Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Modulus of Elasticity | 203 GPa | 29400 ksi | |
Latrobe Lescalloy® AF 1410 VIM-VAR ; 9 in High Strength Alloy Steel LESCALLOY AF1410 VIM-VAR steel exhibits both high strength and very high fracture toughness. It is typically used in the 235/260 ksi (1620/1793 MPa) tensile strength range for a
variety of critical,.. |
|||
Modulus of Elasticity | 203 GPa @Temperature 93.0 °C |
29400 ksi @Temperature 199 °F |
heat-treated at 1121°C (2050°F), rapid quenched, plate |
Haynes Hastelloy® C-22® alloy, 0.71-3.2 mm thick sheet, solution heat treated HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
Modulus of Elasticity | 203 GPa @Temperature 93.0 °C |
29400 ksi @Temperature 199 °F |
heat-treated at 1121°C (2050°F), rapid quenched, plate |
Haynes Hastelloy® C-22® alloy, 10% cold worked sheet, aged 100 hours at 500°C HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
Modulus of Elasticity | 203 GPa @Temperature 93.0 °C |
29400 ksi @Temperature 199 °F |
heat-treated at 1121°C (2050°F), rapid quenched, plate |
Haynes Hastelloy® C-22® alloy, 12.7-50.8 mm thick bar, solution heat treated HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
Modulus of Elasticity | 203 GPa @Temperature 93.0 °C |
29400 ksi @Temperature 199 °F |
heat-treated at 1121°C (2050°F), rapid quenched, plate |
Haynes Hastelloy® C-22® alloy, 20% cold worked sheet HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
Modulus of Elasticity | 203 GPa @Temperature 93.0 °C |
29400 ksi @Temperature 199 °F |
heat-treated at 1121°C (2050°F), rapid quenched, plate |
Haynes Hastelloy® C-22® alloy, 40% cold worked sheet HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
Modulus of Elasticity | 203 GPa @Temperature 93.0 °C |
29400 ksi @Temperature 199 °F |
heat-treated at 1121°C (2050°F), rapid quenched, plate |
Haynes Hastelloy® C-22® alloy, 50% cold worked sheet HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
Modulus of Elasticity | 203 GPa @Temperature 93.0 °C |
29400 ksi @Temperature 199 °F |
heat-treated at 1121°C (2050°F), rapid quenched, plate |
Haynes Hastelloy® C-22® alloy, all-weld metal, GMAW short arc HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
Modulus of Elasticity | 203 GPa @Temperature 93.0 °C |
29400 ksi @Temperature 199 °F |
heat-treated at 1121°C (2050°F), rapid quenched, plate |
Haynes Hastelloy® C-22® alloy, GTAW weld, C-22 base metal, C-22 weld metal HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
Modulus of Elasticity | 203 GPa @Temperature 93.0 °C |
29400 ksi @Temperature 199 °F |
heat-treated at 1121°C (2050°F), rapid quenched, plate |
Haynes Hastelloy® C-22® alloy, GTAW, aged 4000 hours at 450°C (800°F), notched HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
Modulus of Elasticity | 203 GPa @Temperature 93.0 °C |
29400 ksi @Temperature 199 °F |
heat-treated at 1121°C (2050°F), rapid quenched, plate |
Haynes Hastelloy® C-22® alloy, GTAW, aged 4000 hours at 450°C (800°F), unnotched HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
Modulus of Elasticity | 203 GPa @Temperature 93.0 °C |
29400 ksi @Temperature 199 °F |
heat-treated at 1121°C (2050°F), rapid quenched, plate |
Haynes Hastelloy® C-22® alloy, SMAW weld, C-22 base metal, C-22 weld metal HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
Modulus of Elasticity | 203 GPa @Temperature 93.0 °C |
29400 ksi @Temperature 199 °F |
heat-treated at 1121°C (2050°F), rapid quenched, plate |
Haynes Hastelloy® C-22® alloy, transverse, GMAW short arc weldment, plate HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
Modulus of Elasticity | 203 GPa @Temperature 93.0 °C |
29400 ksi @Temperature 199 °F |
heat-treated at 1121°C (2050°F), rapid quenched, plate |
Haynes Hastelloy® C-22® alloy, transverse, GTAW weldment, sheet - plate HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
Modulus of Elasticity | 203 GPa | 29400 ksi | |
Latrobe Lescalloy® AF 1410 VIM-VAR ; 13.5 in High Strength Alloy Steel LESCALLOY AF1410 VIM-VAR steel exhibits both high strength and very high fracture toughness. It is typically used in the 235/260 ksi (1620/1793 MPa) tensile strength range for a
variety of critical,.. |
|||
Modulus of Elasticity | 203 GPa | 29400 ksi | At 90° to rolling direction |
