Polymer Property : Modulus of Elasticity = 1020 ksi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Modulus of Elasticity	5.00 - 7.00 GPa	725 - 1020 ksi	Compression; ISO 527
Raschig Group 6501 DAIP Glass-fiber reinforced diallyl isophthalate molding compound. Good mechanical strength together with retention of high electrical isolation properties under hot humid conditions, exceptional dimensi..
Modulus of Elasticity	5.00 - 7.00 GPa	725 - 1020 ksi	Compression; ISO 527
Raschig Group AMPLA® 2000 melamine-modified polyester Halogen-free, organically and inorganically filled melamine-modified Polyester molding compound. Low post-shrinkage, very good electrical values, high heat resistance, very good sliding behavior, ve..
Modulus of Elasticity	5.00 - 7.00 GPa	725 - 1020 ksi	Injection; ISO 527
Raschig Group AMPLA® 2500 melamine-modified polyester Halogen-free, organically and inorganically filled melamine-modified Polyester molding compound. Excellent elasticity and shock resistance, low post-shrinkage, very good electrical values, high heat..
Modulus of Elasticity	5.00 - 7.00 GPa	725 - 1020 ksi	Injection; ISO 178
Raschig Group AMPLA® 7250 melamine-modified polyester Cellulose reinforced melamine-modified Polyester molding compound. Very good electrical values, excellent heat resistance, excellent surface quality, low post shrinkage. This product meets the allow..
Modulus of Elasticity	5.00 - 7.00 GPa	725 - 1020 ksi	Injection; ISO 527
Raschig Group AMPLA® 7500 melamine-modified polyester Organically and inorganically filled melamine modified Polyester molding compound. Low post-shrinkage, very good electrical values, excellent heat resistance, very good sliding behavior and wear sta..
Modulus of Elasticity	5.00 - 7.00 GPa	725 - 1020 ksi	Injection; ISO 527
Raschig Group DECAL® 1760 Phenolic Glass-fiber reinforced phenolic molding compound. Very good electrical properties, good chemical resistance and mechanical properties. This product meets the allowed upper limits for heavy metals an..
Modulus of Elasticity	5.00 - 7.00 GPa	725 - 1020 ksi	Compression; ISO 527
Raschig Group DECAL® 937 Phenolic Mica reinforced phenolic molding compound. This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU directives 2002/95 (RoHS), 2002/96 (W..
Modulus of Elasticity	2.90 - 7.00 GPa	420 - 1020 ksi	Average value: 4.13 GPa Grade Count:21
Overview of materials for Acetal Copolymer, Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Acetal Copolymer, Mineral Filled". Each property range of values reported is minimum and maximum values ..
Modulus of Elasticity	6.55 - 7.03 GPa	950 - 1020 ksi	Average value: 6.76 GPa Grade Count:4
Overview of materials for PVC, 20% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "PVC, 20% Glass Fiber Reinforced". Specific grades with glass content between 15% and 24% are included. E..
Modulus of Elasticity	0.100 - 7.00 GPa	14.5 - 1020 ksi	Average value: 1.54 GPa Grade Count:94
Overview of materials for Polyvinylidinefluoride (PVDF), Molded/Extruded This property data is a summary of similar materials in the MatWeb database for the category "Polyvinylidinefluoride (PVDF), Molded/Extruded". Each property range of values reported is minimum and m..
Modulus of Elasticity	3.10 - 7.00 GPa	450 - 1020 ksi	Average value: 6.21 GPa Grade Count:12
Overview of materials for Polyphenylene Ether, 20% Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Ether, 20% Glass Filled". Specific grades with glass content between 15% and 24% are inclu..
Modulus of Elasticity	2.55 - 7.00 GPa	370 - 1020 ksi	Average value: 5.73 GPa Grade Count:12
Overview of materials for Polysulfone, 20% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polysulfone, 20% Glass Fiber Reinforced". Specific grades with glass content between 15% and 24% are inc..