Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Modulus of Elasticity | 9.65 GPa @Thickness 1.57 mm |
1400 ksi @Thickness 0.0620 in |
CW; ASTM D229 |
Industrial Laminates/Norplex NP329 Cotton Fabric Description: Bleached linen with melamine resin system. Provides better arc resistance than NP320E. Also, resistant to ammonia based refrigerants. Hard, durable material should be heated to punch, .. |
|||
Modulus of Elasticity | 9.65 GPa @Thickness 1.57 mm |
1400 ksi @Thickness 0.0620 in |
CW; ASTM D229 |
Industrial Laminates/Norplex NP504 Glass Fabric Description: Woven glass fabric with high temperature phenolic resin. Good flexural, compressive and impact strengths at elevated temperatures. Capable of continuous operation at 175° C, see note.. |
|||
Modulus of Elasticity | 9.65 GPa @Thickness 1.57 mm |
1400 ksi @Thickness 0.0620 in |
CW; ASTM D229 |
Industrial Laminates/Norplex NP610 Paper Base Laminate Description: Phenolic paper based grade for mechanical applications. Good tensile, compressive and flexural strength. Primarily a machining material, but may be hot punched up to .093" thick.Thickne.. |
|||
Modulus of Elasticity | 9.65 GPa @Thickness 1.57 mm |
1400 ksi @Thickness 0.0620 in |
CW; ASTM D229 |
Industrial Laminates/Norplex NP660 Paper Base Laminate Description: Lower cost paper phenolic NEMA Grade XP. Uses natural kraft paper without pigmented cover sheet. Warm to hot punching. UL listed. Thickness Tested: 0.062", 0.125" & 0.500" |