AK Steel TRAN-COR® H-0 CARLITE® Grain Oriented Electrical Steel TRAN-COR H CARLITE® high permeability electrical steels offer an outstanding degree of grain orientation, This combination of higher permeability with low residual stress offers the potential for l.. |
|||
Modulus of Elasticity | 203 GPa | 29400 ksi | At 90° to rolling direction |
AK Steel TRAN-COR® H-2 CARLITE® DR® Grain Oriented Electrical Steel TRAN-COR H CARLITE® high permeability electrical steels offer an outstanding degree of grain orientation, This combination of higher permeability with low residual stress offers the potential for l.. |
|||
Modulus of Elasticity | 203 GPa | 29400 ksi | At 90° to rolling direction |
AK Steel TRAN-COR® H-2 CARLITE® Grain Oriented Electrical Steel TRAN-COR H CARLITE® high permeability electrical steels offer an outstanding degree of grain orientation, This combination of higher permeability with low residual stress offers the potential for l.. |
|||
Modulus of Elasticity | 203 GPa | 29400 ksi | At 90° to rolling direction |
AK Steel TRAN-COR® H-0 CARLITE® DR® Grain Oriented Electrical Steel TRAN-COR H CARLITE® high permeability electrical steels offer an outstanding degree of grain orientation, This combination of higher permeability with low residual stress offers the potential for l.. |
|||
Modulus of Elasticity | 203 GPa @Temperature 93.0 °C |
29400 ksi @Temperature 199 °F |
heat-treated at 1121°C (2050°F), rapid quenched, plate |
Haynes Hastelloy® C-22® alloy, GMAW, as welded, notched HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
Modulus of Elasticity | 203 GPa @Temperature 93.0 °C |
29400 ksi @Temperature 199 °F |
heat-treated at 1121°C (2050°F), rapid quenched, plate |
Haynes Hastelloy® C-22® alloy, GTAW weld, 904L base metal, C-22 weld metal HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
Modulus of Elasticity | 203 GPa @Temperature 93.0 °C |
29400 ksi @Temperature 199 °F |
heat-treated at 1121°C (2050°F), rapid quenched, plate |
Haynes Hastelloy® C-22® alloy, GTAW, as welded, unnotched HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
Modulus of Elasticity | 203 GPa @Temperature 93.0 °C |
29400 ksi @Temperature 199 °F |
heat-treated at 1121°C (2050°F), rapid quenched, plate |
Haynes Hastelloy® C-22® alloy, transverse, GTAW short arc weldment, plate HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
Modulus of Elasticity | 203 GPa @Temperature 93.0 °C |
29400 ksi @Temperature 199 °F |
heat-treated at 1121°C (2050°F), rapid quenched, plate |
Haynes Hastelloy® C-22® alloy, transverse, GTAW spray weldment, 12.7 mm (1/2 in.) thick plate HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
Modulus of Elasticity | 203 GPa @Temperature 93.0 °C |
29400 ksi @Temperature 199 °F |
heat-treated at 1121°C (2050°F), rapid quenched, plate |
Haynes Hastelloy® C-22® alloy, transverse, SMAW weldment, 19.1 mm thick plate HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
Modulus of Elasticity | 203 GPa | 29400 ksi | |
Latrobe Lescalloy® AF 1410 VIM-VAR ; 6 in High Strength Alloy Steel LESCALLOY AF1410 VIM-VAR steel exhibits both high strength and very high fracture toughness. It is typically used in the 235/260 ksi (1620/1793 MPa) tensile strength range for a
variety of critical,.. |
|||
Modulus of Elasticity | 203 GPa @Temperature 93.0 °C |
29400 ksi @Temperature 199 °F |
heat-treated at 1121°C (2050°F), rapid quenched, plate |
Haynes Hastelloy® C-22® alloy, 6.4-19.1 mm thick plate, solution heat treated HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
Modulus of Elasticity | 203 GPa @Temperature 93.0 °C |
29400 ksi @Temperature 199 °F |
heat-treated at 1121°C (2050°F), rapid quenched, plate |
Haynes Hastelloy® C-22® alloy, 60% cold worked sheet HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
Modulus of Elasticity | 203 GPa @Temperature 93.0 °C |
29400 ksi @Temperature 199 °F |
heat-treated at 1121°C (2050°F), rapid quenched, plate |
Haynes Hastelloy® C-22® alloy, GTAW weld, 316L base metal, C-22 weld metal HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
Modulus of Elasticity | 203 GPa @Temperature 93.0 °C |
29400 ksi @Temperature 199 °F |
heat-treated at 1121°C (2050°F), rapid quenched, plate |
Haynes Hastelloy® C-22® alloy, SMAW weld, 904L base metal, C-22 weld metal HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |