Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 255 MPa | 37000 psi | 1.3 mm/min; ASTM D790 |
PolyOne Edgetek® PS-30CF/000 HF UV BLACK Polybutylene Terephthalate (PBT) Information provided by PolyOne |
|||
Flexural Strength | 255 MPa | 37000 psi | ASTM D790 |
LNP Stat-Kon® LC-1003 EM Polyetheretherketone, Carbon Fiber Reinforcement
(discontinued **) Features: Good Moldability, Electrically ConductiveForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; howev.. |
|||
Flexural Strength | 255 MPa | 37000 psi | ASTM D790 |
Fiberfil® FV-30 Nylon 6, 30% Glass Reinforced, Heat Stabilized Information provided by FIBERFIL Engineered Plastics |
|||
Flexural Strength | >= 255 MPa | >= 37000 psi | |
MarkeTech Repton 115 Aluminum Oxide Brand 115 features: High Density and Purity.REPTON setter tiles, kiln furniture, and special fixtures are lightweight, ridge, and high strength ceramics that resist distortion and spalling, even whe.. |
|||
Flexural Strength | 255 MPa | 37000 psi | ASTM D790 |
Kolon KOPA® KN333G25CRBK G/F Reinforced Nylon 66 EG-resistant, high strength, dimensionally stableApplications Cooling water pipesInformation provided by API-Kolon. |
|||
Flexural Strength | 255 MPa | 37000 psi | ISO 178 |
Solvay TECHNYL® C 218 MZ20 V10 Black Z PA6, 20/10% mineral/glass fiber, DRY Description: Polyamide PA6, reinforced 20 % mineral filler and 10 % of glass fiber, heat stabilized, for injection molding.Available in: Asia PacificProduct Applications: TECHNYL C 218 MZ20 V10 offe.. |
|||
Flexural Strength | 255 MPa | 37000 psi | ISO 178 |
Solvay TECHNYL® C 218 V 30 PA6, 30% glass fiber, DRY Description: TECHNYL® C 218 V30 is a polyamide 6, heat stabilized, reinforced with 30% of glass fiber, for injection molding. This product is available in black color.Benefits: The product offers.. |
|||
Flexural Strength | 255 MPa | 37000 psi | ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP RFN16S PA 66 LNP LUBRICOMP* RFN16S is a compound based on Nylon 66 resin containing 30% Glass Fiber, 5% MOS2. Added features of this material include: Heat Stabilized, Wear Resistant. |
|||
Flexural Strength | 255 MPa | 37000 psi | ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP RFN16SXZ PA 66 LNP LUBRICOMP* RFN16SXZ is a compound based on Nylon 66 resin containing 30% Glass Fiber, 5% MOS2. Added features of this material include: Heat Stabilized, Wear Resistant. |
|||
Flexural Strength | 255 MPa | 37000 psi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP UX95672 PPA LNP LUBRICOMP* UX95672 is a compound based on Polyphthalamide resin containing Proprietary Filler(s). Added feature of this material is: Wear Resistant. |
|||
Flexural Strength | 255 MPa | 37000 psi | ISO 178 |
Solvay Specialty Polymers Amodel® HFZ A-4133L Polyphthalamide (PPA), 33% Glass Fiber Amodel® HFZ A-4133 L polyphthalamide (PPA) is a 33% glass-reinforced, hot water moldable resin. Key properties include heat resistance, reduced outgassing and high strength and stiffness over a b.. |
|||
Flexural Strength | 255 MPa | 37000 psi | ASTM D790 |
Techmer ES HiFill® PA6 GF33 L RD041 33% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 33% Filler by WeightAdditive: Lubricant Features: LubricatedAppearance: YellowTPCI# 8221102Information provi.. |
|||
Flexural Strength | 255 MPa | 37000 psi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP QF008 PA 6/10 (Asia Pacific) LNP* Thermocomp* QF008 is a compound based on Nylon 6/10 resin containing Glass Fiber. |
|||
Flexural Strength | 255 MPa | 37000 psi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP QF008 PA6.10 LNP* THERMOCOMP* QF008 is a compound based on Nylon 6/10 resin containing 40% Glass Fiber. |
|||
Flexural Strength | 255 MPa | 37000 psi | ASTM D790 |
A. Schulman ComAlloy Hiloy® 517 Polycarbonate, Carbon Fiber Reinforced Data provided by the manufacturer, ComAlloy International Company.30% Carbon Fiber Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Flexural Strength | 255 MPa | 37000 psi | ASTM D790 |
Ashley Polymers Ashlene® 528LS-33GB Nylon 66, Glass Reinforced General purpose glass fiber reinforced Nylon 66, designed for parts requiring excellent thermal and dimensional stability and higher strength than conventional resins.Data provided by the manufactur.. |
|||
Flexural Strength | 255 MPa | 37000 psi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOTUF PF008IR PA 6 (Asia Pacific) LNP* Thermotuf* PF008IR is a compound based on Nylon 6 resin containing Glass Fiber. Added features of this material include: High Impact, Mold Release. |
|||
Flexural Strength | 255 MPa | 37000 psi | ASTM D790 |
PolyOne Edgetek® PI-40GF/000 Polyetherimide (PEI), Glass Filled
(discontinued **) Description/Features:Glass Fiber ReinforcedUL 94 V0PolyOne First ChoiceInformation provided by PolyOne Corporation. |