Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 103 MPa | 15000 psi | ASTM D790 |
Network Polymers Nylon 6609 L Description: Black NylonInformation provided by Network Polymers Inc. |
|||
Flexural Strength | 103 MPa | 15000 psi | ASTM D790 |
Quadrant EPP Nylatron® LFG (ASTM Product Data Sheet) |
|||
Flexural Strength | 103 MPa | 15000 psi | ASTM D790 |
Polymer Resources PPX-G10 Modified-PPO, 10% Glass Reinforced Modified-Polyphenylene Oxide, 10% Glass ReinforcedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information pr.. |
|||
Flexural Strength | 103 MPa | 14900 psi | ASTM D790 |
PolyOne Geon™ 80510 Polyvinyl Chloride, Rigid (PVC, Rigid) Information provided by PolyOne |
|||
Flexural Strength | 103 MPa | 15000 psi | ASTM D790 |
Quantum Nylon 6/6 Information provided by Quantum Advanced Engineering Plastics |
|||
Flexural Strength | 103 MPa | 14900 psi | 1.3 mm/min; ASTM D790 |
PolyOne Edgetek® AS-10GF/000 FR V0 BLACK Acrylonitrile Butadiene Styrene (ABS) Information provided by PolyOne |
|||
Flexural Strength | 103 MPa | 14900 psi | ASTM D 790 |
SABIC Innovative Plastics LNP Lubriloy D20001 PC LNP LUBRILOY* D20001 is a compound based on Polycarbonate resin containing Flame Retardant, Proprietary Lubricant. Added features of this material include: Flame Retardant.This data was supplied by.. |
|||
Flexural Strength | 103 MPa | 15000 psi | ASTM D790 |
Techmer ES HiFill® PA4/6 HS Availability: North AmericaForms: PelletsAdditive: Heat StabilizerFeatures: Heat StabilizedInformation provided by TP Composites, Inc. |
|||
Flexural Strength | 103 MPa | 15000 psi | ASTM D790 |
Techmer ES HiFill® PA6 GF10 TL10 BK 10% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 10% Filler by Weight Additive: Heat Stabilizer and PTFE LubricantFeatures: Heat Stabilized and LubricatedApp.. |
|||
Flexural Strength | 103 MPa | 14900 psi | ASTM D 790 |
SABIC Innovative Plastics LNP Thermocomp ZZ006 PPE+PS (Asia Pacific) LNP* THERMOCOMP* ZZ006 is a compound based on PPE+PS Blend resin containing Milled Glass.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
Flexural Strength | 103 MPa | 14900 psi | ASTM D 790 |
SABIC Innovative Plastics LNP Thermocomp IF002 PA 6/12 LNP* Thermocomp* IF002 is a compound based on Nylon 6/12 resin containing Glass Fiber.This data was supplied by SABIC-IP for the Americas region. |
|||
Flexural Strength | 103 MPa | 14900 psi | ASTM D790 |
Sumitomo Bakelite Durez® 32245 Phenolic, Compression Grade Durez 32245 Black Phenolic is a two-stage glass fiber and mineral filled special purpose molding compound. It is especially designed for applications requiring high strength and dimensional stabilit.. |
|||
Flexural Strength | 103 MPa | 15000 psi | ASTM D790 |
A. Schulman ComAlloy® 510-3010 10% Glass Fiber Reinforced Polycarbonate Information provided by A. Schulman.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Flexural Strength | 103 MPa | 15000 psi | ASTM D790 |
A. Schulman ComAlloy® 510-3010 10% Glass Fiber Reinforced Polycarbonate Information provided by A. Schulman.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Flexural Strength | 103 MPa | 15000 psi | ASTM D790 |
A. Schulman ComAlloy® 510-3010 10% Glass Fiber Reinforced Polycarbonate Information provided by A. Schulman.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Flexural Strength | 103 MPa | 15000 psi | |
TriStar TriSteel AT Metal Backed PTFE Bearing System Ultraflon 601T (AT) POM bronze with PTFE, lined metal back bearing system, high PV, self lube, high speed. This liner will run with zero lubrication required. Most commonly used in clip bearings, li.. |
|||
Flexural Strength | 103 MPa | 15000 psi | ASTM D790 |
A. Schulman ComAlloy® 510-3010 10% Glass Fiber Reinforced Polycarbonate Information provided by A. Schulman.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Flexural Strength | 103 MPa | 14900 psi | |
Cosmic Plastics E4920 Mineral Filled Epoxy Molding Compound, Encapsulated Grade Data provided by the manufacturer. |
|||
Flexural Strength | 103 MPa | 15000 psi | Crosswise; ASTM D790 |
Bedford Plastics Glass Reinforced Polyester Flat Sheet, 3/16" to 1/4" Pultrusion results in the production and supply of one of the worlds strongest and most durable products available today. The pultruded products feature:High StrengthCorrosion Resistant to many che.. |
|||
Flexural Strength | 103 MPa | 14900 psi | ASTM D790 |
A. Schulman ComAlloy Comtuf® 652 Nylon 6/6, Mineral Reinforced, Impact Modified Data provided by the manufacturer, ComAlloy International Company.30% Mineral Reinforced. Superior toughness and impact resistance characterize Comtuf® materialsThe ComAlloy product line has been i.. |
|||
Flexural Strength | 103 - 138 MPa | 15000 - 20000 psi | |
Bulk Molding Compounds BMC 880 Medium Strength Molding Compound BMC 880 is a medium strength, low shrink molding compound designed for outdoor applications. This material is UL Listed 94-V0/5V and is UL approved for outdoor use. It can be supplied in bulk or ext.. |
|||
Flexural Strength | 103 MPa | 14900 psi | ASTM D790 |
Ashley Polymers Ashlene® R6043 Nylon 6 Medium viscosity extrusion grade Nylon 6 resin with excellent melt stability, good melt strength: suitable for extrusion coating and film co-extrusion applications. Excellent grease resistance, tou.. |
|||
Flexural Strength | 103 MPa | 15000 psi | ASTM D570 |
Solvay Specialty Polymers Xydar® M-345 Liquid Crystal Polymer, 45% Mineral Filled
(discontinued **) XYDAR M-345 Liquid Crystal Polymer (LCP) is a 45% mineral-filled injection molding grade with exceptional moldability. XYDAR M-345 resin can fill very thin walls over long flow lengths with little o.. |
|||
Flexural Strength | 103 MPa | 14900 psi | ASTM D790 |
Sumitomo Bakelite North America RX® 853G Fiberglass Reinforced Phenolic Novolac RX 853G is a fiberglass reinforced phenolic novolac compound, featuring dimensional stability, moderate impact resistance, and good strength and modulus.Information supplied by Sumitomo Bak North Am.. |
|||
Flexural Strength | 103 MPa | 14900 psi | |
Cosmic Plastics 6230F Long Glass Fiber Filled Iso Diallyl Phthalate Molding Compound Data provided by the manufacturer. |