Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Modulus of Elasticity | 2.60 GPa | 377 ksi | 4 mm thick;10.0 mm wide molded rod; ISO 178 |
Premix Thermoplastics PRE-ELEC® PET 1451 PRE-ELEC PET 1451 is a conductive thermoplastic compound based on PETG. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-ELEC PET 14.. |
|||
Modulus of Elasticity | 2.60 - 3.00 GPa | 377 - 435 ksi | ASTM D638-04 |
Proto3000 Objet Digital Materials™ RGD5160-DM ABS-like Prototyping Polymer Objet ABS-like Digital Material made of Object RGD515 & Objet RGD535Digital Materials are made up of two Objet materials. The two materials are combined in specific concentrations and structures, to.. |
|||
Modulus of Elasticity | 2.60 - 14.0 GPa | 377 - 2030 ksi | Average value: 6.52 GPa Grade Count:156 |
Overview of materials for Polybutylene Terephthalate (PBT), 20% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), 20% Glass Fiber Filled". Specific grades with glass content between 15.. |
|||
Modulus of Elasticity | 2.60 GPa | 377 ksi | 1 mm/min; ASTM D638 |
Solvay Specialty Polymers Solef® 3208/0150 Anti-friction PVDF Compound
(discontinued **) Key features of this grade: Anti-friction, Formulated. Recommended processing is injection. Available as granules.General information about SOLEF® PVDF: SOLEF® PVDF is a fluorinated semi-crysta.. |
|||
Modulus of Elasticity | 2.60 GPa | 377 ksi | Youngs Modulus, ASTM D638, 10%/min. |
EVALCA EVAL® F100 Ethylene Vinyl Alcohol Copolymer Resin
(discontinued **) 32 mol % Ethylene.Data provided by EVALCA. Applications: Melt phase forming. EVOH is used in packaging applications because of its outstanding gas barrier properties.EVAL™ is now produced as a pa.. |
|||
Modulus of Elasticity | 2.60 GPa | 377 ksi | Youngs Modulus, ASTM D638, 10%/min. |
EVALCA EVAL® LC-F101BZ Ethylene Vinyl Alcohol Copolymer Resin
(discontinued **) 32 mol % Ethylene.Data provided by EVALCA. Applications: Blown film, cast film, melt phase forming, blow molding, profile coextrusion. EVOH is used in packaging applications because of its outstan.. |
|||
Modulus of Elasticity | 2.60 GPa | 377 ksi | Youngs Modulus, ASTM D638, 10%/min. |
EVALCA EVAL® EP-F104BW Ethylene Vinyl Alcohol Copolymer Resin
(discontinued **) 32 mol % Ethylene.Data provided by EVALCA. Applications: Cast film, blow molding, tubes, coex coating. EVOH is used in packaging applications because of its outstanding gas barrier properties.EVAL.. |
|||
Modulus of Elasticity | 2.60 - 10.0 GPa | 377 - 1450 ksi | Average value: 5.70 GPa Grade Count:6 |
Overview of materials for Nylon 6, Mineral Reinforced, Impact Grade This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Mineral Reinforced, Impact Grade". Each property range of values reported is minimum and maximu.. |
|||
Modulus of Elasticity | 2.60 GPa | 377 ksi | ISO 527 |
GEHR Plastics POM-C Acetal Polyoxymethylene can be used in temperatures up to 100°C. The high surface strength is only surpassed by a few materials. POM shows good sliding properties and high resistance to wear and tear be.. |
|||
Modulus of Elasticity | 2.60 - 2.80 GPa | 377 - 406 ksi | 30-40% better than Nylon 6 with 4-5% loading |
Süd-Chemie Nanofil® 9 Polymer Additive Application:PS, PA 6, PA 6.6, PA-AlloysElectronicsElectrical PartsImproves: Mechanical Properties |
|||
Modulus of Elasticity | 2.60 - 2.80 GPa | 377 - 406 ksi | 30-40% better than Nylon 6 with 4-5% loading |
Süd-Chemie Nanofil® SE 3010 Polymer Additive Application:PA 6, PA 6.6, PET, ABS, PS, PC-AlloysElectronicsElectrical PartsAutomotiveTechnical PartsImproves: Mechanical Properties, Melt Viscosity |
|||
Modulus of Elasticity | 2.60 GPa | 377 ksi | ASTM D638 |
Toyobo T-772 Nylon, Plating Grade Key Feature: Plating grade; Glass fiber and mineral reinforced grades; thermal and impact resistantInformation provided by Toyobo Co., Ltd |
