Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 63.0 MPa | 9140 psi | ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP AL002 ABS (Asia Pacific) LNP* LUBRICOMP* AL002 is a compound based on Acrylonitrile Butadiene Styrene resin containing PTFE. Added features of this material include: Internally Lubricated. |
|||
Flexural Strength | 63.0 MPa | 9140 psi | ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP AL002 ABS LNP LUBRICOMP* AL002 is a compound based on Acrylonitrile Butadiene Styrene resin containing 10% PTFE. Added features of this material include: Internally Lubricated. |
|||
Flexural Strength | 63.0 MPa | 9140 psi | ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP AL002 ABS (Europe-Africa-Middle East) LNP* LUBRICOMP* AL002 is a compound based on Acrylonitrile Butadiene Styrene resin containing PTFE. Added features of this material include: Internally Lubricated. |
|||
Flexural Strength | 63.0 MPa | 9140 psi | 2mm/min; ASTM D790 |
Kingfa CPA-6 Toughened PA6 Features:High impactLow tendency to wrapApplications:Injection moldingSport applianceAutomobile partsPower toolsInformation Provided by Kingfa Sci. & Tech. Co., Ltd. |
|||
Flexural Strength | 63.0 MPa | 9140 psi | 5 mm/min; ISO 178 |
Gromax BTE45-DN00N1 Nylon 6 (Dry) Information provided by Gromax Enterprises Corp. |
|||
Flexural Strength | 63.0 MPa | 9140 psi | ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP DL004 PC LNP* Lubricomp* DL004 is a compound based on Polycarbonate resin containing 20% PTFE. Added features of this material include: Internally Lubricated. |
|||
Flexural Strength | 63.0 MPa | 9140 psi | ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP DL004 PC (Asia Pacific) LNP* Lubricomp* DL004 is a compound based on Polycarbonate resin containing PTFE. Added features of this material include: Internally Lubricated. |
|||
Flexural Strength | 63.0 MPa | 9140 psi | ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP DZL34E PC LNP* Lubricomp* DZL34E is a compound based on Polycarbonate resin containing 20% Milled Glass, 15% PTFE. Added features of this material include: Internally Lubricated. |
|||
Flexural Strength | 63.0 MPa | 9140 psi | ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP DZL34E PC (Asia Pacific) LNP* Lubricomp* DZL34E is a compound based on Polycarbonate resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated. |
|||
Flexural Strength | 63.0 MPa | 9140 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP KP004 Acetal LNP LUBRICOMP* KP004 is a compound based on Acetal Copolymer resin containing 20% PTFE/Silicone. Added feature of this material is: Wear Resistant. |
|||
Flexural Strength | 63.0 MPa | 9140 psi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP KP004XXP Acetal Copolymer LNP LUBRICOMP* KP004XXP is a compound based on Acetal Copolymer resin containing 20% PTFE/Silicone. Added feature of this material is: Wear Resistant. |
|||
Flexural Strength | 63.0 MPa | 9140 psi | ISO 178 |
SABIC Innovative Plastics LNP Stat-loy K3000 Acetal Copoly LNP* Stat-loy* K3000 is a compound based on Acetal Copolymer resin containing Anti-Static. Added features of this material include: Antistat.This data was supplied by SABIC-IP for the Americas regi.. |
|||
Flexural Strength | 63.0 MPa | 9140 psi | ISO 178 |
SABIC Innovative Plastics LNP Stat-loy K3000 Acetal Copoly (Asia Pacific) LNP* Stat-loy* K3000 is a compound based on Acetal Copolymer resin containing Anti-Static. Added features of this material include: Antistat.This data was supplied by SABIC-IP for the Asia Pacific .. |
|||
