Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Adhesive Bond Strength | 7.58 MPa | 1100 psi | Lap shear, alum to alum, 4 hrs @ 25°C + 2 hrs @ 65°C |
Tra-Con Tra-Cast 3110 Low Density Epoxy Casting System TRA-CAST 3110 is a unicellular, low density, syntactic-foam epoxy resin casting system of medium viscosity that easily handles, mixes and cures at room temperature. Developed for industrial encapsul.. |
|||
Adhesive Bond Strength | 7.58 MPa | 1100 psi | Lap shear, alum to alum, 24 hrs @ 25°C |
Tra-Con Tra-Bond 216H02 Opaque Black Epoxy Casting Compound TRA-CAST 216H02 is a medium viscosity two-part formulation recommended for general purpose electrical potting and encapsulation applications where the combination of good mechanical thermal and elec.. |
|||
Adhesive Bond Strength | 7.58 MPa | 1100 psi | Lap shear, alum to alum, 15 min @ 100°C |
Tra-Con Tra-Bond 723C01 One-Part Medical Grade Adhesive TRA-BOND 723C01 is a fast, heat curing, one component adhesive targeted at medical applications. The material complies with USP Class VI toxicity requirements and is resistant to gamma sterilization.. |
|||
Adhesive Bond Strength | 7.58 MPa @Temperature 82.2 °C |
1100 psi @Temperature 180 °F |
Aluminum-Aluminum tensile shear |
Armstrong C-1/H20 Epoxy Adhesive A versatile, low viscosity, unfilled resin used for electrical potting and laminating applications. It is an excellent insulator, and provides outstanding chemical resistance to most compoundsInfor.. |
|||
Adhesive Bond Strength | 7.58 MPa | 1100 psi | Al-to-Al Lap Shear; Cured 1 hr at 25ºC; ASTM D1002 |
Aptek 6513-A/B Versatile, fast set adhesive APTEK 6513-A/B is a hazy clear, two component, general purpose, semi-rigid, paste adhesive for bonding to steel, aluminum, wood, concrete, glass, ceramics, bras, and a variety of plastics. It is sp.. |
|||
Adhesive Bond Strength | 7.58 MPa | 1100 psi | Lap shear; 2024 T3 Al Abraded / MEK Wipe; TM R050-37 |
Resinlab® EP1296 Highly Filled, Moderately Thixotropic Black Casting Resin Resinlab™ EP1296 is a highly filled, moderately thixotropic black casting resin designed for applications requiring good thermal conductivity, low shrinkage and a low CTE. It was especially formula.. |