Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 179 MPa | 26000 psi | ASTM D790 |
Polymer Resources PC-G40-[color]-1 Polycarbonate, 40% Glass Reinforced with Mold Release Polycarbonate, 40% Glass Reinforced with Mold ReleaseProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information.. |
|||
Flexural Strength | 179 MPa | 26000 psi | ASTM D790 |
Ravago Manufacturing Americas Hylon® N2033HL Nylon 6 (Cond) Information provided by Ravago. |
|||
Flexural Strength | 179 MPa | 26000 psi | ASTM D790 |
Polymer Resources NY6-G13-[color]-H Nylon 6, 13% Glass Reinforced, Heat Stabilized Nylon 6, 13% Glass Reinforced, Heat Stabilized, LubricatedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon.. |
|||
Flexural Strength | 179 MPa | 26000 psi | ASTM D790 |
IDI Composites E-205 Thermoset Polyester, Sheet ELECTRICAL - U.L. recognized (E53587). Versatile family of compounds designed to meet the most demanding electrical and electronic applications. Excellent dielectric properties and arc/track resista.. |
|||
Flexural Strength | 179 MPa @Temperature 22.0 °C |
26000 psi @Temperature 71.6 °F |
25 mm wide 100 mm long, flat samples; ISO 14125 |
Menzolit Menzolit® SMC 2600 Unsaturated Polyester UP SMC 2600 is a special SMC with electrically conductive properties. Because of its conductivity, SMC 2600 is antistatic and prevents build-up of electrical charges on the surface. Despite of its cond.. |
|||
Flexural Strength | 179 MPa | 26000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Valox® 553 PBT+PC 30% GR PBT+PC, UL94 V-0. Reduced warpage characteristics.Applications; appliance handles, spotlights, electric motors, pump housings, etc. |
|||
Flexural Strength | 179 MPa | 26000 psi | ASTM D790 |
Solvay Specialty Polymers Veradel® AG-330 Polyethersulfone (PESU), 30% Glass Fiber Veradel® AG-330 is a 30% glass fiber reinforced grade of polyethersulfone (PESU). Adding glass fiber to polyethersulfone substantially increases the rigidity, tensile strength, creep resistance, .. |
|||
Flexural Strength | 179 MPa | 26000 psi | ASTM D790 |
Techmer ES HiFill® PPS 0231 B LE Availability: North AmericaForms: PelletsFeatures: High Density and Low ExtractablesAppearance: OpaqueInformation provided by TP Composites, Inc. |
|||
Flexural Strength | 179 MPa | 26000 psi | ASTM D790 |
Techmer ES Luriblend® PA11 GF30 TL20 LE 30% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 30% Filler by WeightAdditive: Heat Stabilizer and PTFE LubricantFeatures: Good Wear Resistance, Low Extractables, Lubricat.. |
|||
Flexural Strength | 179 MPa | 26000 psi | ASTM D790 |
Techmer ES Plaslube® J-1/CF/10/TF/13/SI/2 BK223 PA66 |
|||
Flexural Strength | 179 MPa | 26000 psi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP PF003 PA 6 LNP THERMOCOMP* PF003 is a compound based on Nylon 6 resin containing 15% Glass Fiber. |
|||
Flexural Strength | 179 MPa | 26000 psi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP PF003 PA 6 (Asia Pacific) LNP* THERMOCOMP* PF003 is a compound based on Nylon 6 resin containing Glass Fiber. |
|||
Flexural Strength | 179 MPa | 26000 psi | ASTM D790 |
SABIC Innovative Plastics LNP STAT-KON DE0029EC PC LNP* STAT-KON* DE0029EC is a compound based on Polycarbonate resin containing 10% Carbon Fiber. Added features of this material include: Electrically Conductive, Easy Molding, Flame Retardant. |
|||
Flexural Strength | 179 MPa | 26000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP PX92248 PA 6 LNP* THERMOCOMP* PX92248 is a compound based on Nylon 6 resin containing Proprietary Filler(s). |
|||
Flexural Strength | 179 MPa | 26000 psi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP RFZ349XC PA 66 (Asia Pacific) LNP* THERMOCOMP* RFZ349XC is a compound based on Nylon 66 resin containing Glass Fiber, Milled Glass. Added features of this material include: Flame Retardant. |
|||
Flexural Strength | 179 MPa | 26000 psi | ASTM D790 |
PolyOne LubriOne™ PC-30GF/15T Polycarbonate (PC) LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. L.. |
|||
Flexural Strength | 179 MPa @Temperature 22.8 °C |
26000 psi @Temperature 73.0 °F |
ASTM D790 |
Quadrant EPP Duratron® U2200 PEI Extruded 20% Glass Reinforced Polyetherimide |
|||
Flexural Strength | 179 MPa | 26000 psi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP EFL34HL PEI LNP LUBRICOMP* EFL34HL is a compound based on Polyetherimide resin containing 20% Glass Fiber, 15% PTFE. Added features of this material include: Internally Lubricated, Low Extractable. |
|||
Flexural Strength | 179 MPa | 26000 psi | ISO 178 |
Premix Premi-Glas® 1281-32 VE Glass Reinforced Vinyl Ester SMC
(discontinued **) Description: Premi-Glas® 1281-32 VE SMC is a high strength glass reinforced vinyl ester sheet molding compound formulated for under-the-hood automotive applications. Key features and benefits: Desi.. |