Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Modulus of Elasticity | 8.30 GPa | 1200 ksi | ASTM D638 |
Owens Corning Glass Fiber Reinforced Nylon 6/6, 30 wt.% glass Nylons, as a group, are inert to most organic solvents. They resist alkalis and salt solutions and they are attacked by strong mineral acids and oxidizing agents. Data provided by the manufacturer,.. |
|||
Modulus of Elasticity | 8.30 GPa | 1200 ksi | ASTM D638 |
Owens Corning Glass Fiber Reinforced Polyester (PBT), 30 wt.% glass Thermoplastic Polyesters are resistant to most organic solvents, weak acids and alkalis. They are not recommended with strong acids and alkalis or for prolonged use in hot water. Data provided by t.. |
|||
Modulus of Elasticity | 8.27 - 32.0 GPa | 1200 - 4640 ksi | Average value: 13.0 GPa Grade Count:25 |
Overview of materials for Polybutylene Terephthalate (PBT), 40% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), 40% Glass Fiber Filled". Specific grades with glass content between 35.. |
|||
Modulus of Elasticity | 8.30 - 22.5 GPa @Temperature 60.0 - 150 °C |
1200 - 3260 ksi @Temperature 140 - 302 °F |
Average value: 14.5 GPa Grade Count:1 |
Overview of materials for Nylon 66, Carbon Fiber/PTFE Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Carbon Fiber/PTFE Filled". Each property range of values reported is minimum and maximum value.. |
|||
Modulus of Elasticity | 8.30 GPa | 1200 ksi | |
Lehmann & Voss LUVOCOM® 50/CF/20 Polycarbonate, with carbon fiber, low-warpage Applications: Data processing machinery, precision engineering, film and photo industry, sporting and leisure goods, medical enineering.Strong, stiff parts.Reduced moment of inertia compared with me.. |
|||
Modulus of Elasticity | 8.30 GPa | 1200 ksi | ISO 527-1/-2 |
BASF Ultramid® KR 4365 G5 35% Glass Filled PA6/6T FR (Dry) Description: Partially aromatic polyamide; flame retardant based on red phosphorus; low water absorption, high melting point (295°C); low tendency to form deposits on electrical contacts, very resi.. |
|||
Modulus of Elasticity | 8.27 - 28.3 GPa | 1200 - 4100 ksi | Average value: 16.8 GPa Grade Count:3 |
Overview of materials for Polyphenylene Sulfide (PPS), NCG Fiber This property data is a summary of similar materials in the MatWeb database for the category "PPS + NGG". Each property range of values reported is minimum and maximum values of appropriate MatWeb e.. |
|||
Modulus of Elasticity | 8.27 - 11.0 GPa | 1200 - 1600 ksi | ASTM D638 |
Premix Premi-Glas® 1200-24 Polyester SMC
(discontinued **) Premi-Glas® 1200-24 is a 24% fiberglass-reinforced, thermoset, sheet molding compound designed for Class A Heavy Truck - Bus body panels and Marine cowls parts where smooth, flat, ripple free surfa.. |