Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 64.0 MPa | 9280 psi | ISO 178 |
PolyOne OnFlex™ BIO 5180D-E0014 Thermoplastic Elastomer (TPE) OnFlex™ BIO 5100 series thermoplastic elastomer compounds are glass reinforced thermoplastic polyurethane compounds made from renewable natural sources. These compounds contain at least 20% renewab.. |
|||
Flexural Strength | 64.0 MPa | 9280 psi | ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP DBP32EI PC LNP* Lubricomp* DBP32EI is a compound based on Polycarbonate resin containing 15% PTFE/Silicone and 10% Glass Bead. Added features of this material include: Internally Lubricated. |
|||
Flexural Strength | 64.0 MPa | 9280 psi | ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP DBP32EI PC (Asia Pacific) LNP* Lubricomp* DBP32EI is a compound based on Polycarbonate resin containing PTFE, Carbon Fiber. Added features of this material include: Electrically Conductive, Internally Lubricated. |
|||
Flexural Strength | 64.0 MPa | 9280 psi | at 3.5% strain; ISO 178 |
FKuR Kunststoff Bio-Flex® F 6510 Compostable PLA Blend The BIO-FLEX® trade name indicates blends of co-polyester and PLA* with, depending on the particular grade, a very high content of natural resource material. BIO-FLEX® does not contain any sta.. |
|||
Flexural Strength | 64.0 MPa | 9280 psi | 2mm/min; ASTM D790 |
Kingfa H-12 Modified ABS Features:UL94 HB @ 1.6-3.0mmHigh toughnessHeat resistanceApplications:Automobile exterior trimAutomobile interior trimPower toolsInformation Provided by Kingfa Sci. & Tech. Co., Ltd. |
|||
Flexural Strength | 64.0 MPa | 9280 psi | ASTM D790 |
Kolon KOCETAL® UR302 Toughened Grade Acetal Resin TPU added, improved toughness. Applications: Impact resistant, flexible products. Information provided by API-Kolon |
|||
Flexural Strength | 64.0 MPa | 9280 psi | ASTM D790 |
SABIC Innovative Plastics NORYL SEH80 PPE+HIPS (Asia Pacific) PPE/HIPS unfilled FR-V1 80C UV improved |
|||
Flexural Strength | 64.0 MPa | 9280 psi | ISO 178 |
SABIC Innovative Plastics LNP Lubricomp KZL34 POM LNP* Lubricomp* KZL34 is a compound based on Acetal resin containing Milled Glass and PTFE. Characteristic of this grade is Internally Lubricated.This data was supplied by SABIC-IP for the Americas.. |
|||
Flexural Strength | 64.0 MPa | 9280 psi | ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP AX06437 ABS LNP* THERMOCOMP* AX06437 is a compound based on ABS resin containing Proprietary Filler(s). Added feature of this grade is: Platable. |
|||
Flexural Strength | 64.0 MPa | 9280 psi | ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP AX08306 ABS LNP* THERMOCOMP* AX08306 is a compound based on ABS resin containing Proprietary Filler(s). Added feature of this grade is: Platable. |
|||
Flexural Strength | 64.0 MPa | 9280 psi | ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP AX08306 ABS (Asia Pacific) LNP* Thermocomp* AX08306 is a compound based on Acrylonitrile Butadiene Styrene resin containing Mineral. |
|||
Flexural Strength | 64.0 MPa | 9280 psi | ISO 178 |
SABIC Innovative Plastics LNP THERMOTUF V1000 PA 66 LNP THERMOTUF* V1000 is a compound based on Nylon resin. Added features of this material include: High Impact. |
|||
Flexural Strength | 64.0 MPa | 9280 psi | ASTM D790 |
SABIC Innovative Plastics NORYL PX2790C PPE+HIPS (Asia Pacific) PPE/HIPS unfilled FR-V1, 90C |
|||
Flexural Strength | 64.0 MPa | 9280 psi | ASTM D790 |
Plenco 5118 Phenolic, Granular, Injection Molded PLENCO 05118 is a mineral and graphite filled phenolic molding compound, formulated for bearing seals. 05118 provides for a low coefficient of friction, abrasion resistance, minimal water absorptio.. |
