Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Adhesive Bond Strength | 9.65 MPa | 1400 psi | Lap shear; 2024 T3 Al Abraded / MEK Wipe |
Resinlab® EP1285HD-9 Highly Filled, Medium Viscosity Casting Resin Resinlab™ EP1285 (Formerly Lab Product W021901 series) is a highly filled, medium viscosity black casting resin designed for applications requiring a high degree of thermal conductivity and a low C.. |
|||
Adhesive Bond Strength | 9.65 - 16.5 MPa | 1400 - 2390 psi | Steel, Shear |
Permabond QFS16 Cyanoacrylate Activator The PERMABOND QFS 16 accelerates the cure of cyanoacrylate adhesives to provide a shorter set time. It can be used in a variety of applications but is especially useful when bonding porous or poorly.. |
|||
Adhesive Bond Strength | 9.65 - 36.5 MPa | 1400 - 5300 psi | Average value: 25.7 MPa Grade Count:8 |
Overview of materials for Epoxy Adhesive, Flexible This property data is a summary of similar materials in the MatWeb database for the category "Epoxy Adhesive, Flexible". Each property range of values reported is minimum and maximum values of appro.. |
|||
Adhesive Bond Strength | 9.65 MPa @Thickness 12.7 mm |
1400 psi @Thickness 0.500 in |
ASTM D229 |
Haysite H900 Polyester, Glass Reinforced H900 is recognized throughout the world as a reliable, consistent GPO-3 material. Standard size sheets are available in thicknesses ranging from .094" to 2.00". H900 also exhibits excellent smoke,.. |
|||
Adhesive Bond Strength | 9.65 MPa | 1400 psi | Phenolic-Phenolic; Substrate Failure; Tensile Lap Shear |
Master Bond MB306 Low Viscosity Methyl Cyanoacrylate Features superior bonding properties. Master Bond MB306 is a single component, low viscosity, rapid setting, methyl cyanoacrylate adhesive. Similar to other types of “super glue”, MB306 cures ver.. |
|||
Adhesive Bond Strength | 9.65 MPa | 1400 psi | Lap shear, alum to alum, 24 hrs @ 25°C |
Tra-Con Tra-Bond 2122 Metal Repair Aluminum Epoxy Adhesive TRA-BOND 2122 is a versatile aluminum metal filled epoxy formulation developed for modern industrial casting, bonding and repair applications where a strong aluminum-like adhesive is required. This .. |
|||
Adhesive Bond Strength | 9.65 MPa | 1400 psi | Lap shear, alum to alum, 7 days in water |
Tra-Con Tra-Bond 5126 Medium Viscosity Aerospace-Grade Epoxy Adhesive TRA-BOND 5126 AEROSPACE-GRADE EPOXY ADHESIVE is a two-part, clear (amber), medium viscosity, aerospace-grade epoxy adhesive system recommended for bonding a wide variety of materials for structural .. |
|||
Adhesive Bond Strength | 9.65 MPa | 1400 psi | Lap shear, alum to alum, 15 min @ 120°C |
Tra-Con Tra-Bond 546S04 Thixotropic UV/Blue Light Cure Adhesive TRA-BOND 546S04 is a thixotropic UV/blue light curable adhesive with a secondary heat cure. TRA-BOND 546S04 is ideal for general optics bonding, mounting of lenses, and glob top applications. The .. |
|||
Adhesive Bond Strength | 9.65 MPa | 1400 psi | Lap shear, alum to alum, 1 hr @ 150°C |
Tra-Con Tra-Duct 8205 One-Part Electrically Conductive Silver-Filled Epoxy TRA-DUCT 8205 is an electrically conducting silver-filled epoxy compound recommended for electronic bonding and sealing applications that require a combination of excellent mechanical and electrical.. |
|||
Adhesive Bond Strength | 9.65 MPa | 1400 psi | |
Trelleborg Emerson & Cuming Eccobond® 927-10 E Needle Bonding Epoxy Adhesive Emerson & Cuming 927-10 E Eccobond® Needle Bonding Epoxy AdhesiveOne component, fast curing, epoxy adhesive for needle bonding with polypropylene hubs. Also recommended for bonding sealing or insul.. |
|||
Adhesive Bond Strength | 9.65 MPa | 1400 psi | Lap Shear Strength |
Epoxyset Epoxibond EB-109M-4 Unfilled Epoxy Adhesive A two-component, unfilled, flexible epoxy adhesive used for bonding and small potting applications in the medical, electronics, and aerospace industries. EB-109M-4 puts low stress on fragile parts a.. |
|||
Adhesive Bond Strength | 9.65 MPa | 1400 psi | Lap Shear Strength |
Epoxyset Epoxiohm EO-21M-5 Electrically Conductive Epoxy Adhesive EO-21M-5 is an electrically conductive & thermally conductive, silver filled epoxy adhesive. This two component system is designed to be cured at room temperature or the cure can be accelerated by e.. |
|||
Adhesive Bond Strength | 9.65 MPa | 1400 psi | Lap Shear Strength |
Epoxyset Epoxiohm EO-24 Electrically Conductive Epoxy Adhesive EO-24 is a two components, 100% solids silver-filled epoxy system designed specifically for chip bonding in microelectronic and optoelectronic applications. It is used for thermal management applica.. |
|||
Adhesive Bond Strength | 9.65 MPa | 1400 psi | Lap Shear Strength |
Epoxyset Epoxiohm EO-30FST Electrically Conductive Epoxy Adhesive EO-30-FST is two part, fast cure, silver filled, and high electrical conductivity epoxy adhesive. Both components are silver filled permitting a simple 1:1 mix ratio by weight. It has smooth creamy .. |
|||
Adhesive Bond Strength | 9.65 MPa @Temperature 82.2 °C |
1400 psi @Temperature 180 °F |
Aluminum-Aluminum tensile shear |
Armstrong A-3/A Epoxy Adhesive A Jet black epoxy paste especially formulated for bonding rigid materials. When used with Activator A or E, A-3 exhibits excellent bonding properties to phenolics, precious stones, ceramics, glass,.. |
|||
Adhesive Bond Strength | 9.65 MPa @Temperature 25.0 °C |
1400 psi @Temperature 77.0 °F |
Aluminum-Aluminum tensile shear |
Armstrong C-4/D Epoxy Adhesive A low viscosity, clear amber, unfilled adhesive, recommended for use with activators D or W. C-4 with Activator W offers maximum versatility in that differing degrees of flexibility can be achieved .. |
|||
Adhesive Bond Strength | 9.65 MPa | 1400 psi | Lap shear, alum to alum |
Tra-Con Tra-Bond 872-3 Flexible Epoxy Adhesive TRA-BOND 872-3 transparent, flexible epoxy adhesive is designed for bonding materials with mismatched coefficients of thermal expansion. The long working life of this adhesive makes it ideal for use.. |
|||
Adhesive Bond Strength | 9.65 MPa | 1400 psi | Rogers Test Method |
Rogers Corporation 3001 Thermoplastic Chloro-Fluorocopolymer Bonding Film Rogers 3001 bonding film is a thermoplastic chloro-fluorocopolymer. It is recommended for bonding low dielectric constant PTFE (Teflon® fluorocarbon polymer) microwave stripline packages and other.. |