Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Modulus of Elasticity | 12.4 GPa @Thickness 1.57 mm |
1800 ksi @Thickness 0.0620 in |
LW; ASTM D229 |
Industrial Laminates/Norplex NP193E Synthetic Fabric Description: 17 oz. aramid and "soft glass" fibers are combined to make a fabric that is stronger than pure aramid and less abrasive than glass fabrics. This material is impregnated with a high temp.. |
|||
Modulus of Elasticity | 12.4 GPa @Thickness 1.57 mm |
1800 ksi @Thickness 0.0620 in |
LW; ASTM D229 |
Industrial Laminates/Norplex NP329 Cotton Fabric Description: Bleached linen with melamine resin system. Provides better arc resistance than NP320E. Also, resistant to ammonia based refrigerants. Hard, durable material should be heated to punch, .. |
|||
Modulus of Elasticity | 12.4 GPa @Thickness 1.57 mm |
1800 ksi @Thickness 0.0620 in |
LW; ASTM D229 |
Industrial Laminates/Norplex NP504 Glass Fabric Description: Woven glass fabric with high temperature phenolic resin. Good flexural, compressive and impact strengths at elevated temperatures. Capable of continuous operation at 175° C, see note.. |
|||
Modulus of Elasticity | 12.4 GPa @Thickness 1.57 mm |
1800 ksi @Thickness 0.0620 in |
LW; ASTM D229 |
Industrial Laminates/Norplex NP634 Laminate Description: Warm punching, composite grade with woven glass covers for improved flexural, tensile and impact strength. Electrical properties comparable to NP611.Thickness Tested: 0.062", 0.125" and.. |