Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Adhesive Bond Strength | 14.0 MPa | 2030 psi | Phenolic, Shear; ISO 4587 |
Permabond 2010 Cyanoacrylate, gap filling PERMABOND 200 is a high viscosity product with good flow control useful in wire tacking applications or bonding components. It is fast setting and suitable for use on plastics, rubber and metals. Cy.. |
|||
Adhesive Bond Strength | >= 14.0 MPa | >= 2030 psi | Acrylic, Shear; ISO 4587 |
Permabond 2011 Cyanoacrylate, gel PERMABOND® 2011 is a thixotropic, fast-setting cyanoacrylate particularly suitable for use on vertical and porous substrates. This material can be used on metals, plastics, elastomers, ceramics and.. |
|||
Adhesive Bond Strength | 14.0 MPa | 2030 psi | Phenolic, Shear; ISO 4587 |
Permabond 2011 Cyanoacrylate, gel PERMABOND® 2011 is a thixotropic, fast-setting cyanoacrylate particularly suitable for use on vertical and porous substrates. This material can be used on metals, plastics, elastomers, ceramics and.. |
|||
Adhesive Bond Strength | <= 14.0 MPa | <= 2030 psi | Steel to Ferrite, Substrate Failure, Shear |
Permabond ES550 Epoxy Resin PERMABOND ES550 is a single-part epoxy paste which is slump-resistant (does not flow) during cure. The adhesive is toughened for maximum impact resistance, along with excellent peel and shear streng.. |
|||
Adhesive Bond Strength | 14.0 - 27.0 MPa | 2030 - 3920 psi | Zinc, Shear; ASTM D1002 |
Permabond ES550 Epoxy Resin PERMABOND ES550 is a single-part epoxy paste which is slump-resistant (does not flow) during cure. The adhesive is toughened for maximum impact resistance, along with excellent peel and shear streng.. |
|||
Adhesive Bond Strength | 14.0 - 41.0 MPa | 2030 - 5950 psi | Zinc, Shear; ASTM D1002 |
Permabond ES558 Epoxy Resin PERMABOND ES558 is a single-part epoxy paste which flows like solder when heated during curing. The adhesive is toughened for maximum impact resistance, along with excellent peel and shear strength... |
|||
Adhesive Bond Strength | 14.0 - 27.0 MPa | 2030 - 3920 psi | Aluminum, Shear; ISO 4587 |
Permabond ES562 Epoxy Resin PERMABOND® ES562 is a single-part epoxy adhesive which flows like solder when heated during curing. The adhesive has excellent adhesion to metal surfaces and composites. The high bond strength of t.. |
|||
Adhesive Bond Strength | 14.0 - 27.0 MPa | 2030 - 3920 psi | Zinc, Shear; ISO 4587 |
Permabond ES562 Epoxy Resin PERMABOND® ES562 is a single-part epoxy adhesive which flows like solder when heated during curing. The adhesive has excellent adhesion to metal surfaces and composites. The high bond strength of t.. |
|||
Adhesive Bond Strength | 14.0 - 27.0 MPa | 2030 - 3920 psi | Zinc, Shear; ASTM D1002 |
Permabond ES578 Epoxy Resin PERMABOND® ES578 is a single-part heat cured epoxy adhesive with excellent adhesion to metal surfaces, ceramics as well as composite materials. ES578 provides excellent thermal conductivity and bon.. |
|||
Adhesive Bond Strength | 14.0 MPa | 2030 psi | steel collar and pin shear; ISO 10123 |
Permabond HM160 Anaerobic Retaining Compound Permabond® HM160 is a medium viscosity liquid adhesive that cures when confined between metal parts to form a tough, hard plastic. In the uncured, liquid state, the adhesive wets the metal surfaces.. |
|||
Adhesive Bond Strength | >= 14.0 MPa | >= 2030 psi | Substrate Failure, Steel to Ferrite using Initiator 41 after 24 hours, Shear |
Permabond TA437 Toughened Acrylic Adhesive PERMABOND TA437 is a single component structural acrylic adhesive designed primarily for bonding metals, ferrites and ceramics. The typical fixture time of TA437 when used with Initiator 41 is 30 –.. |
|||
Adhesive Bond Strength | 14.0 - 20.0 MPa | 2030 - 2900 psi | Mild steel, Shear |
Permabond TA437 Toughened Acrylic Adhesive PERMABOND TA437 is a single component structural acrylic adhesive designed primarily for bonding metals, ferrites and ceramics. The typical fixture time of TA437 when used with Initiator 41 is 30 –.. |
|||
Adhesive Bond Strength | >= 14.0 MPa | >= 2030 psi | Substrate Failure, Steel to Ferrite after 24 hours, Shear |
Permabond TA439 Toughened Acrylic Adhesive Permabond® TA439 is a two component structural acrylic adhesive designed primarily for bonding metals, ferrites, ceramics and some plastics. The typical fixture time of is 10-30 seconds. The fast f.. |
|||
Adhesive Bond Strength | >= 14.0 MPa | >= 2030 psi | Ferrite/steel after 24 hours, Shear |
Permabond TA459 Toughened Acrylic Adhesive Permabond TA459 is a structural acrylic adhesive designed primarily for bonding metals, ferrites, ceramics and some thermoplastics. This product was specifically designed to be non-corrosive to sens.. |
|||
Adhesive Bond Strength | >= 14.0 MPa | >= 2030 psi | Ferrite/steel after 24 hours, Shear |
