Polymer Property : Flexural Strength = 262 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Strength	262 MPa	38000 psi	ASTM D790
PolyOne Nymax™ GF 1200 A 33 Natural Polyamide 66 (Nylon 66) The Nymax® GF 1200 Series of glass fiber-reinforced nylon 6/6 compounds have been specifically formulated for applications requiring high stiffness, tensile properties, heat resistance, and durabil..
Flexural Strength	262 MPa	38000 psi	ASTM D790
Ravago Manufacturing Americas Hylon® N1030HL Nylon 6/6 (discontinued **) Available in North America Filler: Glass Fiber Reinforcement, 30% Filler by WeightAdditive: Heat Stabilizer and Lubricant Features: Lubricated and Heat StabilizedAuto Specifications: GM GMW3038P-PA..
Flexural Strength	262 MPa	38000 psi	ASTM D790
Greene Tweed ArlonÂ® 1163 PEEK, Glass Filled ArlonÂ® is a tough, high-temperature, semi-crystalline, thermoplastic presenting a unique combination of mechanical, thermal, chemical and electrical properties. Greene, Tweed uses several proprie..
Flexural Strength	262 MPa	38000 psi	ISO 178
SABIC Innovative Plastics LNP LUBRICOMP OCL36 PPS - Linear LNP LUBRICOMP* OCL36 is a compound based on PPS - Linear resin containing 30% Carbon Fiber, 15% PTFE. Added features of this material include: Electrically Conductive, Wear Resistant.
Flexural Strength	262 MPa	38000 psi	ISO 178
SABIC Innovative Plastics LNP LUBRICOMP RFL26 PA 66 LNP LUBRICOMP* RFL26 is a compound based on Nylon 66 resin containing 30% Glass Fiber, 10% PTFE. Added features of this material include: Wear Resistant.
Flexural Strength	262 MPa	38000 psi	ASTM D790
Techmer ES HiFillÂ® PA6/6 GF30 HS L 30% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 30% Filler by WeightAdditive: Heat Stabilizer and LubricantFeatures: Heat Stabilized and LubricatedProcessin..
Flexural Strength	262 MPa	38000 psi	ASTM D790
Techmer ES LuriblendÂ® PA6/6 CF20 TS15 BK 20% Carbon Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Carbon Fiber, 20% Filler by WeightAdditive: PTFE Lubricant(10%) and Silicone Lubricant Features: Lubricated, Good Wear Resistance and L..
Flexural Strength	262 MPa	38000 psi	ASTM D790
Techmer ES LuriblendÂ® PA6/6 GF33 ML2 33% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 33% Filler by WeightAdditive: Molybdenum Disulfide Lubricant(2%)Features: LubricatedInformation provided by TP Composites,..
Flexural Strength	262 MPa	38000 psi	ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP EX93452 PEI (Asia Pacific) LNP* THERMOCOMP* EX93452 is a compound based on Polyetherimide resin containing Carbon Fiber. Added features of this material include: Electrically Conductive.
Flexural Strength	262 MPa	38000 psi	ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP IC006 PA 6/12 LNP* THERMOCOMP* IC006 is a compound based on Nylon 6/12 resin containing 30% Carbon Fiber. Added features of this material include: Electrically Conductive.
Flexural Strength	262 MPa	38000 psi	ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP IX95700 PA 6/12 (Asia Pacific) LNP* Thermocomp* IX95700 is a compound based on Nylon 6/12 resin containing Glass Fiber.
Flexural Strength	262 MPa	38000 psi	ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP IX95700 PA6.12 LNP* THERMOCOMP* IX95700 is a compound based on Nylon 6/12 resin containing Glass Fiber.
Flexural Strength	262 MPa	38000 psi	ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP RF00AH PA 66 LNP* THERMOCOMP* RF00AH is a compound based on Nylon 66 resin containing 50% Glass Fiber. Added feature of this grade is: Healthcare.
Flexural Strength	262 MPa	38000 psi	1.3 mm/min, 50 mm span; ASTM D 790
SABIC Innovative Plastics Noryl GTX GTX8430W PPE+PA 30% Glass Reinforced PPE+PA Alloy. Typically used for automotive connectors.This data was supplied by SABIC-IP for the Americas region.
Flexural Strength	262 MPa	38000 psi	ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP EF006H PEI (Asia Pacific) LNP* Thermocomp* EF006H is a compound based on Polyetherimide resin containing Glass Fiber.
Flexural Strength	262 MPa	38000 psi	ASTM D790
Chase Plastics CP Pryme® NN133GL (DAM) Nylon 66, 33% Glass Fiber Reinforced, Internally Lubricated Information provided by Chase Plastics.
Flexural Strength	262 MPa	38000 psi	ASTM D790
Adell AW-17 Nylon 66, 35% Glass Reinforced; Superior Finish Data provided by Adell Plastics, Inc.
Flexural Strength	262 MPa	38000 psi	ASTM D790
Adell AW-37 Nylon 66, 35% Glass Reinforced; Superior Finish Data provided by Adell Plastics, Inc.
Flexural Strength	262 MPa	38000 psi	ASTM D790
A. Schulman ComAlloy Lubrilon® 646 Nylon 6/12, Carbon Fiber/PTFE Reinforced Data provided by the manufacturer, ComAlloy International Company. High performance and excellent lubricity with minimal surface wear.The ComAlloy product line has been integrated into the A Schulma..