|||
Flexural Strength | 64.0 MPa | 9280 psi | ISO 178 |
Eastman DuraStar DS2000 Polymer, Natural Durastar DS2000 polymer has excellent appearance and is nearly water-clear. Its most outstanding features are toughness, chemical resistance, and excellent processing characteristics. DS2000 has ver.. |
|||
Flexural Strength | 64.0 MPa | 9280 psi | ISO 178 |
Eastman DuraStar MN621 Polymer, Natural Durastar Polymer MN621 was developed for the medical device industry and contains a mold release It processes easily and requires minimal drying time. It has superior toughness, high clarity and goo.. |
|||
Flexural Strength | 64.0 MPa | 9280 psi | ISO 178 |
Eastman Eastar BR203 Copolyester Eastar BR203 Copolyester contains a mold release additive. It has excellent appearance and is nearly water-clear. Its most outstanding features are its chemical resistance and processing capabilitie.. |
|||
Flexural Strength | 64.0 MPa | 9280 psi | ASTM D790 |
Eastman Tritan TX1800 Copolyester Applications:Consumer and durable goodsExtrusion blow moldingInjection stretch blow moldingKey Attributes:Ease of processingExcellent clarityExcellent Hydrolytic stabilityGood chemical resistanceGoo.. |
|||
Flexural Strength | 64.0 MPa | 9280 psi | ASTM D790 |
Eastman Tritan TX1801 Copolyester, Natural Applications:Consumer and durable goodsExtrusion blow moldingInjection stretch blow moldingKey Attributes:Ease of processingExcellent clarityExcellent Hydrolytic stabilityGood chemical resistanceGoo.. |
|||
Flexural Strength | 64.0 MPa | 9280 psi | 2 mm/min; ISO 178 |
Chi Mei Polylac® PA-726 ABS Electro-plating |
|||
Flexural Strength | 64.0 MPa | 9280 psi | ISO 178 |
Denka TE-10 Transparent Resin Polymer (MABS resin) ABS "TX Polymer" (methyl methacrylate styrene), MS resins as an alternative to acrylic resins, with low density, low moisture absorption, and good moldability, "TH Polymer/TP Polymer," MBS resins with a.. |
|||
Flexural Strength | 64.0 MPa | 9280 psi | ASTM D790 |
Entec Hypro™ PPC-GF20 Natural Impact Polypropylene, 20% Glass Reinforced Information provided by Entec |
|||
Flexural Strength | 64.0 MPa | 9280 psi | ISO 178 |
Eurostar Star L POM D51 POM, Injection Molded Star L POM D51 is a PTFE Lubricated, POM Copolymer Injection Molding ResinInformation provided by Eurostar. |
|||
Flexural Strength | 64.0 MPa | 9280 psi | 15mm/min; ASTM D790 |
Denka MALECCA K-600 ABS A heat-resistant ABS resin based on "DENKA IP" – a Styrene-N-Phenylmaleimide copolymer. It has been designed as an easy-to-use resin by improving conventional heat-resistant ABS resins which had de.. |
|||
Flexural Strength | 64.0 MPa | 9280 psi | ASTM D790 |
Aclo Accutech Polypropylene Homopolymer HP0339G10M20CL Glass/Mineral Reinforced Coupled |
|||
Flexural Strength | 64.0 MPa | 9280 psi | 23°C, 50% RH; ASTM D790 |
Asahi Kasei Xyron® 140V Modified Polyphenylene Ether Flame RetardantInformation provided by Asahi Kasei |
|||
Flexural Strength | 64.0 MPa | 9280 psi | ASTM D790 |
Beijing Chemical Industry KAIFA® M104N MPPO Resin High flame retardant, Good flowInformation provided by Beijing Chemical Industry Research Institute (Group) |
|||
Flexural Strength | 64.0 MPa | 9280 psi | ASTM D790 |
Beijing Chemical Industry KAIFA® M104 MPPO Resin Flame retardant, Good flowInformation provided by Beijing Chemical Industry Research Institute (Group) |
|||
Flexural Strength | 64.0 MPa | 9280 psi | ISO 178 |
SABIC Innovative Plastics LNP THERMOTUF V1000 PA 66 (Asia Pacific) LNP THERMOTUF* V1000 is a compound based on Nylon resin. Added features of this material include: High Impact. |