|||
Modulus of Elasticity | 2.60 GPa | 377 ksi | TD; ExxonMobil Method |
ExxonMobil Label-Lyte™ 65LTR741 OPP Film Product Description: A biaxially oriented, white opaque multi-layer polypropylene film with an expanded core, and coated with a proprietary static resistant coating on one side. The non-coated gloss.. |
|||
Modulus of Elasticity | 2.60 GPa | 377 ksi | TD; ExxonMobil Method |
ExxonMobil Label-Lyte™ 70LTR742 OPP Film Product Description: A matte finish, coated, white, polypropylene film designed for use in demanding thermal transfer, pressure-sensitive label applications. It is also compatible with a wide range .. |
|||
Modulus of Elasticity | 2.60 GPa | 377 ksi | TD; ExxonMobil Method |
ExxonMobil Metallyte™ UHB 35MU842 OPP Film Product Description: A metalized high opacity white oriented polypropylene film. It is biaxially oriented, multi-layer polypropylene film with aluminum deposited on an adhesion promoting layer. The .. |
|||
Modulus of Elasticity | 2.60 GPa | 377 ksi | TD; ExxonMobil Method |
ExxonMobil Label-Lyte™ 60LH538 OPP Film Product Description: A super white opaque polypropylene film face stock with a proprietary caviated core providing high yield and excellent opacity. The coated print surface provides exceptional ink.. |
|||
Modulus of Elasticity | 2.60 GPa | 377 ksi | ISO R527 |
Arkema Group Orgalloy® RS 6600 Polyamide 6.6 Alloy Polyamide Alloy, Rigid grade, Nylon 6.6 basedTubes / Mandrels / Profiles / CablesInformation provided by Arkema Group |
|||
Modulus of Elasticity | 2.60 GPa | 377 ksi | Conditioned; ISO 178 |
Addiplast Addilene H 290 M20F Flame Retardant Polypropylene, 20% Mineral Filled Flame retardant, mineral filled, with halogensInformation provided by Addiplast. |
|||
Modulus of Elasticity | 2.60 GPa | 377 ksi | ISO 178 |
Addiplast Addilene H 526 N30 Polypropylene Homopolymer Improved rigidity, high durabilityInformation provided by Addiplast. |
|||
Modulus of Elasticity | 2.60 GPa | 377 ksi | Conditioned; ISO 178 |
Addiplast Addilene J 490 M20F Flame Retardant Polypropylene, 20% Mineral Filled Flame retardant, mineral filled, with halogensInformation provided by Addiplast. |
|||
Modulus of Elasticity | 2.60 GPa | 377 ksi | ISO 527 |
BASF Ultraform H 4320 Q600 POM Ultraform H4320 Q600 is an extrusion POM high molecular weight grade. This grade enables high extrusion rates with thick-walled product. It also exhibits high thermal stability and a low tendency .. |
|||
Modulus of Elasticity | 2.60 GPa | 377 ksi | SIO 527 |
BASF Ultraform N 2310P Q600 POM Ultraform N2310P Q600 is a general-purpose injection molding POM grade containing special lubricant. Low frictional coefficient giving extremely low wear with otherwise unaltered mechanical propert.. |
|||
Modulus of Elasticity | 2.60 GPa | 377 ksi | ISO 527-2 |
BASF Ultraform® H2320 004 POM Description: Is a POM, high-molecular-weight grade for extrusion of small thin-walled pipes and panel.Information provided by BASF |
|||
Modulus of Elasticity | 2.60 GPa | 377 ksi | 1 mm/min; ASTM D638 |
Solvay Specialty Polymers Solef® 1008 PVDF Homopolymer
(discontinued **) Key features of this grade: Low Viscosity, All Purpose, Injection, Virgin. Recommended processing is injection. Available as powder & granules.General information about SOLEF® PVDF: SOLEF® PVDF .. |
|||
Modulus of Elasticity | 2.60 GPa | 377 ksi | Conditioned; ISO 178 |
Addiplast Addinyl B2 ZM30 Nylon 6, 30% Mineral Filled Mineral filled, increased thermal aging stabilityInformation provided by Addiplast. |
|||
Modulus of Elasticity | 2.60 GPa | 377 ksi | ISO 527-2 |
BASF Ultraform® W2320 0035 LEV POM Description: Is a POM, very free-flowing, rapidly solidifying grade for injection molding, with reduced emission potential.Information provided by BASF |