBRICOMP* KP004AXC is a compound based on Acetal Homopolymer resin containing 20% PTFE/Silicone. Added feature of this material is: Wear Resistant. |
|||
| Flexural Strength | 76.0 MPa | 11000 psi | ISO 178 |
| SABIC Innovative Plastics LNP LUBRICOMP QAP22S PA6.10 LNP* LUBRICOMP* QAP22S is a compound based on Nylon 6/10 resin containing 10% PTFE/Silicone, 10% Aramid Fiber. Added features of this material include: Wear Resistant, Heat Stabilized. |
|||
| Flexural Strength | 76.0 MPa | 11000 psi | ISO 178 |
| SABIC Innovative Plastics LNP LUBRICOMP ZX07421 PPO LN:* LUBRICOMP* ZX07421 is a compound based on PPO resin containing proprietary fillers. Added feature of this grade is: Wear Resistant. |
|||
| Flexural Strength | 76.0 MPa | 11000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics LNP THERMOCOMP AFB42 ABS LNP* THERMOCOMP* AFB42 is a compound based on ABS containing 10% Glass Fiber, 20% Glass Bead. |
|||
| Flexural Strength | 76.0 MPa | 11000 psi | |
| Sumitomo Bakelite Durez® 153 Phenolic, Compression Grade Durez 153 Black Phenolic is a two-stage, asbestos-free, heat resistant/electrical molding material. It exhibits good molded appearance and shock resistance for use on a wide variety of electrical a.. |
|||
| Flexural Strength | 76.0 MPa | 11000 psi | ISO 178 |
| SABIC Innovative Plastics LNP Stat-kon DS0029 PC LNP STAT-KON* DS0029 is a compound based on Polycarbonate resin containing Stainless Steel. Added features of this material include: Electrically Conductive.This data was supplied by SABIC-IP for t.. |
|||
| Flexural Strength | 76.0 MPa | 11000 psi | ISO 178 |
| SABIC Innovative Plastics LNP THERMOCOMP MX89510 PP LNP* THERMOCOMP* MX89510 is a compound based on Polypropylene resin containing Proprietary Filler(s). |
|||
| Flexural Strength | 76.0 MPa | 11000 psi | |
| Sumitomo Bakelite Durez® 25378 Phenolic, Injection Grade Durez 25378 Black Phenolic is a two stage heat resistant/electrical grade molding material having an excellent molded finish, low shrinkage and good heat resistance. Durez 25378 has exceptional UL .. |
|||
| Flexural Strength | 76.0 MPa | 11000 psi | ASTM D790 |
| Plenco 2571 Phenolic, Granular, Transfer Molded PLENCO 02571 is a general purpose, organic filled phenolic molding compound offering optimum cure characteristics while maintaining excellent mechanical and electrical properties. UL recognized unde.. |
|||
| Flexural Strength | 76.0 MPa | 11000 psi | ASTM D790 |
| Unitika AX-1500 Conditioned AX series resins are opaque polymer alloys with a high deflection temperature under load without reinforcement and a chemical resistance as high as those of crystalline resins. They are excellent in.. |
|||
| Flexural Strength | 76.0 MPa | 11000 psi | |
| Cosmic Plastics ID-50 Dacron Filled Ortho Diallyl Phthalate Molding Compound Data provided by the manufacturer. |
|||
| Flexural Strength | 76.0 MPa | 11000 psi | ASTM D790 |
| Plenco 4300 Phenolic, Granular, Compression Molded PLENCO 04300 is a heat resistant, mineral filled phenolic molding compound offering optimum cure characteristics and excellent dimensional stability. It is formulated for wiring devices and electric.. |
|||
| Flexural Strength | 76.0 MPa | 11000 psi | |
| Cosmic Plastics K43 Mineral Filled Iso Diallyl Phthalate Molding Compound Data provided by the manufacturer. |
|||
| Flexural Strength | 76.0 MPa | 11000 psi | ASTM D790 |
| Videolar 500 Crystal Polystyrene (GPPS) Designed for injection moldingVery easy flowing grade for fast cycle injection moldingExcellent processability for filling thin partsFeatures: Good strengthGood temperature resistanceExcellent clari.. |
|||
| Flexural Strength | 76.0 MPa | 11000 psi | 2 mm/min; ISO 178 |
| Chi Mei Polylac® PA-757 ABS High gloss, medium impact |
|||
| Flexural Strength | 76.0 MPa | 11000 psi | 2 mm/min; ISO 178 |
| Chi Mei Polyrex® PG-80N Polystyrene High strength |
|||
| Flexural Strength | 76.0 MPa | 11000 psi | 23°C, 50% RH; ASTM D790 |
| Asahi Kasei Xyron® X5402 PPE/PA Oil ResistantInformation provided by Asahi Kasei |
|||
| Flexural Strength | 76.0 MPa @Temperature 120 °C |
11000 psi @Temperature 248 °F |
ASTM Test |
| BASF Ultramid® 8231G HS 14% Glass Filled PA6 (Dry) Ultramid 8231G HS is a heat stabilized, 14% glass fiber reinforced nylon 6 injection molding compound. It is also available in non-heat stabilized (Ultramid 8231) and/or pigmented versions. The gla.. |
|||
| Flexural Strength | 76.0 MPa | 11000 psi | ISO 178 |
| BASF Ultradur® B 6550 LN PBT Description: High-viscosity grades for the extrusion of loose buffer tubes for optical fibers, semi-finished products for machining, profiles and pipes.Information provided by BASF |
|||
| Flexural Strength | 76.0 MPa | 11000 psi | |
| Cosmic Plastics 224 Dacron Filled Ortho Diallyl Phthalate Molding Compound Data provided by the manufacturer. |
|||
| Flexural Strength | 76.0 MPa | 11000 psi | |
| Cosmic Plastics D44 Mineral Filled Ortho Diallyl Phthalate Molding Compound Data provided by the manufacturer. |
|||