Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Modulus of Elasticity | 202 GPa @Temperature 221 °C |
29300 ksi @Temperature 430 °F |
|
Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 538°C (1000°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man.. |
|||
Modulus of Elasticity | 202 GPa @Temperature 221 °C |
29300 ksi @Temperature 430 °F |
|
Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 704°C (1300°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man.. |
|||
Modulus of Elasticity | 202 GPa @Temperature 221 °C |
29300 ksi @Temperature 430 °F |
|
Haynes Hastelloy® N, 1.6 mm sheet, heat treated at 1175°C, welded and tested as welded Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man.. |
|||
Modulus of Elasticity | 202 GPa @Temperature 221 °C |
29300 ksi @Temperature 430 °F |
|
Haynes Hastelloy® N, weld metal as welded Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man.. |
|||
Modulus of Elasticity | 202 GPa @Temperature 221 °C |
29300 ksi @Temperature 430 °F |
|
Haynes Hastelloy® N, weld metal, aged 500 hours at 649°C (1200°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man.. |
|||
Modulus of Elasticity | 202 GPa @Temperature 300 °C |
29300 ksi @Temperature 572 °F |
Dynamic |
Haynes 282® Nickel Alloy Autogenously Welded Sheet Excellent High Temperature Strength HAYNES® 282® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and la.. |
|||
Modulus of Elasticity | 202 GPa @Temperature 300 °C |
29300 ksi @Temperature 572 °F |
Dynamic |
Haynes 282® Nickel Alloy Gas Tungsten Arc Welded (GTAW) Plate Excellent High Temperature Strength HAYNES® 282® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and la.. |
|||
Modulus of Elasticity | 202 GPa @Temperature 300 °C |
29300 ksi @Temperature 572 °F |
Dynamic |
Haynes 282® Nickel Alloy Sheet, Plate and Bar, Solution Annealed Excellent High Temperature Strength HAYNES® 282® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and la.. |
|||
Modulus of Elasticity | 202 GPa @Temperature 300 °C |
29300 ksi @Temperature 572 °F |
Dynamic |
Haynes 282® Nickel Alloy Sheet, Solution Annealed and Age-hardened Excellent High Temperature Strength HAYNES® 282® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and la.. |
|||
Modulus of Elasticity | 202 GPa @Temperature 300 °C |
29300 ksi @Temperature 572 °F |
Dynamic |
Haynes 282® Nickel Alloy Sheet, Solution Annealed and Cold Worked Excellent High Temperature Strength HAYNES® 282® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and la.. |
|||
Modulus of Elasticity | 202 GPa @Temperature 300 °C |
29300 ksi @Temperature 572 °F |
Dynamic |
Haynes 282® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) All Weld Cruciform Excellent High Temperature Strength HAYNES® 282® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and la.. |
|||
Modulus of Elasticity | 202 GPa @Temperature 300 °C |
29300 ksi @Temperature 572 °F |
Dynamic |
Haynes 282® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) Plate Excellent High Temperature Strength HAYNES® 282® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and la.. |
|||
Modulus of Elasticity | 202 GPa @Thickness 12.7 mm, Temperature 316 °C |
29300 ksi @Thickness 0.500 in, Temperature 600 °F |
(Heat treated at 1066°C (1950°F), rapid quenched, plate) |
HP Alloys Alloy B-2, Solution Treated, 10% Cold Worked Solution Treated, 10% Cold Worked applies to tensile and/or hardness; other properties are typical of this alloy.Data provided by High Performance Alloys, Inc. and Haynes International. |
|||
Modulus of Elasticity | 202 GPa @Thickness 12.7 mm, Temperature 316 °C |
29300 ksi @Thickness 0.500 in, Temperature 600 °F |
(Heat treated at 1066°C (1950°F), rapid quenched, plate) |
HP Alloys Alloy B-2, Solution Treated, 20% Cold Worked Solution Treated, 20% Cold Worked applies to tensile and/or hardness; other properties are typical of this alloy.Data provided by High Performance Alloys, Inc. and Haynes International. |
|||
Modulus of Elasticity | 202 GPa @Thickness 12.7 mm, Temperature 316 °C |
29300 ksi @Thickness 0.500 in, Temperature 600 °F |
(Heat treated at 1066°C (1950°F), rapid quenched, plate) |
HP Alloys Alloy B-2, Solution Treated, 30% Cold Worked Solution Treated, 30% Cold Worked applies to tensile and/or hardness; other properties are typical of this alloy.Data provided by High Performance Alloys, Inc. and Haynes International. |
|||
Modulus of Elasticity | 202 GPa @Thickness 12.7 mm, Temperature 316 °C |
29300 ksi @Thickness 0.500 in, Temperature 600 °F |
(Heat treated at 1066°C (1950°F), rapid quenched, plate) |
HP Alloys Alloy B-2, Solution Treated, 40% Cold Worked Solution Treated, 40% Cold Worked applies to tensile and/or hardness; other properties are typical of this alloy.Data provided by High Performance Alloys, Inc. and Haynes International. |
|||
Modulus of Elasticity | 202 GPa @Temperature 400 °C |
29300 ksi @Temperature 752 °F |
Typical annealed sample; short time elevated temp. |
American Utility Metals Cromgard® Stainless Steel Cromgard is a low cost stainless steel, which is able to provide benefits of good weldability and formability, making it capable of fabrication by conventional techniques. It provides the benefits o.. |
|||
Modulus of Elasticity | 202 GPa @Temperature 300 °C |
29300 ksi @Temperature 572 °F |
Dynamic |
Haynes 282® Nickel Alloy Sheet, Gamma-Prime Strengthened Excellent High Temperature Strength HAYNES® 282® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and land-b.. |
|||
Modulus of Elasticity | 202 GPa @Temperature 221 °C |
29300 ksi @Temperature 430 °F |
|
Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 593°C (1100°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||
Modulus of Elasticity | 202 GPa @Temperature 221 °C |
29300 ksi @Temperature 430 °F |
|
Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 760°C (1400°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||
Modulus of Elasticity | 202 GPa @Temperature 221 °C |
29300 ksi @Temperature 430 °F |
|
Haynes Hastelloy® N, 1.6 mm sheet, aged 128 hours at 815°C (1500°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||
Modulus of Elasticity | 202 GPa @Temperature 221 °C |
29300 ksi @Temperature 430 °F |
|
Haynes Hastelloy® N, 1.6 mm sheet, heat treated at 1175°C, rapid air cooled Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||
Modulus of Elasticity | 202 GPa @Thickness 12.7 mm, Temperature 316 °C |
29300 ksi @Thickness 0.500 in, Temperature 600 °F |
(Heat treated at 1066°C (1950°F), rapid quenched, plate) |
HP Alloys Alloy B-2, Solution Treated, 50% Cold Worked Solution Treated, 50% Cold Worked applies to tensile and/or hardness; other properties are typical of this alloy.Data provided by High Performance Alloys, Inc. and Haynes International. |
|||
Modulus of Elasticity | 202 GPa @Temperature 300 °C |
29300 ksi @Temperature 572 °F |
Dynamic |
Haynes 282® Nickel Alloy Plate, Solution Annealed and Age-Hardened Excellent High Temperature Strength HAYNES® 282® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and land-b.. |
|||
Modulus of Elasticity | 202 GPa @Temperature 221 °C |
29300 ksi @Temperature 430 °F |
|
Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 649°C (1200°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||
Modulus of Elasticity | 202 GPa @Temperature 221 °C |
29300 ksi @Temperature 430 °F |
|
Haynes Hastelloy® N, 1.14 mm sheet, heat treated at 1149°C (2100°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |