Polymer Property : Flexural Strength = 39.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Strength	<= 39.0 MPa	<= 5660 psi	ISO 178
Polykemi AB POLYfill PP CIP1001F Polypropylene Information provided by Polykemi AB
Flexural Strength	<= 39.0 MPa	<= 5660 psi	ISO 178
Polykemi AB POLYfill PP CPQ10015 FF Polypropylene, Mineral Reinforced Information provided by Polykemi AB
Flexural Strength	<= 39.0 MPa	<= 5660 psi	ISO 178
Polykemi AB POLYfill PPC T20020 Polypropylene Copolymer, Mineral Reinforced Information provided by Polykemi AB
Flexural Strength	<= 39.0 MPa	<= 5660 psi	ISO 178
Polykemi AB POLYfill PPC T25020 Polypropylene Copolymer, Mineral Reinforced Information provided by Polykemi AB
Flexural Strength	<= 39.0 MPa	<= 5660 psi	ISO 178
Polykemi AB POLYfill PPC T25020 UV Polypropylene Copolymer, Mineral Reinforced Information provided by Polykemi AB
Flexural Strength	39.0 MPa	5660 psi	0.1 in/min; 0.250" thickness; ASTM D-790B
Chevron Phillips EB6025 HIPS - High Impact Polystyrene (discontinued **) Rubber modified high impact polystyrene.Applications:Cosmetic packagingShower surroundsPoint of purchase displaysThin-wall injection molding and thermoformingFeatures:Smooth, glossy surface finishGo..
Flexural Strength	39.0 MPa	5660 psi	2 mm/min; ISO 178
Polimeri Europa Edistir RK Polystyrene (discontinued **) UL94 V-0, flame retarded, high impact polystyrene. This grade is suitable for injection moulding. It combines high mechanical strength, heat resistance and good processability. Designation: Thermopl..
Flexural Strength	39.0 MPa	5660 psi	2 mm/min; ISO 178
Polimeri Europa Edistir RKL Polystyrene (discontinued **) UL94 V-0, flame retarded, high impact polystyrene. This grade is designed for the extrusion of flame retardant sheets, foils and profiles. Designation: Thermoplastics ISO 2897-PS-I,E,093-06-04-18App..
Flexural Strength	39.0 MPa	5660 psi	2mm/min; ASTM D790
Kingfa FRHIPS-980 Flame Retardant Polystyrene Features:UL 94 V-0 @ 1.6mm, V-0 @ 3.2mmExcellent balance properties, Non-DPOExcellent heat stability & electrical propertyColor tailor-made for clientApplications:Injection moldingGas assistant mold..
Flexural Strength	39.0 MPa	5660 psi	2mm/min; ASTM D790
Kingfa FRHIPS-930 Flame Retardant Polystyrene Features:UL 94 V-0 @ 1.6mm, 5VA @ 2.6mmNon-DPO, high UV stabilityExcellent heat stabilityExcellent electrical propertiesApplications:Injection moldingGas moldingPrinter, photocopier, fax machineElec..
Flexural Strength	39.0 MPa	5660 psi	ASTM D790
LG Chemical LUPOL HF-3308 High Flow Polypropylene, 30% Mineral Fillers LUPOL resins, based on polyolefin with a wide range of characteristics, are a family of low cost engineering plastics.Applications: Automotive: Bumper cover, instrument panel, glove box, air cleaner..
Flexural Strength	39.0 MPa	5660 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP STAT-KON MD000AP PP LNP* STAT-KON* MD000AP is a compound based on Polypropylene containing Carbon Powder. Added features of this grade include: Electrically Conductive, Exceptional Processing.
Flexural Strength	39.0 MPa	5660 psi	ISO 178
SABIC Innovative Plastics LNP STAT-KON MD000AP PP LNP* STAT-KON* MD000AP is a compound based on Polypropylene containing Carbon Powder. Added features of this grade include: Electrically Conductive, Exceptional Processing.
Flexural Strength	39.0 MPa	5660 psi
SPS Guang Zhou SAMATâ„¢ 168(f1) Flame-retarded Polypropylene Characteristic: Good flame resistance, good chemical resistance, good mechanical propertiesApplications: X'mas decorative product, E/E applianceInformation Provided by SPS (Guang Zhou) Ltd.
Flexural Strength	39.0 MPa	5660 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP THERMOCOMP AW00A ABS (Europe-Africa-Middle East) LNP* THERMOCOMP* AW00A is a compound based on Acrylonitrile Butadiene Styrene resin containing Wollastonite.
Flexural Strength	39.0 MPa	5660 psi	dry; ISO 178
DSM Novamid® ST145 NAT PA6-I Impact Modified, Injection Molding
Flexural Strength	39.0 MPa	5660 psi	2 mm/min, 4 mm; ISO 178
Chi Mei Kibiton® PB-5910 SBC High transparency, medium stiffness, toughness
Flexural Strength	39.0 MPa	5660 psi	ASTM D790
Entec Hypro™ PPC-T20 Copolymer Polypropylene, 20% Talc Reinforced Information provided by Entec
Flexural Strength	39.0 MPa	5660 psi	2 mm/min; ISO 178
Chi Mei Polyrex® PH-888H Polystyrene - High Impact High FDI; high heat
Flexural Strength	39.0 MPa	5660 psi	ASTM D790
Entec Hypro™ PPC-CC30 Natural Copolymer Polypropylene, 30% Calcium Carbonate Filled Information provided by Entec
Flexural Strength	39.0 MPa	5660 psi	ASTM D790
Aclo Accuguard Polypropylene CP0467V0CSL Copolymer Flame Retardant Copper Stabilized
Flexural Strength	39.0 MPa	5660 psi	ASTM D790
Aclo Accutech Polyethylene HD0234G20UVL High Density Glass Reinforced UV Stabilized
Flexural Strength	39.0 MPa	5660 psi	ASTM D790
Aclo Accutech Polypropylene Homopolymer HP0334C30L Calcium Reinforced
Flexural Strength	39.0 MPa	5660 psi	ASTM D790
Aclo Accutech Polypropylene Homopolymer HP0334C40L Calcium Reinforced
Flexural Strength	39.0 MPa	5660 psi	ISO 178
Ascend Performance Materials Vydyne® ECO315 BK13 Nylon 66, Flame Retardant, Conditioned Vydyne® ECO366 BK13 is a non-halogenated, unfilled, flame-retardant PA66 homopolymer designed with superior flow properties to assist in filling thin-walled, intricate parts. It is lubricated for m..
Flexural Strength	39.0 MPa	5660 psi	ISO 178
Ascend Performance Materials Vydyne® ECO366 Nylon 66, Flame-retardant, Conditioned Vydyne® ECO366 is a non-halogenated, unfilled, flame-retardant PA66 homopolymer designed with superior flow properties to assist in filling thin-walled, intricate parts. It is lubricated for machin..
Flexural Strength	39.0 MPa	5660 psi	ASTM D790
Aclo Accuguard Polypropylene HP1369V2CSL Homopolymer Flame Retardant Copper Stabilized
Flexural Strength	39.0 MPa	5660 psi	ASTM D790
Teknor Apex Sinpolene TPP2030 Polypropylene Availability: Africa & Middle East; Latin America; Asia Pacific; South America Talc Filler, 30% Filler by Weight Uses: Appliance Components; Automotive Applications; Housings Forms: Pellets Process..