Permabond TA4590 Toughened Acrylic Adhesive Permabond TA4590 is a structural acrylic adhesive designed primarily for bonding metals, ferrites, ceramics and some thermoplastics. This product was specifically designed to be non-corrosive to sen.. |
|||
Adhesive Bond Strength | >= 14.0 MPa | >= 2030 psi | Substrate Failure, Steel to Ferrite, after 24 hours, Shear |
Permabond TA4592 Toughened Acrylic Adhesive PERMABOND® TA4592 is a two component structural acrylic adhesive ideal for bonding magnets and ferrites for electric motors on fast-moving production lines. Permabond® TA4592 provides high strengt.. |
|||
Adhesive Bond Strength | 14.0 - 17.0 MPa | 2030 - 2470 psi | Glass/steel, Shear |
Permabond UV7141 UV-curable Adhesive Permabond UV7141 is a UV-curable adhesive with a secondary anaerobic cure mechanism. This makes it ideal for bonding materials such as ceramic-coated glass, mirrors, etc. where UV-light cannot penet.. |
|||
Adhesive Bond Strength | 14.0 MPa | 2030 psi | Phenolic, Shear; ISO 4587 |
Permabond 240 Cyanoacrylate, gap filling PERMABOND® 240 is a high viscosity product useful in large gap applications. It is ideal for porous substrates. It is fast setting and suitable for use on plastics, rubber and metals. Cyanoacrylate.. |
|||
Adhesive Bond Strength | 14.0 MPa | 2030 psi | Phenolic, Shear; ISO 4587 |
Permabond 919 Cyanoacrylate, High temperature Features & Benefits: Rapid development of high strength; Ease of use – no mixing or heat cure; Bonds most materials; 100% reactive, no solvents.PERMABOND® 919 is an allyl cyanoacrylate adhesive. I.. |
|||
Adhesive Bond Strength | 14.0 MPa | 2030 psi | Phenolic, Shear; ISO 4587 |
Permabond 920 Cyanoacrylate, High temperature PERMABOND® 920 is the original allyl cyanoacrylate adhesive. It is a single part, low viscosity liquid that will cure rapidly at room temperature when pressed into a thin film between parts. PERMAB.. |
|||
Adhesive Bond Strength | 14.0 - 27.0 MPa | 2030 - 3920 psi | Zinc, Shear; ASTM D1002 |
Permabond ES569 Epoxy Resin PERMABOND® ES569 is a single-part heat cured epoxy adhesive with excellent adhesion to metal surfaces as well as composite materials. The high bond strength of this adhesive allows it to replace me.. |
|||
Adhesive Bond Strength | 14.0 MPa | 2030 psi | steel collar and pin shear; ISO 10123 |
Permabond HH040 Anaerobic Retainer Permabond® HH040 is a single component liquid that cures only when in contact with metal parts and oxygen is excluded. The liquid adhesive fills the “air space” between parts and upon cure unitiz.. |
|||
Adhesive Bond Strength | 14.0 MPa | 2030 psi | steel collar and pin shear; ISO 10123 |
Permabond HH040 Pure NSF 61 Approved Anaerobic Retainer Permabond® HH040 PURE is a single component liquid that cures only when in contact with metal parts and oxygen is excluded. The liquid adhesive fills the “air space” between parts and upon cure u.. |
|||
Adhesive Bond Strength | 14.0 MPa | 2030 psi | Tensile shear per ASTM D1002 on etched Al panel |
Von Roll Isola IMI E-Solder® 3022 Electrically Conductive Adhesive Data provided by Von Roll Isola USA.E-SOLDER® epoxy based resin systems can be used at room temperature on heat sensitive materials, can bond dissimilar materials, and do not have flux or residue t.. |
|||
Adhesive Bond Strength | 14.0 MPa | 2030 psi | Varies with substrates |
Loctite® 3273 Acrylic Bonding Adhesive Acrylic Bonding AdhesivesLoctite® Acrylic Adhesives were developed for bonding applications that require tensile, shear and peel strength combined with maximum impact, stress and shock resistance. .. |
|||
Adhesive Bond Strength | 14.0 MPa | 2030 psi | Tensile shear per ASTM D1002 on etched Al panel |
Von Roll Isola IMI E-Solder® 3012 Electrically Conductive Adhesive Data provided by Von Roll Isola USA.E-SOLDER® epoxy based resin systems can be used at room temperature on heat sensitive materials, can bond dissimilar materials, and do not have flux or residue t.. |
|||
Adhesive Bond Strength | >= 14.0 MPa | >= 2030 psi | Acrylic, Shear; ISO 4587 |
Permabond 910FS Cyanoacrylate, Methyl grade PERMABOND® 910FS is the original 100%-methyl cyanoacrylate adhesive. It is a single part, low viscosity liquid that will cure rapidly at room temperature when pressed into a thin film between parts.. |
|||
Adhesive Bond Strength | 14.0 MPa | 2030 psi | Tensile shear per ASTM D1002 on etched Al panel |
Von Roll Isola IMI E-Solder® 3025 Electrically Conductive Adhesive Data provided by Von Roll Isola USA.E-SOLDER® epoxy based resin systems can be used at room temperature on heat sensitive materials, can bond dissimilar materials, and do not have flux or residue t.. |
|||
Adhesive Bond Strength | 14.0 MPa @Temperature 25.0 °C |
2030 psi @Temperature 77.0 °F |
Tensile Lap Shear |
Henkel Hysol EA 9825 Paste Adhesive System Low-density, one-component epoxy syntactic for use on honeycomb composite parts requiring high compressive strength at temperatures up to 350°F / 177°C. Ideal for fastener or attachment potting an.. |