Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Modulus of Elasticity | 10.3 GPa @Thickness 1.57 mm |
1500 ksi @Thickness 0.0620 in |
CW; ASTM D229 |
Industrial Laminates/Norplex NP310 Cotton Fabric Description: Canvas machining grade for structural and mechanical applications. Better impact strength than phenolic paper grades. MIL-I-24768/16. Thickness Tested: 0.062, 0.125", and 0.500". |
|||
Modulus of Elasticity | 10.3 GPa @Thickness 1.57 mm |
1500 ksi @Thickness 0.0620 in |
CW; ASTM D229 |
Industrial Laminates/Norplex NP310E Cotton Fabric Description: Manufactured with a domestic cotton fabric and phenolic resin. Similar to NP310 with improved moisture resistance and electrical properties. Mechanical properties equivalent to NP310. M.. |
|||
Modulus of Elasticity | 10.3 GPa @Thickness 1.57 mm |
1500 ksi @Thickness 0.0620 in |
LW; ASTM D229 |
Industrial Laminates/Norplex NP320U Cotton Fabric Description: Utility version of NP320E. Meets most, but not all, NEMA properties for L and LE, and is not certifiable as a NEMA Grade.Thickness Tested: 0.062", 0.125", and 0.500" |
|||
Modulus of Elasticity | 10.3 GPa @Thickness 1.57 mm |
1500 ksi @Thickness 0.0620 in |
LW; ASTM D229 |
Industrial Laminates/Norplex NP322 Cotton Fabric Description: Linen phenolic laminate with molybdenum disulfide. Provides the same lubricity as NP313, but has better machining qualities. Mechanical strength similar to, but slightly less than NP320.. |
|||
Modulus of Elasticity | 10.3 GPa @Thickness 1.57 mm |
1500 ksi @Thickness 0.0620 in |
LW; ASTM D229 |
Industrial Laminates/Norplex NP325 Cotton Fabric Description: Linen phenolic laminate with graphite added as a solid lubricant. Linen substrate provides better machining and wear resistance than NP315.Thickness Tested: 0.062", 0.125" and 0.500". |
|||
Modulus of Elasticity | 10.3 GPa @Thickness 1.57 mm |
1500 ksi @Thickness 0.0620 in |
LW; ASTM D229 |
Industrial Laminates/Norplex NP344 Cotton Fabric Description: Fine weave canvas laminate with high temperature phenolic resin and molybdenum disulfide lubricant. Good machining properties and low coefficient of thermal expansion. Better machining .. |
|||
Modulus of Elasticity | 10.3 GPa @Thickness 1.57 mm |
1500 ksi @Thickness 0.0620 in |
LW; ASTM D229 |
Industrial Laminates/Norplex NP347 Cotton Fabric Description: Bleached canvas with high temperature phenolic resin with molybdenum disulfide lubricant. Low moisture absorption. Capable of 150°C continuous operation.Thickness Tested: 0.062", 0.1.. |
|||
Modulus of Elasticity | 10.3 GPa @Thickness 1.57 mm |
1500 ksi @Thickness 0.0620 in |
CW; ASTM D229 |
Industrial Laminates/Norplex NP634 Laminate Description: Warm punching, composite grade with woven glass covers for improved flexural, tensile and impact strength. Electrical properties comparable to NP611.Thickness Tested: 0.062", 0.125" and.. |
|||
Modulus of Elasticity | 10.3 GPa @Thickness 1.57 mm |
1500 ksi @Thickness 0.0620 in |
LW; ASTM D229 |
Industrial Laminates/Norplex NP639 Paper Base Laminate Description: Economical paper reinforced laminate developed with capacity to withstand temperatures to 150° C without blistering. High compressive strength and low moisture absorption.Thickness T.. |