Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Fatigue Strength | 490 MPa @# of Cycles 1.00e+7 |
71100 psi @# of Cycles 1.00e+7 |
Sheet; Reverse Bend (UTS = 772 MPa) |
TIMET TIMETAL® 230 Titanium Alloy (Ti-2.5Cu); STA Cold Formable Medium-Strength AlloyFeatures: This binary, age hardening alloy combines the easy formability and weldability of commercially pure titanium with improved mechanical properties, particu.. |
|||
Fatigue Strength | <= 490 MPa @# of Cycles 2.00e+6 |
<= 71100 psi @# of Cycles 2.00e+6 |
|
ArcelorMittal HSLA 460 High strength low alloy steel for cold forming, Hot Rolled Available in the following: S460MCDescription: Steels in the HSLA (High Strength Low Alloy) range are hardened by a combination of precipitation and grain size refining, resulting in high strength w.. |
|||
Fatigue Strength | <= 490 MPa @# of Cycles 1.00e+7 |
<= 71100 psi @# of Cycles 1.00e+7 |
|
ArcelorMittal HSLA 460 High strength low alloy steel for cold forming, Hot Rolled Available in the following: S460MCDescription: Steels in the HSLA (High Strength Low Alloy) range are hardened by a combination of precipitation and grain size refining, resulting in high strength w.. |
|||
Fatigue Strength | <= 490 MPa @# of Cycles 2.00e+6 |
<= 71100 psi @# of Cycles 2.00e+6 |
|
ArcelorMittal FB 590 Hot rolled ferrite-bainite steel Available in the following: uncoated (HDT590F)Description: This range of hot-rolled high strength steels has been developed to meet weight reduction requirements. It comprises four strength levels: .. |
|||
Fatigue Strength | <= 490 MPa @# of Cycles 1.00e+7 |
<= 71100 psi @# of Cycles 1.00e+7 |
|
ArcelorMittal FB 590 Hot rolled ferrite-bainite steel Available in the following: uncoated (HDT590F)Description: This range of hot-rolled high strength steels has been developed to meet weight reduction requirements. It comprises four strength levels: .. |