Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 74.0 MPa | 10700 psi | ISO 178 |
Nilit FRIANYL B63 SG 10 Nylon 6 for injection molding, 10% mineral filled Nylon 6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Flexural Strength | 74.0 MPa | 10700 psi | 2mm/min; ASTM D790 |
Kingfa MAC-501 Modified PC/ABS Alloy Features:Excellent balance propertiesGood weather resistanceGood impact strengthGood processing propertiesSuit for electro-platingApplications:Injection moldingAutomobile license plateWater tank cov.. |
|||
Flexural Strength | 74.0 MPa | 10700 psi | 2mm/min; ASTM D790 |
Kingfa PA66-R0N Flame Retardant PA66 Features:Flame retardantHigh strengthHigh temperature propertiesGood electric propertiesNo bloomingApplications:Injection moldingConnectorsRelay, bobbins, plugsHousehold appliance partsE & E partsIn.. |
|||
Flexural Strength | 74.0 MPa | 10700 psi | ASTM D790 |
Kolon KOCETAL® MS301 Wear Modified Acetal Resin Molybdenum disulfide added, improved wear property. Applications: Products for low noise and friction against metal. Information provided by API-Kolon. |
|||
Flexural Strength | 74.0 MPa | 10700 psi | ASTM D790 |
Kolon KOCETAL® SO301 Wear Modified Acetal Resin Silicone Oil added, improved wear property. Information provided by API-Kolon. |
|||
Flexural Strength | 74.0 MPa @Strain 7.10 % |
10700 psi @Strain 7.10 % |
d.a.m., 2 mm/min; ISO 178-A |
Lanxess Durethan® DP 2325 H3.0 DUS031 000000 Nylon 66 PA 66, non-reinforced, injection molding, improved flowability, impact modified, heat-aging stabilizedInformation provided by LANXESS. |
|||
Flexural Strength | 74.0 MPa @Temperature 22.0 °C |
10700 psi @Temperature 71.6 °F |
25 mm wide 100 mm long, flat samples; ISO 14125 |
Menzolit Menzolit® BMC 3000 Unsaturated Polyester UP BMC 3000 is a special BMC suitable for the use in microwave and cookware applications.It has high temperature resistance, and meets requirements for food contact applications. It has a high gloss fi.. |
|||
Flexural Strength | 74.0 MPa | 10700 psi | ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP IAL12 PA6.12 LNP* LUBRICOMP* IAL12 is a compound based on Nylon 6/12 resin containing 5% PTFE, 10% Aramid Fiber. Added features of this material include: Internally Lubricated. |
|||
Flexural Strength | 74.0 MPa | 10700 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP WL0049 PBT LNP* LUBRICOMP* WL0049 is a compound based on PBT containing 20% PTFE. Added features include: Wear Resistant, Flame Retardant. |
|||
Flexural Strength | 74.0 MPa | 10700 psi | ISO 178 |
SABIC Innovative Plastics LNP LUBRILOY D20001 PPO LNP* LUBRILOY* Z20001 is a compound based on PPO resin containing Proprietary Lubricant. Added features of this material include: Wear Resistant, Flame Retardant. |
|||
Flexural Strength | 74.0 MPa | 10700 psi | ISO 178 |
SABIC Innovative Plastics LNP LUBRILOY RX99650 PA 66 LNP LUBRILOY* RX99650 is a compound based on Nylon 66 resin containing Proprietary Lubricant. Added feature of this material is: Wear Resistant. |
|||
Flexural Strength | 74.0 MPa | 10700 psi | ISO 178 |
SABIC Innovative Plastics LNP LUBRILOY RX99650 PA 66 (Europe-Africa-Middle East) LNP LUBRILOY* RX99650 is a compound based on Nylon 66 resin containing Proprietary Lubricant. Added features of this material include: Internally Lubricated. |
|||
Flexural Strength | 74.0 MPa | 10700 psi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRILOY Z2000 PPE+PS (Asia Pacific) LNP* Lubriloy* Z2000 is a compound based on PPE+PS Blend resin containing Proprietary Lubricant. Added features of this material include: Internally Lubricated. |
|||
Flexural Strength | 74.0 MPa | 10700 psi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRILOY Z2000 PPO LNP* LUBRILOY* Z2000 is a compound based on PPO resin containing Proprietary Lubricant. Added feature of this material is: Wear Resistant. |
|||
Flexural Strength | 74.0 MPa | 10700 psi | ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP WH0270B PBT (Asia Pacific) LNP THERMOCOMP* WH0270B is a compound based on Polybutylene Terephalate resin containing High Specific Gravity Filler. Added features of this material include: High Specific Gravity. |
