Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Modulus of Elasticity | 13.0 - 15.0 GPa | 1890 - 2180 ksi | Injection; ISO 527 |
Raschig Group 2567 AMC Glass fiber-reinforced and inorganically filled polyester molding compound (UP) in various colors. Outstanding mechanical strength similar to BMC/SMC, very good electrical isolation properties and .. |
|||
Modulus of Elasticity | 13.0 - 15.0 GPa | 1890 - 2180 ksi | Injection; ISO 527 |
Raschig Group 2568 AMC Glass fiber-reinforced polyester molding compound. Very good mechanical strength, very good electrical properties and dimensional stability, heat resistant up to 500°C for short time - usable for s.. |
|||
Modulus of Elasticity | 13.0 - 15.0 GPa | 1890 - 2180 ksi | Injection; ISO 527 |
Raschig Group 2572 AMC Glass fiber reinforced Polyester molding compound. Very good mechanical strength, very good electrical properties and dimensional stability, good abrasion stability, high flame retardance in combin.. |
|||
Modulus of Elasticity | 0.824 - 15.0 GPa | 119 - 2180 ksi | Average value: 9.44 GPa Grade Count:182 |
Overview of materials for Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled". Specific grades with glass content between 25.. |
|||
Modulus of Elasticity | 2.28 - 15.0 GPa | 331 - 2180 ksi | Average value: 9.02 GPa Grade Count:8 |
Overview of materials for PET + PBT Unreinforced This property data is a summary of similar materials in the MatWeb database for the category "PET + PBT Unreinforced". Each property range of values reported is minimum and maximum values of appropr.. |
|||
Modulus of Elasticity | 13.5 - 15.0 GPa @Temperature 70.0 - 70.0 °C |
1960 - 2180 ksi @Temperature 158 - 158 °F |
Average value: 10.1 GPa Grade Count:1 |
Overview of materials for Nylon 6, 50% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 50% Glass Fiber Filled". Specific grades with glass content between 45% and 54% are included. E.. |
|||
Modulus of Elasticity | 13.5 - 15.0 GPa @Time 180000 - 1.44e+6 sec |
1960 - 2180 ksi @Time 50.0 - 400 hour |
Average value: 10.1 GPa Grade Count:1 |
Overview of materials for Nylon 6, 50% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 50% Glass Fiber Filled". Specific grades with glass content between 45% and 54% are included. E.. |
|||
Modulus of Elasticity | 1.00 - 15.0 GPa | 145 - 2180 ksi | Average value: 8.43 GPa Grade Count:471 |
Overview of materials for Nylon 66, 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 30% Glass Fiber Filled". Specific grades with glass content between 25% and 34% are included. .. |
|||
Modulus of Elasticity | 1.00 - 15.0 GPa | 145 - 2180 ksi | Average value: 7.98 GPa Grade Count:413 |
Overview of materials for Nylon 6, 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 30% Glass Fiber Filled". Specific grades with glass content between 25% and 34% are included. E.. |
|||
Modulus of Elasticity | 0.210 - 15.0 GPa | 30.5 - 2180 ksi | Average value: 2.32 GPa Grade Count:128 |
Overview of materials for Nylon 6, Impact Grade This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Impact Grade". Each property range of values reported is minimum and maximum values of appropri.. |
|||
Modulus of Elasticity | 2.25 - 15.0 GPa | 326 - 2180 ksi | Average value: 6.31 GPa Grade Count:143 |
Overview of materials for Polypropylene with 30% Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 30% Glass Fiber Filler". Specific grades with glass content between 25% and 34% are i.. |