Flexural Strength | 63.0 MPa | 9140 psi | 2 mm/min; ISO 178 |
Styrolution Novodur® P2M-V ABS Pellets Novodur® P2M-V has high impact strength, high gloss, and low emission. It is used for the production of molded plastic articles. |
|||
Flexural Strength | 63.0 MPa | 9140 psi | ASTM D790 |
SABIC Innovative Plastics NORYL PX2790 PPE+HIPS (Asia Pacific) PPE/HIPS unfilled FR-V1, 90C |
|||
Flexural Strength | 63.0 MPa | 9140 psi | ISO 178 |
SABIC Innovative Plastics LNP STAT-LOY NX13401 PC+ABS LNP* STAT-LOY* NX13401 is a compound based on PC+ABS blend. Added features of this material include: Antistat, Flame Retardant, Excellent Release. |
|||
Flexural Strength | 63.0 MPa | 9140 psi | ASTM D 790 |
SABIC Innovative Plastics Noryl GTX GTX6010 PPE+PA6 (Asia Pacific) PA6 based unfilled GTX. High impact.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
Flexural Strength | 63.0 MPa | 9140 psi | ASTM D790 |
Teknor Apex Sinpolene GPP1610 Polypropylene Availability: Africa & Middle East; Latin America; Asia Pacific; South America Additive: Glass Fiber Reinforcement, 10% Filler by Weight Features: Good Dimensional Stability; High Heat Resistance; .. |
|||
Flexural Strength | 63.0 MPa | 9140 psi | ASTM D790 |
Plenco 4466 Phenolic, Granular, Compression Molded PLENCO 04466 is a heat resistant, mineral and flock filled phenolic molding compound, offering excellent mechanical strength and cosmetic properties. UL recognized under component file E40654. 04466.. |
|||
Flexural Strength | 63.0 MPa | 9140 psi | ASTM D790 |
Plenco 5350 Phenolic, Granular, Compression Molded PLENCO 05350 is a mineral and graphite filled phenolic molding compound, developed for seal applications. PLENCO 05350 offers excellent dimensional stability, lubricity, and low abrasion properties... |
|||
Flexural Strength | 63.0 MPa @Thickness 3.17 mm |
9140 psi @Thickness 0.125 in |
chs 0.05 in/min; ASTM D790 |
Diamond Polymers ABS 9950 Injection Molding Grade Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc. |
|||
Flexural Strength | 63.0 MPa | 9140 psi | chs 0.05 in/min; ASTM D790 |
Diamond Polymers Centrex® HGM Automotive Grade, Injection Molding Grade Centrex HGM resin is an exceptionally high-gloss grade of ASA (acrylonitrile-styrene-acrylate). This injection molding grade has excellent gloss retention, excellent resistance to chemicals and high.. |
|||
Flexural Strength | 63.0 MPa | 9140 psi | 2 mm/min; ISO 178 |
Eurostar Staramide Z1000XXC PA66, Injection Molded Staramide Z1000XXC is an UV Stabilized Polyamide 66 Injection Molding Resin (also known as R1000HI0944)Information provided by Eurostar. |
|||
Flexural Strength | 63.0 MPa | 9140 psi | After conditioning at 23°C and 50% RH; ISO 178 |
Arkema Group Orgalloy® R 60 ES Polyamide Alloy Polyamide Alloy, Film and PackagingInformation provided by Arkema Group |
|||
Flexural Strength | 63.0 MPa | 9140 psi | After conditioning at 23°C and 50% RH; ISO 178 |
Arkema Group Orgalloy® RS 6000 Polyamide 6 Alloy Polyamide Alloy, Rigid grade, Nylon 6 basedTubes / Mandrels / Profiles / CablesInformation provided by Arkema Group |
|||
Flexural Strength | 63.0 MPa | 9140 psi | ASTM D790 |
Aclo Accucomp ABS ABS802L High Impact Grade |
|||
Flexural Strength | 63.0 MPa | 9140 psi | 23°C, 50% RH; ASTM D790 |
Asahi Kasei Xyron® X05516 Modified Polyphenylene Ether AutomotiveInformation provided by Asahi Kasei |
|||
Flexural Strength | 63.0 MPa | 9140 psi | ASTM D790 |
Beijing Chemical Industry KAIFA® GL3200 ABS Flame-Retardant Grade Good flammabilityInformation provided by Beijing Chemical Industry Research Institute (Group) |