|||
Flexural Strength | 74.0 MPa | 10700 psi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOTUF V1000 PA 66 LNP THERMOTUF* V1000 is a compound based on Nylon resin. Added features of this material include: High Impact. |
|||
Flexural Strength | 74.0 MPa | 10700 psi | Outer Fiber Stress at 3.5% Outer Fiber Strain; DIN EN ISO 178 |
Wolf Kunststoff ZEDEX® ZX-530 A5D Polymer Alloy Main Characteristics: Low Creep; Low moisture absorption; Flame retardant; Low impurity ions; Good machinability; FDA compliant LABS; Extremely low outgassing; Less expensive than PEEK; Stress resis.. |
|||
Flexural Strength | 74.0 MPa | 10700 psi | ASTM D790 |
Plenco 4504 Phenolic, Granular, Compression Molded Plenco 04504 is a renumber of Plaslok 504. Plenco 04504 is a two-stage, mineral and cellulose-filled phenolic molding compound having better impact and heat resistance than general purpose molding c.. |
|||
Flexural Strength | 74.0 MPa | 10700 psi | ISO 178 |
Cyclics CBT® 100 Thermoplastic Resin CBT® 100 resin melts to a water-like viscosity when heated, then polymerizes into the engineering thermoplastic resin polybutylene terephthalate (PBT). CBT 200 resin has a processing range between.. |
|||
Flexural Strength | 74.0 MPa | 10700 psi | ISO 178 |
Cyclics CBT® 200 Thermoplastic Resin CBT® 200 resin melts to a water-like viscosity when heated, then polymerizes into the engineering thermoplastic resin polybutylene terephthalate (PBT). CBT 200 resin has a processing range between.. |
|||
Flexural Strength | 74.0 MPa | 10700 psi | ISO 178 |
Denka MALECCA K-090 ABS A heat-resistant ABS resin based on "DENKA IP" – a Styrene-N-Phenylmaleimide copolymer. It has been designed as an easy-to-use resin by improving conventional heat-resistant ABS resins which had de.. |
|||
Flexural Strength | 74.0 MPa | 10700 psi | 15mm/min; ASTM D790 |
Denka MALECCA K-095 ABS A heat-resistant ABS resin based on "DENKA IP" – a Styrene-N-Phenylmaleimide copolymer. It has been designed as an easy-to-use resin by improving conventional heat-resistant ABS resins which had de.. |
|||
Flexural Strength | 74.0 MPa @Strain 3.50 % |
10700 psi @Strain 3.50 % |
ISO 178 |
DuPont Performance Polymers Delrin® FG100P NC010 Acetal (POM)
(Unverified Data**) High Viscosity Acetal Homopolymer Developed for Food Contact Applications Delrin FG100P is a high viscosity acetal homopolymer with improved thermal stability for use in easy to fill molds. It has b.. |
|||
Flexural Strength | 74.0 MPa | 10700 psi | ASTM D790 |
Diamond Polymers NYLON 6650HSL Black Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc. |
|||
Flexural Strength | 74.0 MPa | 10700 psi | ISO 178 |
Azoty Tarnow™ TARNOFORM 300 GB6 POM 30% glass beads filled grade with increased stiffness and hardness with lowered shrinkageInformation provided by Zakłady Azotowe w Tarnowie-Moscicach S.A. |
|||
Flexural Strength | 74.0 MPa | 10700 psi | 23°C, 50% RH; ASTM D790 |
Asahi Kasei Xyron® 240V Modified Polyphenylene Ether Flame RetardantInformation provided by Asahi Kasei |
|||
Flexural Strength | 74.0 MPa @Strain 5.00 %, Temperature 23.0 °C |
10700 psi @Strain 5.00 %, Temperature 73.4 °F |
ASTM D790 |
DuPont Performance Polymers Delrin® 577 BK000 Acetal Homopolymer
(Unverified Data**) Delrin® 577 BK000 is a medium viscosity acetal homopolymer containing 20% glass fiber filler, with high stiffness, low warpage and low creep for superior performance at elevated temperature. It con.. |
|||
Flexural Strength | 74.0 MPa | 10700 psi | 23°C, 50% RH; ASTM D790 |
Asahi Kasei Xyron® X5403 PPE/PA Oil ResistantInformation provided by Asahi Kasei |
|||
Flexural Strength | 74.0 MPa | 10700 psi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOTUF V1000 PA 66 (Asia Pacific) LNP THERMOTUF* V1000 is a compound based on Nylon resin. Added features of this material include: High Impact. |
|||
Flexural Strength | 74.0 MPa | 10700 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP JF002R PES (Europe-Africa-Middle East) LNP* Thermocomp* JF002R is a compound based on Polyethersulfone resin containing Glass Fiber, Glass Bead. Added features of this material include: Mold Release. |