Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Modulus of Elasticity | 9.00 - 10.0 GPa | 1310 - 1450 ksi | Injection; ISO 527 |
Raschig Group AMPLA® 2000 melamine-modified polyester Halogen-free, organically and inorganically filled melamine-modified Polyester molding compound. Low post-shrinkage, very good electrical values, high heat resistance, very good sliding behavior, ve.. |
|||
Modulus of Elasticity | 8.00 - 10.0 GPa | 1160 - 1450 ksi | Compression; ISO 527 |
Raschig Group DECAL® 572R Phenolic Glass-fiber reinforced phenolic molding compound. Exceptional heat resistance with regard to maintaining surface finish and mechanical properties, outstanding mechanical properties, excellent rotati.. |
|||
Modulus of Elasticity | 8.00 - 10.0 GPa | 1160 - 1450 ksi | Injection; ISO 527 |
Raschig Group MELOPAS® 156 MF Melamine Glass fiber reinforced Melamine molding compound. This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU directives 2002/95 (RoHS), 200.. |
|||
Modulus of Elasticity | 4.50 - 10.0 GPa @Temperature 60.0 - 150 °C |
653 - 1450 ksi @Temperature 140 - 302 °F |
Average value: 6.93 GPa Grade Count:1 |
Overview of materials for Polybutylene Terephthalate (PBT), 50% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), 50% Glass Fiber Filled". Specific grades with glass content between 45.. |
|||
Modulus of Elasticity | 4.30 - 10.0 GPa | 624 - 1450 ksi | Average value: 6.97 GPa Grade Count:18 |
Overview of materials for Acrylonitrile Butadiene Styrene (ABS), 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Acrylonitrile Butadiene Styrene (ABS), 30% Glass Fiber Filled". Specific grades with glass content betwe.. |
|||
Modulus of Elasticity | 8.00 - 10.0 GPa | 1160 - 1450 ksi | ISO 527 |
Raschig Group SURAPLAST UPA 63 UP Glass fiber reinforced polyester molding compound. Minimal mold shrinkage and post-shrinkage, very good arc resistance, very good mechanical strength. This product meets the allowed upper limits for.. |
|||
Modulus of Elasticity | 0.827 - 10.0 GPa | 120 - 1450 ksi | Average value: 3.74 GPa Grade Count:17 |
Overview of materials for Epoxy, Cast, Unreinforced This property data is a summary of similar materials in the MatWeb database for the category "Epoxy, Cast, Unreinforced". Each property range of values reported is minimum and maximum values of appr.. |
|||
Modulus of Elasticity | 2.60 - 10.0 GPa | 377 - 1450 ksi | Average value: 5.70 GPa Grade Count:6 |
Overview of materials for Nylon 6, Mineral Reinforced, Impact Grade This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Mineral Reinforced, Impact Grade". Each property range of values reported is minimum and maximu.. |
|||
Modulus of Elasticity | 8.05 - 10.0 GPa @Temperature 80.0 - 80.0 °C |
1170 - 1450 ksi @Temperature 176 - 176 °F |
Average value: 8.63 GPa Grade Count:4 |
Overview of materials for Nylon 66/6, 40% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66/6, 40% Glass Fiber Reinforced". Specific grades with glass content between 35% and 44% are incl.. |
|||
Modulus of Elasticity | 1.70 - 10.0 GPa | 247 - 1450 ksi | Average value: 4.74 GPa Grade Count:75 |
Overview of materials for Nylon 66, Glass Bead Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Glass Bead Filled". Each property range of values reported is minimum and maximum values of ap.. |
|||
Modulus of Elasticity | 0.400 - 10.0 GPa | 58.0 - 1450 ksi | Average value: 6.07 GPa Grade Count:53 |
Overview of materials for Nylon 66, 40% Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 40% Mineral Filled". Specific grades with primary filler content between 35% and 44% are inclu.. |
|||
Modulus of Elasticity | 0.750 - 9.98 GPa | 109 - 1450 ksi | Average value: 2.43 GPa Grade Count:25 |
Overview of materials for Nylon 612, Unreinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 612, Unreinforced". Each property range of values reported is minimum and maximum values of approp.. |
|||
Modulus of Elasticity | 1.40 - 10.0 GPa | 203 - 1450 ksi | Average value: 3.12 GPa Grade Count:6 |
Overview of materials for Nylon, Amorphous Transparent Alloy This property data is a summary of similar materials in the MatWeb database for the category "Nylon, Amorphous Transparent Alloy". Each property range of values reported is minimum and maximum value.. |
|||
Modulus of Elasticity | 1.65 - 10.0 GPa | 240 - 1450 ksi | Average value: 2.80 GPa Grade Count:69 |
Overview of materials for Nylon 66, PTFE Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, PTFE Filled". Each property range of values reported is minimum and maximum values of appropri.. |
|||
Modulus of Elasticity | 2.25 - 10.0 GPa @Temperature 60.0 - 160 °C |
326 - 1450 ksi @Temperature 140 - 320 °F |
Average value: 5.59 GPa Grade Count:7 |
Overview of materials for Polyethersulfone (PES) This property data is a summary of similar materials in the MatWeb database for the category "Polyethersulfone". Each property range of values reported is minimum and maximum values of appropriate M.. |
|||
Modulus of Elasticity | 8.60 - 10.0 GPa @Temperature 60.0 - 160 °C |
1250 - 1450 ksi @Temperature 140 - 320 °F |
Average value: 9.41 GPa Grade Count:2 |
Overview of materials for Polyethersulfone (PES), 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyethersulfone (PES), 30% Glass Fiber Filled". Specific grades with glass content between 25% and 34% .. |