Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | <= 156 MPa | <= 22600 psi | ISO 178 |
Polykemi AB SCANBLEND P AP2060 F20 PBT/ASA, Glass Fiber Reinforced Information provided by Polykemi AB |
|||
Flexural Strength | 156 MPa | 22600 psi | ISO 178 |
PolyOne Bergadur™ PB400 G15 H UF UV Polybutylene Terephthalate (PBT) Information provided by PolyOne |
|||
Flexural Strength | 156 MPa | 22600 psi | ASTM D790 |
SABIC Innovative Plastics Lexan® LGK4010 PC (Asia Pacific) |
|||
Flexural Strength | 156 MPa | 22600 psi | ASTM D790 |
Techmer ES HiFill® PA6 GF15 UV002 15% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 15% Filler by Weight Additive: UV Stabilizer and LubricantFeatures: Good UV Resistance and LubricatedInforma.. |
|||
Flexural Strength | 156 MPa | 22600 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP DF004P PC (Asia Pacific) LNP* Thermocomp* DF004P is a Polycarbonate base resin containing Glass Fiber. Characteristics of this grade are Exceptional Processing. |
|||
Flexural Strength | 156 MPa | 22600 psi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP GF006 PSU LNP THERMOCOMP* GF006 is a compound based on Polysulfone resin containing 30% Glass Fiber. |
|||
Flexural Strength | 156 MPa | 22600 psi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP GF006XXZ PSU LNP THERMOCOMP* GF006XXZ is a compound based on Polysulfone resin containing 30% Glass Fiber. |
|||
Flexural Strength | 156 MPa | 22600 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP JF004LZ PES LNP* Thermocomp* JF004LZ is a compound based on PES containing 20% Glass Fiber. Added features include: Extrusion Grade, Low Extractible. |
|||
Flexural Strength | 156 MPa | 22600 psi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP RF002ES PA 66 LNP THERMOCOMP* RF002ES is a compound based on Nylon 66 resin containing 10% Glass Fiber. Added features of this material include: Easy Molding, Heat Stabilized. |
|||
Flexural Strength | 156 MPa | 22600 psi | ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP RF003H PA 66 LNP* THERMOCOMP* RF003H is a compound based on Nylon 66 containing 15% Glass Fiber. Added feature of this grade is: Healthcare. |
|||
Flexural Strength | 156 MPa | 22600 psi | ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP RF003XXH PA 66 LNP* THERMOCOMP* RF003XXH is a compound based on Nylon 66 containing 15% Glass Fiber. Added feature of this grade is: Healthcare. |
|||
Flexural Strength | 156 MPa | 22600 psi | ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP ZF006 PPE+PS LNP* THERMOCOMP* ZF006 is a compound based on PPE+PS resin containing 30% Glass Fiber. |
|||
Flexural Strength | 156 MPa | 22600 psi | ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP IF003 PA 6/12 LNP THERMOCOMP* IF003 is a compound based on Nylon 6/12 resin containing 15% Glass Fiber. |
|||
Flexural Strength | 156 MPa | 22600 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP THERMOTUF VF004S PA 66 LNP THERMOTUF* VF004S is a compound based on Nylon resin containing Glass Fiber. Added features of this material include: Heat Stabilized. |
|||
Flexural Strength | 156 MPa | 22600 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
SABIC Innovative Plastics LNP Verton NV0081EV_GY7E149 PC+ABS Preliminary data for 40% long fiber single pellet non-halogen FR color filled PC/ABSThis data was supplied by SABIC-IP for the Americas region. |
|||
Flexural Strength | 156 MPa | 22600 psi | ASTM D790 |
SABIC Innovative Plastics NORYL GTX APS130 PPE+PPS (Asia Pacific) PPE+PPS GF30% |
|||
Flexural Strength | 156 MPa | 22600 psi | ASTM D790 |
A. Schulman ComAlloy Voloy® 631 Nylon 6/6, Glass Reinforced, Flow Enhanced, Flame Retardant, UL Data provided by the manufacturer, ComAlloy International Company.13% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Flexural Strength | 156 MPa | 22600 psi | ASTM D790 |
SABIC Innovative Plastics NORYL APS130 PPE+PPS (Asia Pacific) |