Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 211 MPa | 30600 psi | ASTM D790 |
Solvay Specialty Polymers AvaSpire® AV-742 SL30 Polyaryletherketone (PAEK)
(Unverified Data**) AV-742 SL30 is a wear resistant grade of AvaSpire polyaryletherketone (PAEK) designed to provide low wear rates in both non-lubricated and lubricated environments. In addition to outstanding wear re.. |
|||
Flexural Strength | 211 MPa | 30600 psi | ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP RFL36S PA 66 LNP* LUBRICOMP* RFL36S is a compound based on Nylon 66 resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Wear Resistant, Heat Stabilized. |
|||
Flexural Strength | 211 MPa | 30600 psi | ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP RFL36XXY PA 66 LNP* LUBRICOMP* RFL36XXY is a compound based on Nylon 66 containing 30% Glass Fiber, 15% PTFE. Added feature of this grade is: Wear Resistant. |
|||
Flexural Strength | 211 MPa | 30600 psi | ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP RFL36XXZ PA 66 LNP* LUBRICOMP* RFL36XXZ is a compound based on Nylon 66 resin containing 30% Glass Fiber, 15% PTFE. Added feature of this material is: Wear Resistant. |
|||
Flexural Strength | 211 MPa | 30600 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP RFP36 PA 66 (Europe-Africa-Middle East) LNP* Lubricomp* RFP36 is a compound based on Nylon 66 resin containing Glass Fiber, PTFE, Silicone. |
|||
Flexural Strength | 211 MPa @Temperature 23.0 °C |
30600 psi @Temperature 73.4 °F |
4; ISO 178 |
Solvay Specialty Polymers Amodel® A-1565 HS Polyphthalamide (PPA), 65% GlassMineral (Dry) Amodel® A-1565 HS is a 65% glass and mineral-reinforced polyphthalamide (PPA) designed to be cost-effective in applications requiring high stiffness, good dimensional stability and good retention.. |
|||
Flexural Strength | 211 MPa | 30600 psi | ISO 178 |
SABIC Innovative Plastics LNP LUBRILOY RF208 PA 66 LNP LUBRILOY* RF208 is a compound based on Nylon 66 resin containing 40% Glass Fiber, Proprietary Lubricant. Added features of this material include: Wear Resistant. |
|||
Flexural Strength | 211 MPa | 30600 psi | ISO 178 |
SABIC Innovative Plastics LNP LUBRILOY RF208 PA 66 (Asia Pacific) LNP LUBRILOY* RF208 is a compound based on Nylon 66 resin containing Glass Fiber, Proprietary Lubricant. Added features of this material include: Internally Lubricated. |
|||
Flexural Strength | 211 MPa | 30600 psi | ASTM D790 |
Solvay Specialty Polymers AvaSpire® AV-742 SL30 Polyaryletherketone (PAEK) AV-742 SL30 is a wear resistant grade of AvaSpire® polyaryletherketone (PAEK) designed to provide low wear rates in both non-lubricated and lubricated environments. In addition to outstanding wea.. |
|||
Flexural Strength | 211 MPa | 30600 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP Stat-kon DEF13 PC LNP* Stat-kon* DEF13 is a compound based on Polycarbonate resin containing Glass Fiber, Glass Fiber, Carbon Fiber. Added features of this material include: Electrically Conductive.This data was sup.. |
|||
Flexural Strength | 211 MPa | 30600 psi | ASTM D790 |
SABIC Innovative Plastics LNP STAT-KON DX10315C PC (Asia Pacific) LNP* Stat-Kon* DX10315C is carbon fiber filled polycarbonate composite with good stiffness, good flow ability, ESD safety, and high level of cleanliness for the most demanding application. This comp.. |
|||
Flexural Strength | 211 MPa | 30600 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP D452 PC COPOLYMER (Asia Pacific) LNP* Thermocomp* D452 (or EXTC8202) is a compound based on SABIC unique Polycarbonate copolymer resin containing Glass Fiber, Flame Retardant. Added features of this material include: High modulus, .. |
|||
Flexural Strength | 211 MPa | 30600 psi | ASTM D790 |
Unitika AXG-1500-300 Dry Characteristics: Glass-reinforced grades of the AX1500 resin, excellent in heat and chemical resistancesFavorable rigidity and dimensional accuracyInformation provided by Unitika Ltd. |
|||
Flexural Strength | 211 MPa | 30600 psi | 2.8mm/min; ASTM D790 |
Asia International Enterprise (Hong Kong) 60G5F Nylon 66, 25% Filled Information provided by Asia International Enterprise (Hong Kong) Ltd. |
|||
Flexural Strength | 211 MPa | 30600 psi | ASTM D790 |
Applied Composites 179 Polyester SMC Industry Application: TransportationProduct Application: Auto InteriorsInformation provided by Applied Composites Corporation. |
|||
Flexural Strength | 211 MPa | 30600 psi | ASTM D790 |
A. Schulman ComAlloy Voloy® 682 Nylon 6/6, Glass Fiber, Nylon 6/6 Alloy, Flame Retardant, UL Data provided by the manufacturer, ComAlloy International Company.45% Glass Reinforced. Halogen- and phosphorous-freeThe ComAlloy product line has been integrated into the A Schulman product line. |
|||
Flexural Strength | 211 MPa @Temperature 23.0 °C |
30600 psi @Temperature 73.4 °F |
ISO 178 |
Solvay Specialty Polymers Amodel® A-1565 HS Polyphthalamide (PPA)
(Unverified Data**) Amodel A-1565 HS is a 65% glass and mineral-reinforced polyphthalamide (PPA) designed to be cost-effective in applications requiring high stiffness, good dimensional stability and good retention of .. |