Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 358 MPa | 51900 psi | ASTM D790 |
Quantum Composites QC-2150 50% Glass Reinforced Phenolic SMC QC-2150 is a glass reinforced phenolic engineered structural composite molding compound. It exhibits outstanding low flammability characteristics. QC-2150 is recommended for applications such as a.. |
|||
Flexural Strength | 358 MPa | 51900 psi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP RF00BS PA 66 (Asia Pacific) LNP* Thermocomp* RF00BS is a compound based on Nylon 66 resin containing Glass Fiber. Added features of this material include: Heat Stabilized. |
|||
Flexural Strength | 358 MPa | 51900 psi | ASTM D 790 |
SABIC Innovative Plastics LNP Thermocomp RF00CS PA 66 LNP* Thermocomp* RF00CS is a compound based on Nylon 66 resin containing Glass Fiber. Added features of this material include: Heat Stabilized.This data was supplied by SABIC-IP for the Americas re.. |
|||
Flexural Strength | 358 MPa | 51900 psi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP RF00CSXS PA 66 (Asia Pacific) LNP* Thermocomp* RF00CSXS is a compound based on Nylon 66 resin containing Glass Fiber. Added features of this material include: Heat Stabilized. |
|||
Flexural Strength | 358 MPa | 51900 psi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP RF00CSXZ PA 66 LNP* THERMOCOMP* RF00CSXZ is a compound based on Recycled Nylon 66 resin containing 60% Glass Fiber. Added features of this material include: Heat Stabilized. |
|||
Flexural Strength | 358 MPa | 51900 psi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP RX98372H PA 66 (Asia Pacific) LNP* Thermocomp* RX98372H is a compound based on Nylon 66 resin containing Glass Fiber. |
|||
Flexural Strength | 358 MPa | 51900 psi | ASTM D790 |
Unitika E-RUNG60 Ultra high-rigidity PA6, Dry Ultra high-rigidityInformation provided by Unitika Ltd. |
|||
Flexural Strength | 358 MPa | 51900 psi | ASTM F417 |
CoorsTek AD-96 Alumina (nom. 96% Al2O3) Thermal Shock Delta Tc = 250°C - Thermal shock tests are performed by quenching samples in water from different elevated temperatures. Delta Tc is the change in temperature which results in a shar.. |
|||
Flexural Strength | 358 MPa | 51900 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP STAT-KON RC008 PA 66 (Europe-Africa-Middle East) LNP* Stat-kon* RC008 is a compound based on Nylon 66 resin containing Carbon Fiber. Added features of this material include: Electrically Conductive. |